Leading Manufacturer for D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory from Comoros
1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade...
Innovation, quality and reliability are the core values of our company. These principles today more than ever form the basis of our success as an internationally active mid-size company for Leading Manufacturer for D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory from Comoros, We, with great passion and faithfulness, are willing to provide you with perfect services and striding forward with you to create a bright future.
1. Relevant D2 Steel Specifications
|Standard||ASTM A681||DIN EN ISO 4957||JIS G4404|
2. D2 Tool Steel Chemical Composition
|DIN ISO 4957||C||Mn||P||S||Si||Cr||V||Mo|
3. AISI Grade D2 Steel Mechanical Properties
|Hardness, Knoop (converted from Rockwell C hardness)||769||769|
|Hardness, Rockwell C||62||62|
|Izod impact unnotched||77.0 J||56.8 ft-lb|
|Elastic modulus||190-210 GPa||27557-30457 ksi|
|Thermal expansion||10.4 x 10-6/ºC||20-100||
4. AISI/ASTM A681 D2 Grade Steel Forging
Heating for forging of AISI D2 tool steel should
be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
should always be annealed after forging.
5. D2 Tool Steel Heat Treatment
ASTM D2 steels alloy should be preheated very slowly to 815oC (1500oF) and then temperature can be increased to 1010oC (1850oF). They are then held at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).
Annealing of D2 tool steels material should be done at 871 to 898oC (1600 to 1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or less.after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.
When desirable to relieve the strains of machining, heat D2 grade steel slowly to 1050°-1250°F, allow to equalize, and then cool in still air (Strain Relieving).
Preheat Prior To Hardening
Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.
After thorough preheating, heat to 1800°-1850°F. Hold the work piece at the hardening temperature until it is completely and uniformly heated.
AISI D2 steel tool material is an air hardening steel and will develop hardness on cooling in still air. To avoid scaling and prevent decarburization of the work piece surface, controlled atmosphere or vacuum furnaces are recommended. If these furnaces are not available, pack hardening, salt baths or wrapping the piece in stainless steel foil will provide some degree of surface protection in the hardening process. Parts should be allowed to cool to 150F, or to where they can be held in the bare hand, and then temper immediately.
The tempering temperature on material D2 steel may be varied according to the desired hardness. D2 steels can be tempered at 204oC (400oF) for achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell C hardness of 54.
6. D2 Tool Steel Material Application
AISI grade D2 tool steels are used for long run tooling applications, where wear resistance is important, such as blanking or forming dies and thread rolling dies.
Some main applications for D2 tool steel are as below:
Blanking Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls, Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear Parts.
We usually hold D2 tool steel on sale activities, and you would have our price on regular schedule. Contact us and sign in our newsletter to have D2 tool steel materials price list and commercial quote today.
For this video, a 3/8″ hole in an aluminum boat is repaired with Super Alloy 5 1/16′” rod and a Bernzomatic, oxygen/MAPP gas torch that can be found at almost any hardware store. Propane or MAPP gas without an oxygen feed will not work on aluminum boats due to the aluminum heat dissipation. Always clean the aluminum with an abrasive such as a sanding disk, wire wheel etc before starting your brazing process. SUPER ALLOY 1 CANNOT BE USED TO REPAIR ALUMINUM BOATS. IT IS NOT STRONG ENOUGH FOR THIS APPLICATION.
For more videos and information, or to order, visit http://MuggyWeld.com
Please read all instructions prior to use at: http://muggyweld.com/packets/superalloy5postsale.pdf
Please visit http://www.aws.org/technical/facts/ prior to using Muggy Weld products, and adhere to all AWS welding safety guidelines. Further product safety information is available at http://muggyweld.com/safety-guidelines.
Muggy Weld LLC shall not be liable for any loss, injury, claim, liability, or damage of any kind resulting in any way from (a) your use of this Site, (b) any services or products obtained from this Site, (c) any errors in or omissions from this Site, (d) the unavailability or interruption of this Site or any features thereof, (e) any content contained on this Site.
MSDS sheets available with purchase from MuggyWeld.com, upon request, with purchase.
Installing White Sound Defense uncaptured guide rod in a Glock pistol using the tool technique