Online Manufacturer for AISI 8620 Steel | 1.6523 | 21NiCrMo2 | SNCM220 Supply to Hyderabad

Online Manufacturer for
 AISI 8620 Steel | 1.6523 | 21NiCrMo2 | SNCM220 Supply to Hyderabad

Short Description:

AISI 8620 Steel is a low alloy nickel, chromium, molybdenum case hardening steel,generally supplied in the as rolled condition with a maximum hardness HB 255max. SAE steel 8620 offers high external strength and good internalstrength, making it highly wear resistant. AISI 8620 steel has a highercore strength than grades 8615 and 8617. SAE 8620 alloy steel isflexible during hardening treatments, thus enabling improvement ofcase/core properties. Pre hardened and tempered (uncarburized) 8620 ca...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    Our company since its inception, always regards product quality as enterprise life, continuously improve production technology, improve product quality and continuously strengthen enterprise total quality management, in strict accordance with the national standard ISO 9001:2000 for Online Manufacturer for AISI 8620 Steel | 1.6523 | 21NiCrMo2 | SNCM220 Supply to Hyderabad, We are sincerely welcome good friends from numerous circles at dwelling and abroad come to cooperate!


    AISI 8620 Steel

    is a low alloy nickel, chromium, molybdenum case hardening steel,
    generally supplied in the as rolled condition with a maximum hardness HB

    255max. SAE steel 8620 offers high external strength and good internal
    strength, making it highly wear resistant. AISI 8620 steel has a higher
    core strength than grades 8615 and 8617.

    SAE 8620 alloy steel is
    flexible during hardening treatments, thus enabling improvement of
    case/core properties. Pre hardened and tempered (uncarburized) 8620 can
    be further surface hardened by nitriding but will not respond
    satisfactorily to flame or induction hardening due to its low carbon
    content.

    Steel 8620 is suited for applications which require a
    combination of toughness and wear resistance. This grade is commonly
    supplied in round bar.

    1. AISI 8620 Steel Supply Range

    8620 Round Bar: diameter 80mm – 1200mm
    8620 Steel Plate: thickness 10mm – 1500mm x width 200mm – 3000mm
    8620 Square Bar: 140mm – 460mm
    8620 tubes are also available against your detailed request.
    Surface Finish: Black, Rough Machined, Turned or as per given requirements.

    2. SAE 8620 Steel Specification and Relevant Standards

    Country

    USA DIN BS BS

    Japan

    Standard

    ASTM A29 DIN 1654 EN 10084

    BS 970

    JIS G4103

    Grades

    8620

    1.6523/
    21NiCrMo2

    1.6523/
    20NiCrMo2-2

    805M20

    SNCM220

    3. ASTM 8620 Steels & Equilvalents Chemical Composition

    Standard Grade C Mn P S Si Ni Cr Mo
    ASTM A29 8620 0.18-0.23 0.7-0.9 0.035 0.040 0.15-0.35 0.4-0.7 0.4-0.6 0.15-0.25
    DIN 1654 1.6523/
    21NiCrMo2
    0.17-0.23 0.65-0.95 0.035 0.035 ≦0.40 0.4-0.7 0.4-0.7 0.15-0.25
    EN 10084 1.6523/
    20NiCrMo2-2
    0.17-0.23 0.65-0.95 0.025 0.035 ≦0.40 0.4-0.7 0.35-0.70 0.15-0.25
    JIS G4103 SNCM220 0.17-0.23 0.6-0.9 0.030 0.030 0.15-0.35 0.4-0.7 0.4-0.65 0.15-0.3
    BS 970 805M20 0.17-0.23 0.6-0.95 0.040 0.050 0.1-0.4 0.35-0.75 0.35-0.65 0.15-0.25

    4. AISI 8620 Steel Mechanical Properties

    • 8620 Physical Properties:

    Density (lb / cu. in.) 0.283
    Specific Gravity 7.8
    Specific Heat (Btu/lb/Deg F – [32-212 Deg F]) 0.1
    Melting Point (Deg F) 2600
    Thermal Conductivity 26
    Mean Coeff Thermal Expansion 6.6
    Modulus of Elasticity Tension 31

    • 8620 Steel Mechanical Properties

    Properties Metric Imperial
    Tensile strength 530 MPa 76900 psi
    Yield strength 385 MPa 55800 psi
    Elastic modulus 190-210 GPa 27557-30458 ksi
    Bulk modulus (typical for steel) 140 GPa 20300 ksi
    Shear modulus (typical for steel) 80 GPa 11600 ksi
    Poisson’s ratio 0.27-0.30 0.27-0.30
    Izod Impact 115 J 84.8 ft.lb
    Hardness, Brinell 149 149
    Hardness, Knoop (converted from Brinell hardness) 169 169
    Hardness, Rockwell B (converted from Brinell hardness) 80 80
    Hardness, Vickers (converted from Brinell hardness) 155 155
    Machinability (hot rolled and cold drawn, based on 100 machinability for AISI 1212 steel) 65 65

    5. Forging of Material 8620 Steel

    AISI

    8620 alloy steel is forged at a start temperature of around 2250ºF
    (1230ºC) down to approximately 1700ºF(925ºC.) prior to the hardening
    heat treatment or carburizing. The alloy is air cooled after forging.

