AISI 4340 steel is a medium carbon, low alloy steel known for its toughness andstrength in relatively large sections. AISI 4340 is also one kind ofnickel chromium molybdenum steels. 4340 alloy steel is generallysupplied hardened and tempered in the tensile range of 930 – 1080 Mpa.Pre hardened and tempered 4340 steels can be further surface hardened by flame or induction hardening and by nitriding. The 4340 steel has goodshock and impact resistance as well as wear and abrasion resistanc...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    The company keeps to the operation concept "scientific management, high quality and efficiency primacy, customer supreme for professional factory provide AISI 4340 Steel | 36CrNiMo4 | 1.6511 | EN24 | 817M40 | SNCM439 Factory from Manila, winning customers' trust is the gold key to our success! If you are interested in our products, please feel free to visit our web site or contact us.


    AISI 4340 steel
    is a medium carbon, low alloy steel known for its toughness and
    strength in relatively large sections. AISI 4340 is also one kind of
    nickel chromium molybdenum steels. 4340 alloy steel is generally
    supplied hardened and tempered in the tensile range of 930 – 1080 Mpa.
    Pre hardened and tempered 4340 steels can be further surface hardened by
    flame or induction hardening and by nitriding. The 4340 steel has good
    shock and impact resistance as well as wear and abrasion resistance in
    the hardened condition. AISI 4340 steel properties offer good ductility
    in the annealed condition, allowing it to be bent or formed. Fusion and
    resistance welding is also possible with our 4340 alloy steel. ASTM 4340
    material is often utilized where other alloy steels do not have the
    hardenability to give the strength required. For highly stressed parts
    it is excellent choice. AISI 4340 alloy steel can also be machined by
    all customary methods.

    Due to availability the ASTM 4340 grade steel is often substituted
    with European based standards 817M40/EN24 and 1.6511/36CrNiMo4 or Japan
    based SNCM439 steel. You have the detailed data of 4340 steel below.

    1. AISI 4340 Steel Specification and Relevant Standards

    Country USA Britain Britain Japan
    Standard ASTM A29 EN 10250 BS 970 JIS G4103
    Grades 4340 36CrNiMo4/
    1.6511
    EN24/817M40 SNCM 439/SNCM8

    2. ASTM 4340 Steels And Equilvalents Chemical Composition

    Standard Grade C Mn P S Si Ni Cr Mo
    ASTM A29 4340 0.38-0.43 0.60-0.80 0.035 0.040 0.15-0.35 1.65-2.00 0.70-0.90 0.20-0.30
    EN 10250 36CrNiMo4/
    1.6511
    0.32-0.40 0.50-0.80 0.035 0.035 ≦0.40 0.90-1.20 0.90-1.2 0.15-0.30
    BS 970 EN24/817M40 0.36-0.44 0.45-0.70 0.035 0.040 0.1-0.40 1.00-1.40 0.20-0.35
    JIS G4103 SNCM 439/SNCM8 0.36-0.43 0.60-0.90 0.030 0.030 0.15-0.35 1.60-2.00 0.60-1.00 0.15-0.30

    3. AISI Alloy 4140 Steel Mechanical Properties

    Mechannical Properties

    (Heat Treated Condition )

    Condition Ruling section
    mm
    Tensile Strength MPa Yield Strength
    MPa
    Elong.
    %
    Izod Impact
    J
    Brinell
    Hardness
    T 250 850-1000 635 13 40 248-302
    T 150 850-1000 665 13 54 248-302
    U 100 930-1080 740 12 47 269-331
    V 63 1000-1150 835 12 47 293-352
    W 30 1080-1230 925 11 41 311-375
    X 30 1150-1300 1005 10 34 341-401
    Y 30 1230-1380 1080 10 24 363-429
    Z 30 1555- 1125 5 10 444-

    Thermal Properties

    Properties Metric Imperial
    Thermal expansion co-efficient (20°C/68°F, specimen oil hardened, 600°C (1110°F) temper 12.3 µm/m°C 6.83 µin/in°F
    Thermal conductivity (typical steel) 44.5 W/mK 309 BTU in/hr.ft².°F

    4. Forging of 4340 Alloy Steel

    Preheat
    the steel 4340 first, heat up to 1150°C – 1200°C maximum for forging,
    hold until temperature is uniform throughout the section.

    Do not forge
    below 850 °C. 4340 has good forging characteristics but care must be
    taken when cooling as the steel shows susceptibility to cracking.
    Following forging operation the work piece should be cooled as slowly as
    possible. And cooling in in sand or dry lime is recommended etc.

    5. AISI 4340 Steel Grade Heat Treatment

    • Stress Relieving

    For
    pre-hardened steel stress relieving is achieved by heating steel 4340
    to between 500 to 550°C. Heat to 600 °C – 650 °C, hold until temperature
    is uniform throughout the section, soak for 1 hour per 25 mm section,
    and cool in still air.

    • Annealing

    A
    full anneal may be done at 844°C (1550 F) followed by controlled
    (furnace) cooling at a rate not faster than 10°C (50 F) per hour down to
    315°C (600 F). From 315°C 600 F it may be air cooled.

    • Tempering

    AISI
    4340 alloy steel should be in the heat treated or normalized and heat
    treated condition before tempering. The tempering temperature for
    depends upon the strength level desired. For strength levels in the 260 –
    280 ksi range temper at 232°C (450 F). For strength in the 125 – 200
    ksi range temper at 510°C (950 F). And don’t temper the 4340 steels if
    it is in the 220 – 260 ksi strength range as tempering can result in
    degradation of impact resistance for this level of strength.

