Rapid Delivery for EN DIN 34CrNiMo6 | 1.6582 | 4337 Engineering Steel Manufacturer in Houston

Rapid Delivery for EN DIN 34CrNiMo6 | 1.6582 | 4337 Engineering Steel Manufacturer in Houston

Short Description:

EN 34CrNiMo6 Steel is an important alloy engineering steel grade as per BS EN10083-3:2006. 34CrNim06 steel has high strength, high toughness and good hardenability. EN / DIN 34CrNiMo6 alloy steel has the stability ofresistance to overheating, but the white sensitivity of 34CrNiM06 ishigh. It also has the temper brittleness, so the weldability of34CrNiMo6 material is poor. The steel 34CrNiMo6 needs the hightemperature preheating before welding in order to eliminate the stressafter welding proc...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    Our company since its inception, always regards product quality as enterprise life, continuously improve production technology, improve product quality and continuously strengthen enterprise total quality management, in strict accordance with the national standard ISO 9001:2000 for Rapid Delivery for EN DIN 34CrNiMo6 | 1.6582 | 4337 Engineering Steel Manufacturer in Houston, We will wholeheartedly welcome all clients in the industry both at home and abroad to cooperate hand in hand, and create a bright future together.


    EN 34CrNiMo6 Steel

    is an important alloy engineering steel grade as per BS EN
    10083-3:2006. 34CrNim06 steel has high strength, high toughness and good

    hardenability. EN / DIN 34CrNiMo6 alloy steel has the stability of
    resistance to overheating, but the white sensitivity of 34CrNiM06 is
    high. It also has the temper brittleness, so the weldability of
    34CrNiMo6 material is poor. The steel 34CrNiMo6 needs the high
    temperature preheating before welding in order to eliminate the stress
    after welding processing.


    1.EN Steel 34CrNiMo6 Supply Range

    Round Steel Bar Sizes: diameter 80mm – 1200mm
    Other steel shape and sizes available according to your requirements.

    Surface finish: Black, machined, peeled, turned or according to other customers’ pecial requirements.

    2.EN 34CrNiMo6 Steel Standards And Equivalents

    BS EN 10083 -3: 2006 34CrNiMo6 / 1.6582 ASTM A29: 2004 4337
    BS EN 10250 – 3: 2000

    3. EN/DIN 34CrNiMo6 Steel Chemical Composition Properties

    BS EN 10083 – 3:2006 34CrNiMo6
    /1.6582
    C Mn Si P S Cr Mo Ni
    0.30-0.38 0.5-0.8 0.40 max 0.025 max 0.035 max 1.3-1.7 0.15-0.30 1.3-1.7
    BS EN 10250-3:2000 C Mn Si P S Cr Mo Ni
    0.30-0.38 0.5-0.8 0.40 max 0.035 max 0.035 max 1.3-1.7 0.15-0.30 1.3-1.7
    ASTM A29: 2004 4337 C Mn Si P S Cr Mo Ni
    0.30-0.40 0.6-0.8 0.20-0.35 0.035 max 0.040 max 0.70-0.90 0.20-0.30 1.65-2.00

    4.Mechanical Properties of EN/DIN 34CrNiM06 / 1.6582 Alloy Steel

    Properties < 16 >16 – 40 >40 – 100 >100 – 160 >160 – 250
    Thickness t [mm] < 8 8<t<20 20<t<60 60<t<100 100<t<160
    Yield strength Re [N/mm2] min. 1000 min. 900 min. 800 min. 700 min. 600
    Tensile strength Rm [N/mm2] 1200 – 1400 1100 – 1300 1000 – 1200 900 – 1100 800 – 950
    Elongation A [%] min. 9 min. 10 min. 11 min. 12 min. 13
    Reduction of area Z [%] min. 40 min. 45 min. 50 min. 55 min. 55
    Toughness CVN [J] min. 35 min. 45 min. 45 min. 45 min. 45

    5.Heat Treatment of 34CrNiMo6 Engineering Steel

    Quenched and Tempered (Q+T) of 34CrNiMo6 Steel

      Heat 34CrNiMo6 round steel slowly to the temperature of 850°C;

      Soak at this hardening temperature quench in oil;

      Temper as soon as 34CrNiMo6 steels reach room temperature.

      Heat uniformly to the suitable temperature;

      Withdraw from the furnace and cool in the air.

      The usual tempering temperature is 600°C which depending on the actual requirements.

      6.Forging of DIN 34CrNiMo6 / 1.6582 Steel

      Hot forming temperature: 1100-900oC.

      7.Machinability of Steel34CrNiMo6

      Machining

      is best done with this 1.6582 alloy steel in the annealed or normalized

      and tempered condition. It can be machined by all conventional methods.

      8.Welding

      The

      alloy materials can be fusion or resistance welded. Preheat and post
      heat weld procedures should be followed when welding this alloy by
      established methods.

      9.Application

      EN DIN
      34CrNiMo6 steel is used to make tools which demands good plasticity and
      high strength. It is usually selected to make the big size and important

      parts, such as heavy machinery axle,turbine shaft blade, high load of
      transmission parts, fasteners, crank shafts, gears, as well as heavily
      loaded parts for motor construction etc.

      Otai Steel is reliable to

      supply engineering 34CrNiMo6 steels / 1.6582 engineering alloy steels.
      Please tell us your detailed requirements and have the best offer soon.

    • Previous:
    • Next:




  • Drilling stainless steel can be difficult, but cutting a hole in stainless steel using a hole saw is even more difficult. In this video I cut out a 1 inch hole in some 316 stainless steel which has about a 2mm wall thickness. A traditional hole saw will really struggle on this grade of stainless steel, which is why I use the Starrett carbide tipped hole saw.
    You can buy these Holesaws at the following link https://www.starrett.co.uk/shop/power_tool_accessories/holesaws/tct_carbide_tipped_d/

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Tree

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Heart