New Delivery for AISI 4340 Steel | 36CrNiMo4 | 1.6511 | EN24 | 817M40 | SNCM439 Factory from Venezuela

New Delivery for
 AISI 4340 Steel | 36CrNiMo4 | 1.6511 | EN24 | 817M40 | SNCM439 Factory from Venezuela

Short Description:

AISI 4340 steel is a medium carbon, low alloy steel known for its toughness andstrength in relatively large sections. AISI 4340 is also one kind ofnickel chromium molybdenum steels. 4340 alloy steel is generallysupplied hardened and tempered in the tensile range of 930 – 1080 Mpa.Pre hardened and tempered 4340 steels can be further surface hardened by flame or induction hardening and by nitriding. The 4340 steel has goodshock and impact resistance as well as wear and abrasion resistanc...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    we can offer high quality products, competitive price and best customer service. Our destination is "You come here with difficulty and we give you a smile to take away" for New Delivery for AISI 4340 Steel | 36CrNiMo4 | 1.6511 | EN24 | 817M40 | SNCM439 Factory from Venezuela, "Create Values,Serving Customer!" is the aim we pursue. We sincerely hope that all customers will establish long term and mutually beneficial cooperation with us.If you wish to get more details about our company, Please contact with us now


    AISI 4340 steel
    is a medium carbon, low alloy steel known for its toughness and
    strength in relatively large sections. AISI 4340 is also one kind of
    nickel chromium molybdenum steels. 4340 alloy steel is generally
    supplied hardened and tempered in the tensile range of 930 – 1080 Mpa.
    Pre hardened and tempered 4340 steels can be further surface hardened by
    flame or induction hardening and by nitriding. The 4340 steel has good
    shock and impact resistance as well as wear and abrasion resistance in
    the hardened condition. AISI 4340 steel properties offer good ductility
    in the annealed condition, allowing it to be bent or formed. Fusion and
    resistance welding is also possible with our 4340 alloy steel. ASTM 4340
    material is often utilized where other alloy steels do not have the
    hardenability to give the strength required. For highly stressed parts
    it is excellent choice. AISI 4340 alloy steel can also be machined by
    all customary methods.

    Due to availability the ASTM 4340 grade steel is often substituted
    with European based standards 817M40/EN24 and 1.6511/36CrNiMo4 or Japan
    based SNCM439 steel. You have the detailed data of 4340 steel below.

    1. AISI 4340 Steel Specification and Relevant Standards

    Country USA Britain Britain Japan
    Standard ASTM A29 EN 10250 BS 970 JIS G4103
    Grades 4340 36CrNiMo4/
    1.6511
    EN24/817M40 SNCM 439/SNCM8

    2. ASTM 4340 Steels And Equilvalents Chemical Composition

    Standard Grade C Mn P S Si Ni Cr Mo
    ASTM A29 4340 0.38-0.43 0.60-0.80 0.035 0.040 0.15-0.35 1.65-2.00 0.70-0.90 0.20-0.30
    EN 10250 36CrNiMo4/
    1.6511
    0.32-0.40 0.50-0.80 0.035 0.035 ≦0.40 0.90-1.20 0.90-1.2 0.15-0.30
    BS 970 EN24/817M40 0.36-0.44 0.45-0.70 0.035 0.040 0.1-0.40 1.00-1.40 0.20-0.35
    JIS G4103 SNCM 439/SNCM8 0.36-0.43 0.60-0.90 0.030 0.030 0.15-0.35 1.60-2.00 0.60-1.00 0.15-0.30

    3. AISI Alloy 4140 Steel Mechanical Properties

    Mechannical Properties

    (Heat Treated Condition )

    Condition Ruling section
    mm
    Tensile Strength MPa Yield Strength
    MPa
    Elong.
    %
    Izod Impact
    J
    Brinell
    Hardness
    T 250 850-1000 635 13 40 248-302
    T 150 850-1000 665 13 54 248-302
    U 100 930-1080 740 12 47 269-331
    V 63 1000-1150 835 12 47 293-352
    W 30 1080-1230 925 11 41 311-375
    X 30 1150-1300 1005 10 34 341-401
    Y 30 1230-1380 1080 10 24 363-429
    Z 30 1555- 1125 5 10 444-

    Thermal Properties

    Properties Metric Imperial
    Thermal expansion co-efficient (20°C/68°F, specimen oil hardened, 600°C (1110°F) temper 12.3 µm/m°C 6.83 µin/in°F
    Thermal conductivity (typical steel) 44.5 W/mK 309 BTU in/hr.ft².°F

    4. Forging of 4340 Alloy Steel

    Preheat
    the steel 4340 first, heat up to 1150°C – 1200°C maximum for forging,
    hold until temperature is uniform throughout the section.

