Original Factory D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Supply to Bahrain
1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade...
We take "customer-friendly, quality-oriented, integrative, innovative" as objectives. "Truth and honesty" is our management ideal for Original Factory D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Supply to Bahrain, Our aim is to help customers realize their goals. We are making great efforts to achieve this win-win situation and sincerely welcome you to join us
1. Relevant D2 Steel Specifications
|Standard||ASTM A681||DIN EN ISO 4957||JIS G4404|
2. D2 Tool Steel Chemical Composition
|DIN ISO 4957||C||Mn||P||S||Si||Cr||V||Mo|
3. AISI Grade D2 Steel Mechanical Properties
|Hardness, Knoop (converted from Rockwell C hardness)||769||769|
|Hardness, Rockwell C||62||62|
|Izod impact unnotched||77.0 J||56.8 ft-lb|
|Elastic modulus||190-210 GPa||27557-30457 ksi|
|Thermal expansion||10.4 x 10-6/ºC||20-100||
4. AISI/ASTM A681 D2 Grade Steel Forging
Heating for forging of AISI D2 tool steel should
be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
should always be annealed after forging.
5. D2 Tool Steel Heat Treatment
ASTM D2 steels alloy should be preheated very slowly to 815oC (1500oF) and then temperature can be increased to 1010oC (1850oF). They are then held at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).
Annealing of D2 tool steels material should be done at 871 to 898oC (1600 to 1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or less.after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.
When desirable to relieve the strains of machining, heat D2 grade steel slowly to 1050°-1250°F, allow to equalize, and then cool in still air (Strain Relieving).
Preheat Prior To Hardening
Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.
After thorough preheating, heat to 1800°-1850°F. Hold the work piece at the hardening temperature until it is completely and uniformly heated.
AISI D2 steel tool material is an air hardening steel and will develop hardness on cooling in still air. To avoid scaling and prevent decarburization of the work piece surface, controlled atmosphere or vacuum furnaces are recommended. If these furnaces are not available, pack hardening, salt baths or wrapping the piece in stainless steel foil will provide some degree of surface protection in the hardening process. Parts should be allowed to cool to 150F, or to where they can be held in the bare hand, and then temper immediately.
The tempering temperature on material D2 steel may be varied according to the desired hardness. D2 steels can be tempered at 204oC (400oF) for achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell C hardness of 54.
6. D2 Tool Steel Material Application
AISI grade D2 tool steels are used for long run tooling applications, where wear resistance is important, such as blanking or forming dies and thread rolling dies.
Some main applications for D2 tool steel are as below:
Blanking Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls, Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear Parts.
We usually hold D2 tool steel on sale activities, and you would have our price on regular schedule. Contact us and sign in our newsletter to have D2 tool steel materials price list and commercial quote today.
Don demonstrates the Tippmann Clicker die cutting machine die cutting leather using a steel rule cutting die. The Tippmann electric die cutting press is ideal for die cutting leather, die cutting textiles, die cutting fur, die cutting textiles, die cutting printed books, die cutter for paper, die cutter for samples, die cutter for scrap booking. If you would like to see if the Tippmann Clicker press will work for your die cutting application let us know, as we would be happy to provide live die cutting tests for you. You can send us sample material and we will show you a live die cutting test with our live tippmann clicker die cutting test camera
Clean up drawn wire for nail manufacturing,Round drawn clear wire for nail manufacturing inquiry at email@example.com Factory producer spherical clear drawn wire,Clean up ball wire,Shiny ring nails exported to Euro.America, Sweden. Clean up drawn steel wire for vivid ring shank popular nail manufacturing. Metal wire for vivid ring nail manufacturing.real manufacturing facility supplier.large excellent finest price. Diameter : 1.five-three.five-4.0mm Tensile strenght : 500-1000N. Deal: 800-1200kg coil
clear steel wire for nail manufacturing/articel rould drawn clear wire for nail manufacturing.dimensions and tolerance, dim.tol.+/-.03mm
tensile energy Rm850-900-1000 Deal roll dia ID500mm
the MOQ 1-5Tons
The content is Q195/235 #forty five,60,65,70 C7D C9D.
deal requests roll sizing is ID/OD 508/840mm
banded with 4 iron bands and 4 eyebolts
MOQ 1-5Tons #forty five, #60, #65, #70 Q195/235/22A
three. all your quoted goods satisfy global standard .Significant excellent and competitive price.
HEBEI XUANKE Trading CO LTD.(HUIXIN Construction Supplies CO LTD.)
Mobile phone: 0086-15630186759