Supply for D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Wholesale to Brasilia
1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade...
The key to our success is "Good Product Quality, Reasonable Price and Efficient Service" for Supply for D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Wholesale to Brasilia, Adhering to the business principle of mutual benefits, we have won good reputation among our customers because of our perfect services, quality products and competitive prices. We warmly welcome customers from home and abroad to cooperate with us for common success.
1. Relevant D2 Steel Specifications
|Standard||ASTM A681||DIN EN ISO 4957||JIS G4404|
2. D2 Tool Steel Chemical Composition
|DIN ISO 4957||C||Mn||P||S||Si||Cr||V||Mo|
3. AISI Grade D2 Steel Mechanical Properties
|Hardness, Knoop (converted from Rockwell C hardness)||769||769|
|Hardness, Rockwell C||62||62|
|Izod impact unnotched||77.0 J||56.8 ft-lb|
|Elastic modulus||190-210 GPa||27557-30457 ksi|
|Thermal expansion||10.4 x 10-6/ºC||20-100||
4. AISI/ASTM A681 D2 Grade Steel Forging
Heating for forging of AISI D2 tool steel should
be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
should always be annealed after forging.
5. D2 Tool Steel Heat Treatment
ASTM D2 steels alloy should be preheated very slowly to 815oC (1500oF) and then temperature can be increased to 1010oC (1850oF). They are then held at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).
Annealing of D2 tool steels material should be done at 871 to 898oC (1600 to 1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or less.after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.
When desirable to relieve the strains of machining, heat D2 grade steel slowly to 1050°-1250°F, allow to equalize, and then cool in still air (Strain Relieving).
Preheat Prior To Hardening
Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.
After thorough preheating, heat to 1800°-1850°F. Hold the work piece at the hardening temperature until it is completely and uniformly heated.
AISI D2 steel tool material is an air hardening steel and will develop hardness on cooling in still air. To avoid scaling and prevent decarburization of the work piece surface, controlled atmosphere or vacuum furnaces are recommended. If these furnaces are not available, pack hardening, salt baths or wrapping the piece in stainless steel foil will provide some degree of surface protection in the hardening process. Parts should be allowed to cool to 150F, or to where they can be held in the bare hand, and then temper immediately.
The tempering temperature on material D2 steel may be varied according to the desired hardness. D2 steels can be tempered at 204oC (400oF) for achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell C hardness of 54.
6. D2 Tool Steel Material Application
AISI grade D2 tool steels are used for long run tooling applications, where wear resistance is important, such as blanking or forming dies and thread rolling dies.
Some main applications for D2 tool steel are as below:
Blanking Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls, Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear Parts.
We usually hold D2 tool steel on sale activities, and you would have our price on regular schedule. Contact us and sign in our newsletter to have D2 tool steel materials price list and commercial quote today.
Stainless steel Small diameter tank inner surface automation polishing machine www.jotunpolishing.com email@example.com
Product Name:Long shaft polish arm tank inner surface automatic grinding machine
Brand Name:Jotun machinery
Color option:Yellow/blue/gray etc based on order
Machine Condition:100% New
Machine Weight:2200 kg
Control System:PLC/CNC Or Customized
Polishing Machine dimension:3500x1600x3080 mm
Power supply:380V/50Hz/3P Or Customized
Grinding efficiency:8-15 m2/Hour
Function/Usage:Polishing tank/dished heads’ surface
Others service:OEM/ODM/Oversea after-sales support
HeFei Jotun Machinery company is a professional manufacturer of Polishing and forging machines,We have our own two factory in Anhui province China with Well-equipped testing facilities and strong technical force.All our products gained CE,ISO,CCC certificates etc.
Main products:stainless steel/carbon steel tank/plate surface treatment polishing/grinding machine,hydraulic press brake,plate shear,rolling machine iron worker etc.
Números complejos de rectangular a polar
Suscribete a nuestro canal y no olvides dar like
Ingresa a nuestro sitio web y recibe asesorías en línea o presenciales
Siguenos en las diferentes redes sociales
Twitter : https://twitter.com/ProfesorJAAC