Manufactur standard D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Supply to Germany
1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade...
The company upholds the philosophy of "Be No.1 in quality, be rooted on credit and trustworthiness for growth", will continue to serve old and new customers from home and overseas whole-heatedly for Manufactur standard D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Supply to Germany, We welcome customers, business associations and friends from all parts of the world to contact us and seek cooperation for mutual benefits.
1. Relevant D2 Steel Specifications
|Standard||ASTM A681||DIN EN ISO 4957||JIS G4404|
2. D2 Tool Steel Chemical Composition
|DIN ISO 4957||C||Mn||P||S||Si||Cr||V||Mo|
3. AISI Grade D2 Steel Mechanical Properties
|Hardness, Knoop (converted from Rockwell C hardness)||769||769|
|Hardness, Rockwell C||62||62|
|Izod impact unnotched||77.0 J||56.8 ft-lb|
|Elastic modulus||190-210 GPa||27557-30457 ksi|
|Thermal expansion||10.4 x 10-6/ºC||20-100||
4. AISI/ASTM A681 D2 Grade Steel Forging
Heating for forging of AISI D2 tool steel should
be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
should always be annealed after forging.
5. D2 Tool Steel Heat Treatment
ASTM D2 steels alloy should be preheated very slowly to 815oC (1500oF) and then temperature can be increased to 1010oC (1850oF). They are then held at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).
Annealing of D2 tool steels material should be done at 871 to 898oC (1600 to 1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or less.after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.
When desirable to relieve the strains of machining, heat D2 grade steel slowly to 1050°-1250°F, allow to equalize, and then cool in still air (Strain Relieving).
Preheat Prior To Hardening
Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.
After thorough preheating, heat to 1800°-1850°F. Hold the work piece at the hardening temperature until it is completely and uniformly heated.
AISI D2 steel tool material is an air hardening steel and will develop hardness on cooling in still air. To avoid scaling and prevent decarburization of the work piece surface, controlled atmosphere or vacuum furnaces are recommended. If these furnaces are not available, pack hardening, salt baths or wrapping the piece in stainless steel foil will provide some degree of surface protection in the hardening process. Parts should be allowed to cool to 150F, or to where they can be held in the bare hand, and then temper immediately.
The tempering temperature on material D2 steel may be varied according to the desired hardness. D2 steels can be tempered at 204oC (400oF) for achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell C hardness of 54.
6. D2 Tool Steel Material Application
AISI grade D2 tool steels are used for long run tooling applications, where wear resistance is important, such as blanking or forming dies and thread rolling dies.
Some main applications for D2 tool steel are as below:
Blanking Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls, Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear Parts.
We usually hold D2 tool steel on sale activities, and you would have our price on regular schedule. Contact us and sign in our newsletter to have D2 tool steel materials price list and commercial quote today.
GM OE cables contain numerous key attributes to be certain they meet the in good shape, sort and functionality of the at first mounted aspect these kinds of as manufacturing facility crimp copper alloy cable terminals , coated terminal connections and abrasion resistant exterior insulation.
http://www.acdelco.com/automobile-sections/wire-and-cable.html – Learn extra about Wires & Cables
http://www.acdelco.com/automobile-sections-retail outlet-locator.html - Identify a Parts Retail Store
http://www.acdelco.com/automobile-restore-provider-center-locator.html - Locate a Professional Provider Centre
surface drainage systems – The future of Plumbing and Stainless Grates!
Our Website: http://www.paigestainless.com.au/click-drain/
Google Business Page: https://plus.google.com/+PaigestainlessAustralia
See our product at 0:59
CLICK DRAIN™ developed using PAIGE STAINLESS HEELGUARD® has developed a full stainless steel drainage system using this centuries technology for ease of onsite fitting.
This patented product enables both builders and plumbers to basically style the drain on site as required, its clever and unique `click` together system has out let sections, joiner sections, change of direction sections and stop ends to create a drain for all site requirements.”
No one else has actually manufactured Heelguard to the Architectural Market for over Twenty Years to the Australian Design Requirement.
Monday-Friday: 9:00am – 5:00pm
YOU COULD REACH US THROUGH:
27 Cessna Drive, Caboolture QLD 4510, Australia
Tel: + 61 7 5499 1511
Fax: +617 5499 0741
Linear Surface Water Drainage
Platforms and Decks
FULL CUSTOM SYSTEMS ARE OUR SPECIALTY.