ASTM A295 is specification which covers 52100 high carbon bearing quality steelto be used in the manufacture of anti-friction bearings. And 52100 bearing steel is the most common steel grade in ASTM A295 standard for high-carbon anti-friction bearing steel. What is 52100 bearing steel? AISI/ASTM 52100 bearing steel is a high carbon, chromium containing low alloysteel that is through hardening and noted in particular for use asbearings. 52100 bearing steel is one kind of special steel with ...
With our excellent management, strong technical capability and strict quality control system, we continue to provide our clients with reliable quality, reasonable prices and excellent services. We aim at becoming one of your most reliable partners and earning your satisfaction for Quality Inspection for ASTM 52100 Bearing Steel | 1.3505 | 100Cr6 | SUJ2 | EN31 Supply to Greece, We encourage you to make contact as we are looking for partners in our venture. We are sure you will find doing business with us not only fruitful but also profitable. We are ready to serve you with what you require.
is specification which covers 52100 high carbon bearing quality steel
to be used in the manufacture of anti-friction bearings. And is the most common steel grade in ASTM A295 standard for high-carbon anti-friction bearing steel.
What is 52100 bearing steel?
52100 bearing steel is a high carbon, chromium containing low alloy
steel that is through hardening and noted in particular for use as
52100 bearing steel is one kind of special steel with features of
high wear resistance and rolling fatigue strength. High-carbon chromium
bearing steel, engineering steel and some types of stainless steel and
heat resistant steel are used as materials of bearings and for other
Advantages of Chrome Bearing Steel 52100:
Superior hardness, 60-67 on Rockwell hardness scale (Rc) at room temperature
High carbon chrome alloy steel
Operates continually at temperatures up to 120°C
Used to produce precision ball bearings and roller bearings
Long working life
1. Relevant Steel Specification of ASTM 52100 Bearing Steel
|Standard||ASTM A295||DIN 17230|
2. Chemical Composition of 52100 Bearing Steel and Equivalents
3. Mechanical Properties of ASTM A295 52100 Bearing Steel
|Bulk modulus (typical for steel)||140 GPa||20300 ksi|
|Shear modulus (typical for steel)||80 GPa||11600 ksi|
|Elastic modulus||190-210 GPa||27557-30458 ksi|
|Hardness, Knoop (converted from Rockwell C hardness)||875||875|
|Hardness, Rockwell C (quenched in oil from 150°C tempered)||62||62|
|Hardness, Rockwell C (quenched in water from 150°C tempered)||64||64|
|Hardness, Rockwell C (quenched in oil)||64||64|
|Hardness, Rockwell C (quenched in water)||66||66|
|Hardness, Vickers (converted from Rockwell C hardness)||848||848|
|Machinability (spheroidized annealed and cold drawn. Based on 100 machinability for AISI 1212 steel)||40||40|
52100 Steel Physical Properties
|Density||7.81 g/cm3||0.282 lb/in³|
52100 Alloy Steel Thermal Properties
|Thermal expansion co-efficient (@ 23-280°C/73.4- 36°F, annealed)||11.9 µm/m°C||6.61 µin/in°F|
|Thermal conductivity (typical steel)||46.6 W/mK||323 BTU in/hr.ft².°F|
4. Forging of A295 52100 Bearing Steel
52100 alloy steel is forged at 927 to 1205°C, and should not be forged
below 925ºC. A post-forge equalization treatment is recommended at 745ºC
for 4-6 hours followed by air cooling for SAE/AISI 52100 steel.
6. Heat Treatment for ASTM 52100 Bearing Steel
52100 alloy bearing steel is heated at 816°C followed by quenching in
oil. Before performing this process, it is subjected to normalizing heat
treatment at 872°C followed by slowly cooling in order to reduce the
AISI 52100 bearing steels alloy can be hot worked at 205 to 538°C.
AISI 52100 bearing steel can be cold worked using conventional techniques in the annealed or normalized conditions.
For spheroidize anneale, the following isothermal anneal is recommended:
1500ºF (815ºC) for 3 hours
1350ºF (735ºC) for 4 hours
1250ºF (675ºC) for 3 hours
Slow cool to 1000ºF (540ºC) then air cool.
AISI 52100 alloy bearing steel could be hardened by quenching in water from 801-829 degree or quench in oil from 816-842 degree.
Temper to desired hardness as indicated by tempering curves after water or oil quench.
5. Applications of 52100 Bearing Steel
steel 52100 grade bearing steel is mainly used for the manufacture of
aircraft bearings and other highly stressed parts. This steel grade
52100 steel is preferably vacuum arc re-melted to give optimum
Typical applications: Bearing Manufacture, CV joints, ball screws, gauges, knife etc.
Punch and dies provide strong resistance against wear, especially when working with stainless steel. Round punch and die sets are fully machined from the highest quality tool steel (ISO) with 8 cutting sides and are hardened to 55 rockwell. Square punch and die sets are manufactured from the highest quality tool steel (ISO) by EDM machine centre and are also hardened to 55 rockwell.
The HP-3 hydraulic hole puncher is a portable unit weighing only 4.5kg with an output performance at 10 ton capacity. This unit requires little effort to operate and allows a professional finish on the job with no damage to finished paint products. The HP-3 also offers a 2 speed pump for faster punching and can punch up to 2.4mm stainless steel.
This hydraulic punching unit is best used in the sheet metal industry, electrical switchboards, sink wastes, kitchen fabricators etc.
For further information please visit us at http://www.stainelec.com.au
For More Info Visit Our New Website http://fav.net.in/Hydraulic-Fittings/ Or Contact as on email@example.com. Also you can visit http://instrumentation-fittings.com/hydraulic-fittings/