Hot-selling attractive price H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel in Karachi

Hot-selling attractive price
 H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel in Karachi

Short Description:

H13 Tool Steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications. H13 tool steel is classified as group H steels by the AISI classification system. This series of steels start from H1 to H19. AISI H-13 tool steel is characterized by: Good resistance to abrasion at both low and high temperatures High level of toughness and ductility Uniform and high level of machinability and polishability Good high-temperature strength and resistance to t...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    We always stick to the principle "Quality First, Prestige Supreme". We are fully committed to providing our clients with competitively priced quality products, prompt delivery and professional service for Hot-selling attractive price H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel in Karachi, we have built a reliable reputation among many customers. Quality&customer first are always our constant pursuit. We spare no efforts to make better products. Look forward to long-term cooperation and mutual benefits!


    H13 Tool Steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications. H13 tool steel is classified as group H steels by the AISI classification system. This series of steels start from H1 to H19.

    AISI H-13 tool steel is characterized by:

    • Good resistance to abrasion at both low and high temperatures

    • High level of toughness and ductility

    • Uniform and high level of machinability and polishability

    • Good high-temperature strength and resistance to thermal fatigue

    • Excellent through-hardening properties

    • Very limited distortion during hardening

    In
    steel H13, the molybdenum and vanadium act as strengthening agents. The
    chromium content assists die steel H-13 to resist softening when used
    at high temperatures. H-13 die steels offers an excellent combination of
    shock and abrasion resistance, and possesses good red hardness. It is
    capable of withstanding rapid cooling and resists premature heat
    checking. Tool Steel H13 has good machinability, good weldability, good
    ductility, and can be formed by conventional means.

    Due to H13
    tool steel excellent combination of high toughness and fatigue
    resistance, AISI H13 hot work tool steel is used more than any other
    tool steel in tooling applications.

    1. Common H13 Tool Steel Related Specifications

    Country USA German Japan
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404
    Grades H13 1.2344/X40CrMoV5-1 SKD61

    2. H13 Tool Steel Chemical Composition

    ASTM A681 C Mn P S Si Cr V Mo
    H13 0.32 0.45 0.2 0.6 0.03 0.03 0.8 1.25 4.75 5.5 0.8 1.2 1.1 1.75
    DIN ISO 4957 C Mn P S Si Cr V Mo
    1.2344 /X40CrMoV5-1 0.35 0.42 0.25 0.5 0.03 0.02 0.8 1.2 4.8 5.5 0.85 1.15 1.1 1.5
    JIS G4404 C Mn P S Si Cr V Mo
    SKD61 0.35 0.42 0.25 0.5 0.03 0.02 0.8 1.2 4.8 5.5 0.8 1.15 1.0 1.5

    3. AISI H13 Steel Mechanical Properties

    Properties

    Metric Imperial
    Tensile strength, ultimate (@20°C/68°F, varies with heat treatment) 1200 – 1590 MPa 174000 – 231000 psi
    Tensile strength, yield (@20°C/68°F, varies with heat treatment) 1000 – 1380 MPa 145000 – 200000 psi
    Reduction of area (@20°C/68°F) 50.00% 50.00%
    Modulus of elasticity (@20°C/68°F) 215 GPa 31200 ksi
    Poisson’s ratio 0.27-0.30 0.27-0.30

    4. Forging of H13 Tool Steel
    Heating for forging must be done slowly and uniformly. Soak through at
    1900°-2000°F and reheat as often as necessary, stopping work when the
    temperature drops below 1650°F. After forging, cool slowly in lime,
    mica, dry ashes or furnace. H-13 should always be annealed after
    forging.

    5. Heat Treatment for H13 Tool Steels

    • Annealing

    Heat
    slowly to 1550°-1650°F, hold until entire mass is heated through, and
    cool slowly in the furnace (40F per hour) to about 1000°F, after which
    cooling rate may be increased. Suitable precautions must be taken to
    prevent excessive carburization or decarburization.

    • Stress Relieving

    When
    desirable to relieve the strains of machining, heat slowly to
    1050°-1250°F, allow to equalize, and then cool in still air (Strain
    Relieving). Â

    • Preheat Prior to Hardening

    Warm slightly before charging into the preheat furnace, which should be operating at 1400°-1500°F.

    • Hardening

    H13
    tool steel is a steel having very high hardenability and should be
    hardened by cooling in still air. The use of a salt bath or controlled
    atmosphere furnace is desirable to minimize decarburization, and if not
    available, pack hardening in spent pitch coke is suggested. The
    temperature employed is usually 1800°-1850°F, depending on size section.

    • Quenching

    Quench
    in still air or dry air blast. If complicated forms are to be hardened,
    an interrupted oil quench can be used. Quench part in oil and remove
    from bath when it just loses its color (1000°-1100°F). Finish cooling to
    below 150°-125°F in air, then temper immediately.