    Tempering should be avoided if possible within the range 250 °C – 450 °C due to temper brittleness.

    • Flame or Induction Hardening

    As mentioned above, pre-hardened and tempered 4340 steel bars or plates can be further surface hardened by either the flame or induction hardening
    methods resulting in a case hardness in excess of Rc 50. AISI 4340
    steel parts should be heated as quickly as possible to the austenitic
    temperature range (830 °C – 860 °C) and required case depth followed by
    an immediate oil or water quenching, depending upon hardness required,
    workpiece size/shape and quenching arrangements.

    Following
    quenching to hand warm, tempering at 150°C – 200°C will reduce stresses
    in the case with minimal effect on its hardness.

    All de-carburised surface material must first be removed to ensure best results.

    • Nitriding

    Hardened
    and tempered 4340 alloy steel can also be nitrided, giving a surface
    hardness of up to Rc 60. Heat to 500°C – 530°C and hold for sufficient
    time (from 10 to 60 hours) to develop the depth of case. Nitriding
    should be followed by slow cooling (no quench) reducing the problem of
    distortion. The nitrided grade 4340 materials can therefore be machined
    to near final size, leaving a small grinding allowance only. The tensile
    strength of the 4340 steel material core is usually not affected since
    the nitriding temperature range is generally below the original
    tempering temperature employed.

    Surface hardness achievable is 600 to 650HV.

    6. Machinability

    Machining
    is best done with the alloy steel 4340 in the annealed or normalized
    and tempered condition. It can be readily machined by all conventional
    methods such as sawing, turning, drilling etc. However in the high
    strength conditions of 200 ksi or greater the machinability is only from
    25% to 10% that of the alloy in the annealed condition.

    7. Welding

    Welding
    of steel 4340 in the hardened and tempered condition (as normally
    supplied), is not recommended and should be avoided if at all possible,
    because of the danger of quench cracking, as the mechanical properties
    will be altered within the weld heat affected zone.

    If welding
    must be carried out, pre-heat to 200 to 300°C and maintain this while
    welding. Immediately after welding stress relieve at 550 to 650°C, prior
    to hardening and tempering.

    If welding in the hardened and
    tempered condition is really necessary, then the work piece, immediately
    on cooling to hand warm, should be if possible stress relieved at 15 °C
    below the original tempering temperature.

    8. Application of 4340 Steel

    AISI
    4340 steel is used in most industry sectors for applications requiring
    higher tensile/yield strength than 4140 steel can provide.

    Some typical applications such as:

    • Aircraft Landing Gear

    • Automotive,

    • Oil and Gas Drilling,

    • Forging,

    • Warm and Cold Forming,

    • Machine Building,

    • Transfer Systems, like power transmission gears and shafts.

    • General
      engineering industries and structural use applications, such as: heavy
      duty shafts, gears, axles, spindles, couplings, pins, chucks, molds etc.

  • Previous:
  • Next:



  • Proformance Unlimited’s Chrysler 440 with 475hp crate engine package. You can view pricing at the following link: https://www.customcrateengines.com/engines/chrysler/440-chrysler-crate-engine-with-475-hp.html
    Seasoned Chrysler 440 Block
    Bored and honed with deck plate
    Mains have been aligned
    Block has been decked
    Dura Bond cam bearings installed
    Brass freeze plug and oil galley kit installed
    Block painted with 3 coats of high temp ceramic engine paint customer’s choice of color
    Eagle 4340 forged steel crankshaft 3.750 stroke
    Eagle H-Beam connecting rods with 7/16 cap screws
    High performance forged pistons (SRP, or Mahle)
    Performance rod and main bearing (Clevite, King or Federal Mogul)
    Hastings performance rings hand filed to match application
    The complete rotating assembly will be balanced
    Comp Cams custom ground hydraulic roller performance camshaft
    Three piece true double roller timing set
    Retro fit tie-bar hydraulic roller lifters
    Edelbrock performance aluminum cylinder
    High performance valve springs and retainers (to match camshaft)
    Manley chrome moly push rods
    Performance shaft mount roller rockers
    Melling high volume oil pump
    Melling oil pick up
    Chrome oil pan
    Chrome dip stick and tube
    Chrome timing cover
    Engine will be assembled with all new bolts
    A set of ARP head bolts
    Fel-Pro performance gaskets
    Professional Products performance balancer
    Edelbrock aluminum Performer RPM intake manifold
    Chrome thermostat housing
    Holley Ultra HP carburetor w/ electric choke
    Chrome air cleaner
    Pro Billet distributor (requires MSD 6AL Ignition Control)
    MSD Blaster II coil and bracket
    Autolite spark plugs
    Taylor 8mm ignition wires (color of choice black, red, blue, yellow, green, orange no extra charge)
    High flow water pump
    Chrome valve covers
    Chrome breather
    Engines are photo documented during the building process so you can see the quality of parts and workmanship that goes into your engine
    Each engine is dyno tested, timing set and carburetor adjusted for optimum performance
    We video tape your engine and send you a copy



    高速・高送り・高能率・切屑処理で加工コスト低減を実現します。
    刃径11.0~35.0。深さ3D・5D・7Dに対応。

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Plane

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Car