professional factory provide AISI304| SUS304| EN1.4948 in Doha

professional factory provide
 AISI304| SUS304| EN1.4948 in Doha

Short Description:

Chemical Composition of Stainless Steel 304 Table 1. Chemical composition for 304 stainless steel alloys % 304 304L 304H C 0.0 – 0.07 0.0 – 0.03 0.04 – 0.08 Mn 0.0 – 2.0 0.0 – 2.00 0.0 – 2.0 Si 0.0 – 1.00 0.0 – 1.00 0.0 – 1.0 P 0.0 – 0.05 0.0 – 0.05 0.0 – 0.04 S 0.0 – 0.03 0.0 – 0.02 0.0 – 0.02 Cr 17.50 – 19.50 17.50 – 19.50 ...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    continue to improve, to ensure product quality in line with market and customer standard requirements. Our company has a quality assurance system have been established for professional factory provide AISI304| SUS304| EN1.4948 in Doha, If you have any comments about our company or products, please feel free to contact us, your coming mail will be highly appreciated.


    Chemical Composition of Stainless Steel 304

    Table 1. Chemical composition for 304 stainless steel alloys

    %

    304

    304L

    304H

    C

    0.0 – 0.07

    0.0 – 0.03

    0.04 – 0.08

    Mn

    0.0 – 2.0

    0.0 – 2.00

    0.0 – 2.0

    Si

    0.0 – 1.00

    0.0 – 1.00

    0.0 – 1.0

    P

    0.0 – 0.05

    0.0 – 0.05

    0.0 – 0.04

    S

    0.0 – 0.03

    0.0 – 0.02

    0.0 – 0.02

    Cr

    17.50 – 19.50

    17.50 – 19.50

    17.00 – 19.00

    Ni

    8.00 – 10.50

    8.00 – 10.50

    8.00 – 11.00

    Fe

    Balance

    Balance

    Balance

    N

    0.0-0.11

    0.0-0.11

    0.0 – 0.10

    Properties of Stainless Steel 304

    Mechanical Properties of Stainless Steel 304

    Table 2a. Mechanical properties for 304 stainless steel alloys – sheet up to 8 mm thick

    Grade

    304

    304L

    304H

    Tensile Strength (MPa)

    540 – 750

    520 – 700

    -

    Proof Stress (MPa)

    230 Min

    220 Min

    -

    Elongation A50 mm

    45 Min %

    45 Min %

    -


    Table 2b. Mechanical properties for 304 stainless steel alloys – plate from 8 – 75 mm thick

    Grade

    304

    304L

    304H

    Tensile Strength (MPa)

    520 – 720

    500 – 700

    -

    Proof Stress (MPa)

    210 Min

    200 Min

    -

    Elongation A5

    45 Min %

    45 Min %

    -


    Table 2c. Mechanical properties for 304 stainless steel alloys – bar and section up to 160 mm diameter / thickness

    Grade

    304

    304L

    304H

    Tensile Strength (MPa)

    500 – 700

    500 – 700

    500 – 700

    Proof Stress (MPa)

    190

    175 Min

    185 Min

    Elongation A50 mm

    45 Min %

    45 Min %

    40 Min %

    Hardness Brinell

    215 Max HB

    215 Max HB

    -

    Physical Properties of Stainless Steel 304

    Table 3. Physical properties for 304 stainless steel alloys

    Property

    Value

    Density

    8.00 g/cm3

    Melting Point

    1450 °C

    Modulus of Elasticity

    193 GPa

    Electrical Resistivity

    0.072 x 10-6 Ω.m

    Thermal Conductivity

    16.2 W/m.K

    Thermal Expansion

    17.2 x 10-6 /K

    Alloy Designations

    Stainless steel 304 also corresponds to the following standard designations and specifications:

    Euronorm

    UNS

    BS

    En

    Grade

    1.4301

    S30400

    304S15

    304S16

    304S31

    58E

    304

    1.4306

    S30403

    304S11

    -

    304L

    1.4307

    -

    304S11

    -

    304L

    1.4311

    -

    304S11

    -

    304L

    1.4948

    S30409

    304S51

    -

    304H

    Corrosion Resistance of Stainless Steel 304

    Stainless steel 304
    has excellent corrosion resistance in a wide variety of environments
    and when in contact with different corrosive media. Pitting and crevice
    corrosion can occur in environments containing chlorides. Stress
    corrosion cracking can occur at temperatures over 60°C.