    Do not forge
    below 850 °C. 4340 has good forging characteristics but care must be
    taken when cooling as the steel shows susceptibility to cracking.
    Following forging operation the work piece should be cooled as slowly as
    possible. And cooling in in sand or dry lime is recommended etc.

    5. AISI 4340 Steel Grade Heat Treatment

    • Stress Relieving

    For
    pre-hardened steel stress relieving is achieved by heating steel 4340
    to between 500 to 550°C. Heat to 600 °C – 650 °C, hold until temperature
    is uniform throughout the section, soak for 1 hour per 25 mm section,
    and cool in still air.

    • Annealing

    A
    full anneal may be done at 844°C (1550 F) followed by controlled
    (furnace) cooling at a rate not faster than 10°C (50 F) per hour down to
    315°C (600 F). From 315°C 600 F it may be air cooled.

    • Tempering

    AISI
    4340 alloy steel should be in the heat treated or normalized and heat
    treated condition before tempering. The tempering temperature for
    depends upon the strength level desired. For strength levels in the 260 –
    280 ksi range temper at 232°C (450 F). For strength in the 125 – 200
    ksi range temper at 510°C (950 F). And don’t temper the 4340 steels if
    it is in the 220 – 260 ksi strength range as tempering can result in
    degradation of impact resistance for this level of strength.

    Tempering should be avoided if possible within the range 250 °C – 450 °C due to temper brittleness.

    • Flame or Induction Hardening

    As mentioned above, pre-hardened and tempered 4340 steel bars or plates can be further surface hardened by either the flame or induction hardening
    methods resulting in a case hardness in excess of Rc 50. AISI 4340
    steel parts should be heated as quickly as possible to the austenitic
    temperature range (830 °C – 860 °C) and required case depth followed by
    an immediate oil or water quenching, depending upon hardness required,
    workpiece size/shape and quenching arrangements.

    Following
    quenching to hand warm, tempering at 150°C – 200°C will reduce stresses
    in the case with minimal effect on its hardness.

    All de-carburised surface material must first be removed to ensure best results.

    • Nitriding

    Hardened
    and tempered 4340 alloy steel can also be nitrided, giving a surface
    hardness of up to Rc 60. Heat to 500°C – 530°C and hold for sufficient
    time (from 10 to 60 hours) to develop the depth of case. Nitriding
    should be followed by slow cooling (no quench) reducing the problem of
    distortion. The nitrided grade 4340 materials can therefore be machined
    to near final size, leaving a small grinding allowance only. The tensile
    strength of the 4340 steel material core is usually not affected since
    the nitriding temperature range is generally below the original
    tempering temperature employed.

    Surface hardness achievable is 600 to 650HV.

    6. Machinability

    Machining
    is best done with the alloy steel 4340 in the annealed or normalized
    and tempered condition. It can be readily machined by all conventional
    methods such as sawing, turning, drilling etc. However in the high
    strength conditions of 200 ksi or greater the machinability is only from
    25% to 10% that of the alloy in the annealed condition.

    7. Welding

    Welding
    of steel 4340 in the hardened and tempered condition (as normally
    supplied), is not recommended and should be avoided if at all possible,
    because of the danger of quench cracking, as the mechanical properties
    will be altered within the weld heat affected zone.

    If welding
    must be carried out, pre-heat to 200 to 300°C and maintain this while
    welding. Immediately after welding stress relieve at 550 to 650°C, prior
    to hardening and tempering.

    If welding in the hardened and
    tempered condition is really necessary, then the work piece, immediately
    on cooling to hand warm, should be if possible stress relieved at 15 °C
    below the original tempering temperature.

    8. Application of 4340 Steel

    AISI
    4340 steel is used in most industry sectors for applications requiring
    higher tensile/yield strength than 4140 steel can provide.

    Some typical applications such as:

    • Aircraft Landing Gear

    • Automotive,

    • Oil and Gas Drilling,

    • Forging,

    • Warm and Cold Forming,

    • Machine Building,

    • Transfer Systems, like power transmission gears and shafts.

    • General
      engineering industries and structural use applications, such as: heavy
      duty shafts, gears, axles, spindles, couplings, pins, chucks, molds etc.

