Low MOQ for H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel Factory from India

Low MOQ for
 H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel Factory from India

Short Description:

H13 Tool Steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications. H13 tool steel is classified as group H steels by the AISI classification system. This series of steels start from H1 to H19. AISI H-13 tool steel is characterized by: Good resistance to abrasion at both low and high temperatures High level of toughness and ductility Uniform and high level of machinability and polishability Good high-temperature strength and resistance to t...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    We are proud of the high customer satisfaction and wide acceptance due to our persistent pursuit of high quality both on product and service for Low MOQ for H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel Factory from India, We are sincerely welcome good friends from numerous circles at dwelling and abroad come to cooperate!


    H13 Tool Steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications. H13 tool steel is classified as group H steels by the AISI classification system. This series of steels start from H1 to H19.

    AISI H-13 tool steel is characterized by:

    • Good resistance to abrasion at both low and high temperatures

    • High level of toughness and ductility

    • Uniform and high level of machinability and polishability

    • Good high-temperature strength and resistance to thermal fatigue

    • Excellent through-hardening properties

    • Very limited distortion during hardening

    In
    steel H13, the molybdenum and vanadium act as strengthening agents. The
    chromium content assists die steel H-13 to resist softening when used
    at high temperatures. H-13 die steels offers an excellent combination of
    shock and abrasion resistance, and possesses good red hardness. It is
    capable of withstanding rapid cooling and resists premature heat
    checking. Tool Steel H13 has good machinability, good weldability, good
    ductility, and can be formed by conventional means.

    Due to H13
    tool steel excellent combination of high toughness and fatigue
    resistance, AISI H13 hot work tool steel is used more than any other
    tool steel in tooling applications.

    1. Common H13 Tool Steel Related Specifications

    Country USA German Japan
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404
    Grades H13 1.2344/X40CrMoV5-1 SKD61

    2. H13 Tool Steel Chemical Composition

    ASTM A681 C Mn P S Si Cr V Mo
    H13 0.32 0.45 0.2 0.6 0.03 0.03 0.8 1.25 4.75 5.5 0.8 1.2 1.1 1.75
    DIN ISO 4957 C Mn P S Si Cr V Mo
    1.2344 /X40CrMoV5-1 0.35 0.42 0.25 0.5 0.03 0.02 0.8 1.2 4.8 5.5 0.85 1.15 1.1 1.5
    JIS G4404 C Mn P S Si Cr V Mo
    SKD61 0.35 0.42 0.25 0.5 0.03 0.02 0.8 1.2 4.8 5.5 0.8 1.15 1.0 1.5

    3. AISI H13 Steel Mechanical Properties

    Properties

    Metric Imperial
    Tensile strength, ultimate (@20°C/68°F, varies with heat treatment) 1200 – 1590 MPa 174000 – 231000 psi
    Tensile strength, yield (@20°C/68°F, varies with heat treatment) 1000 – 1380 MPa 145000 – 200000 psi
    Reduction of area (@20°C/68°F) 50.00% 50.00%
    Modulus of elasticity (@20°C/68°F) 215 GPa 31200 ksi
    Poisson’s ratio 0.27-0.30 0.27-0.30

    4. Forging of H13 Tool Steel
    Heating for forging must be done slowly and uniformly. Soak through at
    1900°-2000°F and reheat as often as necessary, stopping work when the
    temperature drops below 1650°F. After forging, cool slowly in lime,
    mica, dry ashes or furnace. H-13 should always be annealed after
    forging.

    5. Heat Treatment for H13 Tool Steels

    • Annealing

    Heat
    slowly to 1550°-1650°F, hold until entire mass is heated through, and
    cool slowly in the furnace (40F per hour) to about 1000°F, after which
    cooling rate may be increased. Suitable precautions must be taken to
    prevent excessive carburization or decarburization.

    • Stress Relieving

    When
    desirable to relieve the strains of machining, heat slowly to
    1050°-1250°F, allow to equalize, and then cool in still air (Strain
    Relieving). Â

    • Preheat Prior to Hardening

    Warm slightly before charging into the preheat furnace, which should be operating at 1400°-1500°F.

    • Hardening

    H13
    tool steel is a steel having very high hardenability and should be
    hardened by cooling in still air. The use of a salt bath or controlled
    atmosphere furnace is desirable to minimize decarburization, and if not
    available, pack hardening in spent pitch coke is suggested. The
    temperature employed is usually 1800°-1850°F, depending on size section.

    • Quenching

    Quench
    in still air or dry air blast. If complicated forms are to be hardened,
    an interrupted oil quench can be used. Quench part in oil and remove
    from bath when it just loses its color (1000°-1100°F). Finish cooling to
    below 150°-125°F in air, then temper immediately.

