Stainless steels generally contain between 10-20%chromium as the main alloying element and are valued for high corrosionresistance. With over 11% chromium, steel is about 200 times moreresistant to corrosion than mild steel. These steels can be divided into three groups based on their crystalline structure: Austenitic: Austenitic steels are non-magnetic and non heat-treatable, andgenerally contain 18% chromium, 8% nickel and less than 0.8% carbon. Austenitic steels form the largest porti...
Detail produktu
Štítky produktu
Nerezavějící oceli generally contain between 10-20%
chromium as the main alloying element and are valued for high corrosion
resistance. With over 11% chromium, steel is about 200 times more
resistant to corrosion than mild steel. These steels can be divided into
three groups based on their crystalline structure:
-
Austenitické :
Austenitické oceli jsou nemagnetické a non tepelně zpracovatelné, a
obvykle obsahují 18% chrómu, 8% niklu a méně než 0,8% uhlíku. Austenitické oceli
tvoří největší podíl na světovém trhu z nerezové oceli a jsou
často používány v zařízení na zpracování potravin, kuchyňské nádobí a potrubí. -
Feritické : Feritické oceli obsahují stopová množství niklu, 12 až 17% chrómu, méně než 0,1% uhlíku, spolu s dalších legovacích prvků, jako je molybden, hliníku nebo titanu. Tyto magnetické oceli nelze zpevnit s tepelným zpracováním, ale může být posílena tvářením za studena.
-
Martenzitické :
Martenzitické oceli obsahují 11-17% chrómu, méně než 0,4% niklu, a
až do 1,2% uhlíku. Tyto magnetické a tepelně zpracovatelné oceli se používají
nože, řezné nástroje, stejně jako zubní a chirurgické zařízení.