  • Previous:
  • Next:



  • http://www.DKCKnives.com
    paul@dkcknives.com

    Damascus Folding Knife Damascus Hunting Knife Damascus Bowie Knife Best Survival Knife Groomsmen Gifts Tanto Hunting Knife Tactical Knife

    Knives Come With A Sheath Custom High Quality Double Layers of Hard Genuine Leather. The leather is water proof and has double layers inside. The leather we used to make sheath is Camel, Goat and Buffalo. The leather has been treated with extra process to get the natural looks of snake, alligator, leopard, skins etc, and we tried to matches each sheath cover with the knife handle. Extra work is done on the leather sheath cover to make it colorful, unique and beautiful.
    Collectors Knife Feels Great In Your Hand and Pocket ! Great For Personal Use, Or A Fine Gift DKC KNIVES TM..The Collection You Will Be Proud Of
    Over 320 Layers, 15N20 & 1095 Damascus Mixture of steel and high, low Carbon and HRC approximately 50 to 60. The knife blade is 100% hand forged and is the results of hours of work. The Damascus steel used for this knife was created by forge welding multiple layers of 15N20 & 1095 steel into a solid billet. Heat Treatment: Excellent heat treatment to blade/ oil quenched. Our craftsman use heat treatment and oil quenching to create a perfect blade. The billet of the blade is forged, welded and hand hammered several times and dipped in the motel salt to get the unique patterns.
    To make a custom hand made knife is a skillful art that requires hard work and careful attention. This marvelous knife is very impressive due to its excellent design & detail. We take great pride when designing our knives. The knife is well balanced and has an excellent grip, creating a natural weight and feel when held. Our craftsman put extra work in each knife by carefully designing, carving and hand making it into a breathtaking work of art. There may be slight variations in finish, colors, etc. because they are hand made and variations in natural materials. You are purchasing a knife that will give you many years of great service as well as provide a family heirloom that you can hand down to family members. Please see our full line of knives…we have a fast growing base of knife collectors that eagerly wait for new knife releases. Buy two or three different model DKC KnivesTM and you will see. Our knives are value priced and compare to other custom knives costing two to five times the amount we sell our knives for. Since knives are one of those areas where its possible for fake copies to be made, please be sure to purchase only from SAN FRANCISCO SUPPLY the only authorized factory reseller of DKC Knives. In addition, starting January 1, 2015 most of our knives will have a DKCTM engraving. Look for factory information in your box about knife care. Knives are well boxed, and typically arrive wrapped in plastic with a good coat of oil to protect the knife. When you receive your knife, take a soft cloth and clean off the knife..but as with all steel knives..keep it well oiled to preserve function, look, and beauty. Knives are for responsible adults only. You must be 18 Years or older to purchase this knife. While all our knives are field quality, we do not support or advocate the use of knives for any type of violent activity. We look forward to having you as a long term customer and thanks for purchasing a fine quality knife. THANKS FROM DKC KNIVES !



    Check out how to watch the special concert on your computer or mobile device.
    Concert Zone Site Will air an Julien Baker Special Show Perfomance at Brooklyn Steel, Brooklyn, NY, US
    You must be logged in to continue streaming.
    Live On :::: http://today.live4stream.com/Julien-Baker-at-Brooklyn-Steel,-Brooklyn,-NY,-US-April-19-2017-/tq-Bp_2FOGA (Live stream will be available after Login)

    Julien Baker Brooklyn Steel, Brooklyn, NY, US April 19 2017
    Julien Baker Concert review and setlist
    watch Julien Baker in Brooklyn Steel, Brooklyn, NY, US Live stream airs Tonight Online
    Julien Baker Concert in Brooklyn Steel, Brooklyn, NY, US April 19 2017
    Missed Julien Baker Concert?? , is now available to stream full.
    Exclusive Julien Baker LIVE 2017 – Show – Live at Brooklyn Steel, Brooklyn, NY, US .
    Julien Baker LIVE 2017 Brooklyn Steel, Brooklyn, NY, US – April 19 2017 at Brooklyn Steel, Brooklyn, NY, US
    Global Superstar Julien Baker Will visit Brooklyn Steel, Brooklyn, NY, US For the Tour Concert in April 19 2017
    Watch Julien Baker Live 2017 streaming at Brooklyn Steel, Brooklyn, NY, US for April 19 2017
    Julien Baker Ticket Now available on ConcertZone , Worlds largest live streaming concert online
    Live concertZone can now confirm that Julien Baker will concert at Brooklyn Steel, Brooklyn, NY, US on April 19 2017
    Get the Julien Baker setlist of the concert at Brooklyn Steel, Brooklyn, NY, US on April 19 2017

    Facebook: https://www.facebook.com/
    Twitter: https://twitter.com/
    Instagram: http://instagram.com/
    ====================================
    En Vivo | Ao Vivo | In Direct
    ———-Thanks you—————

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Flag

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Plane