    6. ASTM 8620 Steel Heat Treatment

    • Annealing

    AISI

    8620 steel may be given a full anneal by heat to 820℃ – 850℃, and hold
    until temperature is uniform throughout the section and cool in furnace
    or air cooled.

    • Tempering

    Tempering

    of heat treated and water quenched parts of 8620 steels (not
    carburized) is done at 400 F to 1300 F to improve case toughness with
    minimal effect on its hardness. This will also reduce the possibility of

    grinding cracks.

    • Hardening

    The

    AISI steel 8620 will be austenitized at around 840°C – 870°C, and oil
    or water quenched depending upon section size and intricacy. Cool in Air

    or Oil required.

    • Normalizing

    1675ºF

    (910ºC) and air cool. This is another method of improving machinability

    in 8620 material; normalizing might also be used prior to case
    hardening.

    7. Machinability of SAE 8620 Steel

    The

    8620 alloy steel is readily machined after heat treatment and/or
    carburizing, should be at a minimum so as not to impair the hardened
    case of the part. Machining may be done by conventional means prior to
    heat treatment – after carburizing machining is usually limited to
    grinding.

    8. Welding of 8620 Materials

    The
    alloy 8620 may be welded as rolled condition by conventional methods,
    usually gas or arc welding. Preheating at 400 F is beneficial and
    subsequent heating after welding is recommended – consult the approved
    weld procedure for the method used. However, welding in the case
    hardened or through hardened condition is not recommended

    9. Application of ASTM 8620 Steel

    AISI

    8620 steel material is used extensively by all industry sectors for
    light to medium stressed components and shafts requiring high surface
    wear resistance with reasonable core strength and impact properties.

    Typical

    applications are: Arbors, Bearings, Bushings, Cam Shafts, Differential
    Pinions, Guide Pins, King Pins, Pistons Pins, Gears, Splined Shafts,
    Ratchets, Sleeves and other applications where it is helpful to have a
    steel that can be readily machined and carburized to controlled case
    depths.

  • Previous:
  • Next:



  • STRN103 fall 2013 (Engineering materials)
    Lab demonstration
    Tension test on a mild steel bar



    Like a cassette stove, I tried to make a small rocket stove with a portable property that it is easy to ignite and extinguish and can be easily used outdoors regardless of the season.

    It was not exaggeration of the moment of bliss, but I wanted to taste a certain amount of enjoyment, such as brewing coffee in the garden or steaming the potatoes · I made it small.

    * Combustion version will be uploaded at a later date.

    · Of course, in emergencies it will be of great help as a thermal energy source.
    * Naming taken from the appearance like a fire hydrant: Please see how to make fire man.

    * Combustion → Extinguishment → Movie of cleanup is planned to be up soon.

    * Twig shoot bamboo is fuel (energy) = small diameter:
    I think that you can pick up a number of Shinkotake and twigs in the surrounding forests and dry it, and enjoy using it as a fuel to boil water or cook easily.
    · It is ideal that it keeps burning in the time according to the necessity with the smallest possible flame (it is unexpected that it will be used for a long time by burning fire gun).

    * Easy way of making:
    Just connect the water pipe to the “T” with a fitting and the rocket stove prototype is completed.
    Next, fill the holes above and below the large coffee cans, insert the insulation through the tubes and close them with heat resistant putty.
    Drilling the lid and the ash receiver etc into empty cans work.

    * Measures against wind, Extinguishing with water → Easy cleanup:
    Most of the rocket stove seems to have little consideration for fire fighting, but when you actually use it, you will feel “uneasy about the wind that builds up during burning”, ” Handling of heat “may take time and may be troublesome.
    However, since the rocket stoves using water pipes can be extinguished easily by putting in water, it is also possible to cool the heat promptly.
    In addition, burning residue is discharged together with water.

    · Measures to strengthen the wind:
    When the wind is strengthened during burning, it is possible to seal the rocket stove (although there is a word) by closing the mouth of each pipe exactly with empty cans.

    * High material cost? :
    Steel pipes that are also used for water pipes are thick, so they are no problem for quenching with water, and they will not last for 10 years and 20 years without worry of pain due to high temperature or corrosion due to rust.
    · “Lid / ash receiver” made from empty cans is regarded as “consumable material”, and it is made on the premise that it will be damaged by using it.

    Thank you for your viewing for a long time.
    It would be greatly appreciated if you could make a rocket stove of everyone and serve as a relaxing time with a rocket stove.

    Creative silver studio Otanko Nasu!

    http://craftsman-na.com/silver-works/

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Tree

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the House