Manufacturer for D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory for Jakarta

Manufacturer for D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory for Jakarta

Short Description:

1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade D2 ...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    We are experienced manufacturer. Wining the majority of the crucial certifications of its market for Manufacturer for D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory for Jakarta, As we are moving forward, we keep an eye on our ever-expanding product range and make improvement to our services.


    1. Relevant D2 Steel Specifications

    Country USA German Japan
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404
    Grades D2 1.2379/X153CrMo12 SKD11

    2. D2 Tool Steel Chemical Composition

    ASTM A681 C Mn P S Si Cr V Mo
    D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2
    DIN ISO 4957 C Mn P S Si Cr V Mo
    1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1
    JIS G4404 C Mn P S Si Cr V Mo
    SKD11 1.4 1.6
    0.6 0.03 0.03
    0.4 11 13 0.2 0.5 0.8 1.2

    3. AISI Grade D2 Steel Mechanical Properties

    Mechanical Properties Metric Imperial
    Hardness, Knoop (converted from Rockwell C hardness) 769 769
    Hardness, Rockwell C 62 62
    Hardness, Vickers 748 748
    Izod impact unnotched 77.0 J 56.8 ft-lb
    Poisson’s ratio 0.27-0.30 0.27-0.30
    Elastic modulus 190-210 GPa 27557-30457 ksi

    Thermal Properties

    Properties

    Conditions

    T (°C)

    Treatment

    Thermal expansion 10.4 x 10-6/oC 20-100

    4. AISI/ASTM A681 D2 Grade Steel Forging

    Heating for forging of AISI D2 tool steel should
    be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
    as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
    die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
    should always be annealed after forging.

    5. D2 Tool Steel Heat Treatment

      Heat Treatment

      ASTM D2 steels alloy should be preheated very slowly to 815oC (1500oF) and then temperature can be increased to 1010oC (1850oF). They are then held at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).

        Annealing

        Annealing of D2 tool steels material should be done at 871 to 898oC (1600 to 1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or less.after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.

          Stress Relieving

          When desirable to relieve the strains of machining, heat D2 grade steel slowly to 1050°-1250°F, allow to equalize, and then cool in still air (Strain Relieving).

            Preheat Prior To Hardening

            Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.

              Hardening

              After thorough preheating, heat to 1800°-1850°F. Hold the work piece at the hardening temperature until it is completely and uniformly heated.

                Quenching

                AISI D2 steel tool material is an air hardening steel and will develop hardness on cooling in still air. To avoid scaling and prevent decarburization of the work piece surface, controlled atmosphere or vacuum furnaces are recommended. If these furnaces are not available, pack hardening, salt baths or wrapping the piece in stainless steel foil will provide some degree of surface protection in the hardening process. Parts should be allowed to cool to 150F, or to where they can be held in the bare hand, and then temper immediately.

                  Tempering

                  The tempering temperature on material D2 steel may be varied according to the desired hardness. D2 steels can be tempered at 204oC (400oF) for achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell C hardness of 54.

                  6. D2 Tool Steel Material Application
                  AISI grade D2 tool steels are used for long run tooling applications, where wear resistance is important, such as blanking or forming dies and thread rolling dies.

                  Some main applications for D2 tool steel are as below:

                  Blanking Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls, Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear Parts.

                  We usually hold D2 tool steel on sale activities, and you would have our price on regular schedule. Contact us and sign in our newsletter to have D2 tool steel materials price list and commercial quote today.


                • Previous:
                • Next:



  • “FD Grip” The No.1 earthquake-resistant rebar coupler in Japan, the highest seismic country, for over 30 years.

    http://www.fujibolt.com



    http://www.spainmadesimple.com/costa-blanca/benidorm/webcams/

    The centre of attraction for all the bars is the area known as The English Square. The end of the evening will see the older crowd in Sinatras, with most people ending up at Cafe Benidorm which is a place known for pulling, chatting up and flirting. Opposite is Champions bar which is also popular with the bull riding on the outside terrace. The younger crowd will prefer Bahamas, Beachcomber and the Hippodrome.

    Generally we have to say Benidorm nightlife is on the whole very safe, with most revellers just intent on drinking a lot and having a good laugh and good time but we have witnessed the occasional fight – and always in this English square area, just outside CafeB. Be also careful and alert when stumbling home, there are pickpockets and Romanian/Eastern European gypsies who surround you and basically mug you when you are drunk.

    This area is known as ‘The Square‘ and the night goes on until the sun comes up at dawn. To get to the Square head for Avenida Mallorca where it meets Calle Gerona. To stay in this area consider the Hotel Orange, Rio Park Hotel, Hotel Pueblo or the Hotel Venus.

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Plane

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Heart