    • Tempering

    Tempering
    practice may vary with size and application, but is usually performed
    in the range of maximum secondary hardness or higher. Double tempering
    is recommended. The results below is H13 that was air quenched from
    1800°F and tempered for 4 hours at various temperatures. The results may
    be used as a guide, keeping in mind that parts of heavy section or mass
    may be several points lower in hardness.

    6. Application of AISI H13 Tool Steel

    • As Tools for Extrusion

    Part Aluminium, mag­nesium alloys, HRC Copper al­loys HRC Stainless steel HRC
    Dies, Backers, die-holders, liners, dummy blocks, stems 44-50 43-47 45-50
    41-50 40-48 40-48

    Austenitizing temperature

    1,870-1,885°F 1,900-1,920°F
    (1,020-1,030°C) (1,040-1,050°C)
    • As Plastic Molding Tool Steel

    Part Austenitizing temp. HRC
    Injection molds Compression/ transfer molds 1,870-1,885°F (1,020-1,030°C) 50-52
    Tempering 480°F (250°C)
    • Other Applications

    Applications Austenitizing temp HRC
    Severe cold punching, scrap shears 1,870-1,885°F 50-52
    (1,020-1,030°C)
    Tempering 480°F (250°C)
    Hot shearing 1,870-1,885°F
    (1,020-1,030°C) 50-52
    Tempering 480°F (250°C) or
    1,070-1,110°F 45-50
    (575-600°C)
    Shrink rings (e.g. for cemented carbide dies) 1,870-1,885°F 45-50
    (1,020-1,030°C)
    Tempering 1,070-1,110°F
    (575–600°C)
    Wear-resisting parts 1,870-1,885°F Core
    50-52
    Surface
    ~1000HV1
    (1,020-1,030°C)
    Tempering 1,070°F (575°C)
    nitrided

     

    If
    there are any queries about AISI H13 tool steel for hot working
    applications, please feel free to leave a comment below. And welcome
    enquiry of AISI H13 tool steel, we are professional and reliable
    supplier  for prime H13 tool steel materials.

  • Previous:
  • Next:



  • Walter Drill Bits Drill Though Rounded Hardened Impact Steel With A Cordless Hand Drill. www.Walter.com
    Twist Drilling Walter Surface Technologies High Speed Steel (HSS) drill bits set the standards for efficiency. With self-centering split-points, high flow spiral design for quick chip evacuation, heavy duty, fully ground body construction, it is easy to see why Walter twist drilling products are one of the best! Available in a variety of length, sizes, shanks and fluting, Walter offers a breadth of state-of-the art drill bits for all your needs.

    https://www.walter.com/products/tooling/twist-drilling/sst-plus-drill-bits

    Spring Steel is Rockwell Hardness C 41-60
    Please Click The Subscribe Button Below And Share Video With G+, Facebook, Twitter and all Your Favorite Social Media!
    Comments and questions are encouraged but please be respectful.
    Visit http://wayneslockshop.com/ For More tips and tricks for the Locksmith Industry

    http://tricountylocksmithservice.com/

    All views and opinions are the alleged interaction with any product shown and not a fact stated by Wayne Winton and orTriCounty Locksmith Service. The information shown in any video is 100% opinion of Wayne Winton and protected by the 1st amendment, the freedom of speech. Some products may be provided by the company being reviewed and others are purchased independently by Wayne Winton, Tri County Locksmith Service. Either way it does not reflect the content of the review. All products are given a fair equal chance to perform. All videos are property of Wayne Winton and all rights are reserved. If you would like to post any video please contact Wayne Winton at: Tricountylocksmithservice@gmail.com for permission.
    Disclaimer: Do not try this at home! Any content seen here is for entertainment only! Do Not try anything seen here yourself or there may be danger of bodily harm or legal consequences for your actions! Any illegal activity is prohibited and Wayne Winton and or Tri County Locksmith Service are not responsible for your actions!
    Wayne Winton, © 2014. All rights reserved. Publication, reproduction or distribution of this film by any means whatsoever – including without limitation electronic transmission via internet or e-mail, or re-uploading existing videos & re-uploading such material on any website anywhere in the world — is strictly prohibited without the prior written consent of Wayne Winton. Please note that Wayne Winton, Tri County Locksmith Service does not state any confirmed facts only personal opinions. I am not directly affiliated with any of the vendors or manufacturers in this video. Wayne Winton, Tri County Locksmith Service is not liable for any damage or loss through the use of products or techniques shown – Use at your own risk! This film and the Wayne Winton, Tri County Locksmith Service film series broadcast on YouTube is intended for entertainment purposes only.
    Tri County Locksmith Service



    With the Summer Slam Dance Championship only week away, the girls feel extra pressure to show off their talents and prove to Miss D that they have what it takes to be captain of the team next season.

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Plane

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Star