    • Tempering

    Tempering
    practice may vary with size and application, but is usually performed
    in the range of maximum secondary hardness or higher. Double tempering
    is recommended. The results below is H13 that was air quenched from
    1800°F and tempered for 4 hours at various temperatures. The results may
    be used as a guide, keeping in mind that parts of heavy section or mass
    may be several points lower in hardness.

    6. Application of AISI H13 Tool Steel

    • As Tools for Extrusion

    Part Aluminium, mag­nesium alloys, HRC Copper al­loys HRC Stainless steel HRC
    Dies, Backers, die-holders, liners, dummy blocks, stems 44-50 43-47 45-50
    41-50 40-48 40-48

    Austenitizing temperature

    1,870-1,885°F 1,900-1,920°F
    (1,020-1,030°C) (1,040-1,050°C)
    • As Plastic Molding Tool Steel

    Part Austenitizing temp. HRC
    Injection molds Compression/ transfer molds 1,870-1,885°F (1,020-1,030°C) 50-52
    Tempering 480°F (250°C)
    • Other Applications

    Applications Austenitizing temp HRC
    Severe cold punching, scrap shears 1,870-1,885°F 50-52
    (1,020-1,030°C)
    Tempering 480°F (250°C)
    Hot shearing 1,870-1,885°F
    (1,020-1,030°C) 50-52
    Tempering 480°F (250°C) or
    1,070-1,110°F 45-50
    (575-600°C)
    Shrink rings (e.g. for cemented carbide dies) 1,870-1,885°F 45-50
    (1,020-1,030°C)
    Tempering 1,070-1,110°F
    (575–600°C)
    Wear-resisting parts 1,870-1,885°F Core
    50-52
    Surface
    ~1000HV1
    (1,020-1,030°C)
    Tempering 1,070°F (575°C)
    nitrided

     

    If
    there are any queries about AISI H13 tool steel for hot working
    applications, please feel free to leave a comment below. And welcome
    enquiry of AISI H13 tool steel, we are professional and reliable
    supplier  for prime H13 tool steel materials.

  • Previous:
  • Next:



  • Description http://www.advancedglobalmaterials.com, or Call us at 631-286-8570 for a quote. We supply all AMS Specs, Alloy Steel,Stainless Steel,Aluminum, Titanium and Nickel



    India’s initial indigenous aircraft carrier (IAC-one) for the Indian Navy has been floated out at condition-owned Cochin Shipyard Restricted (CSL) throughout a ceremony attended by substantial-position naval officials and ministers. The IAC-one is a forty,000 tonne air defence platform and will be named INS Vikrant. Because of to delays in the tasks, the INS is probable to enter support only in 2015. Since this India’s initial endeavor at creating a sea-borne aircraft carrier, a modular design pattern was remaining adopted wherein finish blocks were being crafted off site and then equipped in get to velocity up the design.

    The hull of the aircraft carrier INS Vikrant was floated out of its dry-dock facility and it was a very low key party. Seemingly, the dry-dock facility was necessary for urgent business perform at the shipyard and the precise start is expected to consider place a year from now. The floating ceremony was adopted by a assessment of the development on the aircraft carrier and the future study course of action to complete the task on time. According to resources, the task perform has skipped its deadline owing to the delays in design at the CSL.

    At this time, the indigenous aircraft carrier has taken on about fourteen,000 tonnes and the procedure of interior outfitting will be carried out. This will include the laying of pipes ahead of the carrier is dry-docked again in mid-2012. This will be adopted by integration of the propulsion gear-box and generators other than other issues. The gasoline turbines are also in the procedure of remaining mounted and the aircraft carrier is still 50 percent the tonnage.

    The aircraft carrier INS Vikrant will have an endurance of eight,000 nautical miles and will be to carry a maximum of 30 aircraft. INS Vikrant will have extensive-assortment area-to-air missile (LR SAM) techniques with a multi-operate radar, a close-in weapon process, the most modern C/D band early air-warning radar and the V/UHF tactical air-navigational and direction getting techniques. The carrier will have two consider-off runways and landing will be accomplished working with arrester wires. The ship’s integration with the Indian Navy’s community-centric functions will present for power multiplication. The Indian Navy ideas to equip INS Vikrant with a combine of MiG-29K / LCA Naval Variant at the moment remaining made by condition-owned Aeronautical Improvement Agency (ADA). Nevertheless, owing to delays, an RFI (ask for for info) has been issued to several world aviation majors, including American Boeing, French Dassault and Russian MiG firms, for an alternate deck-based mostly aircraft.

    Relating to the delays in the indigenous aircraft task, it has been set up that the shipping and delivery of gear containers and associated techniques experienced retarded the design price. There has also been decrease in the source of metal but the trouble was prevail over as Defence Metallurgical Investigation Laboratory (DMRL) and the Metal Authority of India (SAIL) delivered indigenous substantial-grade metal for the task. The high quality of the gearbox was also sorted with a neighborhood Indian agency producing the main gear-box with support from a German agency.

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Tree

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Flag