    Heat Resistance of Stainless Steel 304

    Stainless steel 304 has
    good resistance to oxidation in intermittent service up to 870°C and in
    continuous service to 925°C. However, continuous use at 425-860°C is
    not recommended if corrosion resistance in water is required. In this
    instance 304L is recommended due to its resistance to carbide
    precipitation.

    Where high strength is required at temperatures above 500°C and up to
    800°C, grade 304H is recommended. This material will retain aqueous
    corrosion resistance.

    Fabrication of Stainless Steel 304

    Fabrication of all stainless steels should
    be done only with tools dedicated to stainless steel materials. Tooling
    and work surfaces must be thoroughly cleaned before use. These
    precautions are necessary to avoid cross contamination of stainless steel by easily corroded metals that may discolour the surface of the fabricated product.

    Cold Working of Stainless Steel 304

    Stainless steel 304 readily
    work hardens. Fabrication methods involving cold working may require an
    intermediate annealing stage to alleviate work hardening and avoid
    tearing or cracking. At the completion of fabrication a full annealing
    operation should be employed to reduce internal stresses and optimise
    corrosion resistance.

    Hot Working of Stainless Steel 304

    Fabrication methods, like forging, that involve hot working should
    occur after uniform heating to 1149-1260°C. The fabricated components
    should then be rapidly cooled to ensure maximum corrosion resistance.

    Heat Treatment of Stainless Steel 304

    Stainless steel 304 cannot be hardened by heat treatment.

    Solution treatment or annealing can be done by rapid cooling after heating to 1010-1120°C.

    Machinability

    Stainless steel 304 has good machinability. Machining can be enhanced by using the following rules:

    • Cutting edges must be kept sharp. Dull edges cause excess work hardening.

    • Cuts should be light but deep enough to prevent work hardening by riding on the surface of the material.

    • Chip breakers should be employed to assist in ensuring swarf remains clear of the work

    • Low thermal conductivity of austenitic alloys results in heat
      concentrating at the cutting edges. This means coolants and lubricants
      are necessary and must be used in large quantities.

    Welding of Stainless Steel 304

    Fusion welding performance for Stainless steel 304 is excellent both with and without fillers. Recommended filler rods and electrodes for stainless steel 304 is grade 308 stainless steel.
    For 304L the recommended filler is 308L. Heavy welded sections may
    require post-weld annealing. This step is not required for 304L. Grade
    321 may be used if post-weld heat treatment is not possible.

    Applications of Stainless Steel 304

    Stainless steel 304 is typically used in:

    • Sinks and splashbacks

    • Saucepans

    • Cutlery and flatware

    • Architectural panelling

    • Sanitaryware and troughs

    • Tubing

    • Brewery, dairy, food and pharmaceutical production equipment

    • Springs, nuts, bolts and screws

  • Previous:
  • Next:



  • This video demonstrates how to strap a wooden crate with 19mm steel strapping using steel strapping tools. The 19mm steel strapping is tensioned with a S246 feedwheel tensioner. The 19mm seal is crimped closed with a C3126 19mm steel crimper and the steel is cut from the roll with a H201 hand cutter. MIPAQ imports and distributes hundreds of packaging tools and machines. To view our full range of packaging machines, tools, equipment and consumables please visit www.mipaq.co.za.



    I’ve had a number of friends and family members tell me they need to keep a teflon nonstick pan around because they just can’t cook eggs without it. Teflon is unquestionably bad news for your health and anyone who has owned a nonstick pan over the years has watched the coating eventually flake off. Guess where all that Teflon is going? In your food!

    For those wondering, this style of scrambled egg is one we picked up in Brasil. I like them because the egg is about half way between scrambled and fried. If you finish it the way I did here you can also get some yoke that is still soft while the whites are completely cooked. You can obviously cook them to be firmer if you like. If you want a more traditional scrambled finish, just whisk them up before you put them in the pan.

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Plane

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Cup