Hot-selling attractive price AISI 8620 Steel | 1.6523 | 21NiCrMo2 | SNCM220 Wholesale to Latvia
AISI 8620 Steel is a low alloy nickel, chromium, molybdenum case hardening steel,generally supplied in the as rolled condition with a maximum hardness HB 255max. SAE steel 8620 offers high external strength and good internalstrength, making it highly wear resistant. AISI 8620 steel has a highercore strength than grades 8615 and 8617. SAE 8620 alloy steel isflexible during hardening treatments, thus enabling improvement ofcase/core properties. Pre hardened and tempered (uncarburized) 8620 ca...
Our eternal pursuits are the attitude of "regard the market, regard the custom, regard the science" and the theory of "quality the basic, trust the first and management the advanced" for Hot-selling attractive price AISI 8620 Steel | 1.6523 | 21NiCrMo2 | SNCM220 Wholesale to Latvia, "Passion, Honesty, Sound service, Keen cooperation and Development" are our goals. We are here expecting friends all over the world!
is a low alloy nickel, chromium, molybdenum case hardening steel,
generally supplied in the as rolled condition with a maximum hardness HB
255max. SAE steel 8620 offers high external strength and good internal
strength, making it highly wear resistant. AISI 8620 steel has a higher
core strength than grades 8615 and 8617.
SAE 8620 alloy steel is
flexible during hardening treatments, thus enabling improvement of
case/core properties. Pre hardened and tempered (uncarburized) 8620 can
be further surface hardened by nitriding but will not respond
satisfactorily to flame or induction hardening due to its low carbon
Steel 8620 is suited for applications which require a
combination of toughness and wear resistance. This grade is commonly
supplied in round bar.
1. AISI 8620 Steel Supply Range
8620 Round Bar: diameter 80mm – 1200mm
8620 Steel Plate: thickness 10mm – 1500mm x width 200mm – 3000mm
8620 Square Bar: 140mm – 460mm
8620 tubes are also available against your detailed request.
Surface Finish: Black, Rough Machined, Turned or as per given requirements.
2. SAE 8620 Steel Specification and Relevant Standards
3. ASTM 8620 Steels & Equilvalents Chemical Composition
4. AISI 8620 Steel Mechanical Properties
8620 Physical Properties:
Density (lb / cu. in.) 0.283
Specific Gravity 7.8
Specific Heat (Btu/lb/Deg F – [32-212 Deg F]) 0.1
Melting Point (Deg F) 2600
Thermal Conductivity 26
Mean Coeff Thermal Expansion 6.6
Modulus of Elasticity Tension 31
8620 Steel Mechanical Properties
|Tensile strength||530 MPa||76900 psi|
|Yield strength||385 MPa||55800 psi|
|Elastic modulus||190-210 GPa||27557-30458 ksi|
|Bulk modulus (typical for steel)||140 GPa||20300 ksi|
|Shear modulus (typical for steel)||80 GPa||11600 ksi|
|Izod Impact||115 J||84.8 ft.lb|
|Hardness, Knoop (converted from Brinell hardness)||169||169|
|Hardness, Rockwell B (converted from Brinell hardness)||80||80|
|Hardness, Vickers (converted from Brinell hardness)||155||155|
|Machinability (hot rolled and cold drawn, based on 100 machinability for AISI 1212 steel)||65||65|
5. Forging of Material 8620 Steel
8620 alloy steel is forged at a start temperature of around 2250ºF
(1230ºC) down to approximately 1700ºF(925ºC.) prior to the hardening
heat treatment or carburizing. The alloy is air cooled after forging.
6. ASTM 8620 Steel Heat Treatment
8620 steel may be given a full anneal by heat to 820℃ – 850℃, and hold
until temperature is uniform throughout the section and cool in furnace
or air cooled.
of heat treated and water quenched parts of 8620 steels (not
carburized) is done at 400 F to 1300 F to improve case toughness with
minimal effect on its hardness. This will also reduce the possibility of
AISI steel 8620 will be austenitized at around 840°C – 870°C, and oil
or water quenched depending upon section size and intricacy. Cool in Air
or Oil required.
(910ºC) and air cool. This is another method of improving machinability
in 8620 material; normalizing might also be used prior to case
7. Machinability of SAE 8620 Steel
8620 alloy steel is readily machined after heat treatment and/or
carburizing, should be at a minimum so as not to impair the hardened
case of the part. Machining may be done by conventional means prior to
heat treatment – after carburizing machining is usually limited to
8. Welding of 8620 Materials
alloy 8620 may be welded as rolled condition by conventional methods,
usually gas or arc welding. Preheating at 400 F is beneficial and
subsequent heating after welding is recommended – consult the approved
weld procedure for the method used. However, welding in the case
hardened or through hardened condition is not recommended
9. Application of ASTM 8620 Steel
8620 steel material is used extensively by all industry sectors for
light to medium stressed components and shafts requiring high surface
wear resistance with reasonable core strength and impact properties.
applications are: Arbors, Bearings, Bushings, Cam Shafts, Differential
Pinions, Guide Pins, King Pins, Pistons Pins, Gears, Splined Shafts,
Ratchets, Sleeves and other applications where it is helpful to have a
steel that can be readily machined and carburized to controlled case
Methods of Demagnetisation
The magnetic property of the magnet can be totally or partially destroyed by rough handling, by heating, by induction or by passing electricity. Click on each method for more information.
Hammering, dropping and rough handling of the magnet can be demagnetise the magnet.
A magnet loses its magnetism if it is heated above a certain temperature called it’s ‘Curie point’. The curie point of iron is 770 degree celsius and that of the steel is 880 degree celsius, the curie point if nickel is 358 degree celsius and that for cobalt is 1121 degree celsius.
If two magnets are placed side by side with similar poles together each induces opposite polarity in the other as a result the magnets lose magnetism to avoid the self demagnetisation the magnets are placed in pairs side by side with their unlike poles together as shown here
By passing electricity place the given bar but has to be demagnetise inside a long coil of insulated copper wire in the east west direction. Connect the copper wire to a source of alternating current as shown here. Switch on the circuit. Now slowly reduce the current to 0.
The magnet loses its magnetism as alternating current changes direction continuously. This change in direction of current disturbs the alignment of molecular magnets resulted in the demagnetisation.
http://MuggyWeld.com SSF-6 Silver Solder can braze copper nickel, cupre nickel, copper, brass, bronze, steel, or stainless in any combination. This product can be successfully applied using MAPP, natural gas, oxyacetylene, or propane.
This unique brazing rod is stronger than most MIG welding wires, at more than 70,000 PSI
For more videos and information, or to order, visit http://MuggyWeld.com
Please read all instructions prior to use at: http://muggyweld.com/packets/ssff6ssq6postsale.pdf
Please visit http://www.aws.org/technical/facts/ prior to using Muggy Weld products, and adhere to all AWS welding safety guidelines. Further product safety information is available at http://muggyweld.com/safety-guidelines.
Muggy Weld LLC shall not be liable for any loss, injury, claim, liability, or damage of any kind resulting in any way from (a) your use of this Site, (b) any services or products obtained from this Site, (c) any errors in or omissions from this Site, (d) the unavailability or interruption of this Site or any features thereof, (e) any content contained on this Site.
MSDS sheets available with purchase from MuggyWeld.com, upon request.