Renewable Design for D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory from Liverpool

Renewable Design for
 D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory from Liverpool

Short Description:

1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    we can offer high quality products, competitive price and best customer service. Our destination is "You come here with difficulty and we give you a smile to take away" for Renewable Design for D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory from Liverpool, Welcome to build the well and long standing business relationships with our company to create a glorious future together .customers' satisfaction is our eternal pursuit


    1. Relevant D2 Steel Specifications

    Country USA German Japan
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404
    Grades D2 1.2379/X153CrMo12 SKD11

    2. D2 Tool Steel Chemical Composition

    ASTM A681 C Mn P S Si Cr V Mo
    D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2
    DIN ISO 4957 C Mn P S Si Cr V Mo
    1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1
    JIS G4404 C Mn P S Si Cr V Mo
    SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2

    3. AISI Grade D2 Steel Mechanical Properties

    Mechanical Properties Metric Imperial
    Hardness, Knoop (converted from Rockwell C hardness) 769 769
    Hardness, Rockwell C 62 62
    Hardness, Vickers 748 748
    Izod impact unnotched 77.0 J 56.8 ft-lb
    Poisson’s ratio 0.27-0.30 0.27-0.30
    Elastic modulus 190-210 GPa 27557-30457 ksi

    Thermal Properties

    Properties

    Conditions

    T (°C)

    Treatment

    Thermal expansion 10.4 x 10-6/ºC 20-100

    4. AISI/ASTM A681 D2 Grade Steel Forging

    Heating for forging of AISI D2 tool steel should
    be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
    as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
    die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
    should always be annealed after forging.

    5. D2 Tool Steel Heat Treatment

    • Heat Treatment

    ASTM  D2 steels alloy should be preheated very slowly to 815oC (1500oF) and  then temperature can be increased to 1010oC (1850oF). They are then held  at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).

    • Annealing

    Annealing  of D2 tool steels material should be done at 871 to 898oC (1600 to  1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or  less.after which cooling rate may be increased. Suitable precautions  must be taken to prevent excessive carburization or decarburization.

    • Stress Relieving

    When  desirable to relieve the strains of machining, heat D2 grade steel  slowly to 1050°-1250°F, allow to equalize, and then cool in still air  (Strain Relieving).

    • Preheat Prior To Hardening

    Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.

    • Hardening

    After  thorough preheating, heat to 1800°-1850°F. Hold the work piece at the  hardening temperature until it is completely and uniformly heated.

    • Quenching

    AISI  D2 steel tool material is an air hardening steel and will develop  hardness on cooling in still air. To avoid scaling and prevent  decarburization of the work piece surface, controlled atmosphere or  vacuum furnaces are recommended. If these furnaces are not available,  pack hardening, salt baths or wrapping the piece in stainless steel foil  will provide some degree of surface protection in the hardening  process. Parts should be allowed to cool to 150F, or to where they can  be held in the bare hand, and then temper immediately.

    • Tempering

    The  tempering temperature on material D2 steel may be varied according to  the desired hardness. D2 steels can be tempered at 204oC (400oF) for  achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell  C hardness of 54.

    6. D2 Tool Steel Material Application
     AISI grade D2 tool steels are used for long run tooling applications,  where wear resistance is important, such as blanking or forming dies and  thread rolling dies.

    Some main applications for D2 tool steel are as below:

    Blanking  Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long  Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls,  Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread  Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear  Parts.

    We usually hold D2 tool  steel on sale activities, and you would have our price on regular  schedule. Contact us and sign in our newsletter to have D2 tool steel  materials price list and commercial quote today.

  • Previous:
  • Next:



  • : Irwin 15 piece HSS Professional Drill Bit Set
    HSS drill bits are designed to drill into a wide variety of materials such as metals, plastics and wood. All tradesmen will use them, as will most DIY’ers and home owners. HSS (High Speed Steel) drills are also known by many as ‘Jobber’ drills. HSS drills are not all manufactured to the same high standards and quality can vary dramatically. Poor quality drills will lead to very poor performance and a drill bit that will go blunt almost immediately. Irwin have been specialists in drilling for years and are well known for supplying top quality drill bits into industry and manufacturing.
    This professional 15 piece HSS set has been developed for trade use. The drill bits have 135° Split Point tips to reduce slipping, which is a common fault in many other HSS drills. The edges are precision ground so that the cutting angles are consistent and provide fast, clean cuts time and time again. This, along with the flute design along the shank, enables waste material to be removed quickly and efficiently. Again, this will result in a faster, cleaner and more accurate holes. This is critical if you are working to specific sizes and tolerances. They are ideal for metal, wood and plastic.
    The set is supplied in a robust lockable case. Each drill bit is stored in its own hole with an easy to read size guide for quick identification.
    This 15 piece set contains the following sizes:
    1.5, 2.0, 2.5, 3.0, 3.5, 4.0, 4.5, 5.0, 5.5, 6.0, 6.5, 7.0, 8.0, 9.0 and 10mm.

    Contents & Features
    • Precision ground drill bits.
    • 135° Split point tips to reduce ‘wander’.
    • Popular sizes: 1.5, 2.0, 2.5, 3.0, 3.5, 4.0, 4.5, 5.0, 5.5, 6.0, 6.5, 7.0, 8.0, 9.0 and 10mm.
    • Lockable storage case.
    • Ideal for drilling wood, metal, plastics, chipboard, plywood and similar materials.



    “FD Grip” The No.1 earthquake-resistant rebar coupler in Japan, the highest seismic country,
    for over 30 years.
    TEL:+62-21-6471-2565 http://www.fujibolt.com/index.html

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Cup

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Plane