Hot Sale for D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory from Dominica
1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade...
We insist on offering high quality production with good business concept, honest sales and the best and fast service. it will bring you not only the high quality product and huge profit, but the most significant is to occupy the endless market for Hot Sale for D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory from Dominica, Welcome to build the well and long standing business relationships with our company to create a glorious future together .customers' satisfaction is our eternal pursuit
1. Relevant D2 Steel Specifications
|Standard||ASTM A681||DIN EN ISO 4957||JIS G4404|
2. D2 Tool Steel Chemical Composition
|DIN ISO 4957||C||Mn||P||S||Si||Cr||V||Mo|
3. AISI Grade D2 Steel Mechanical Properties
|Hardness, Knoop (converted from Rockwell C hardness)||769||769|
|Hardness, Rockwell C||62||62|
|Izod impact unnotched||77.0 J||56.8 ft-lb|
|Elastic modulus||190-210 GPa||27557-30457 ksi|
|Thermal expansion||10.4 x 10-6/ºC||20-100||
4. AISI/ASTM A681 D2 Grade Steel Forging
Heating for forging of AISI D2 tool steel should
be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
should always be annealed after forging.
5. D2 Tool Steel Heat Treatment
ASTM D2 steels alloy should be preheated very slowly to 815oC (1500oF) and then temperature can be increased to 1010oC (1850oF). They are then held at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).
Annealing of D2 tool steels material should be done at 871 to 898oC (1600 to 1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or less.after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.
When desirable to relieve the strains of machining, heat D2 grade steel slowly to 1050°-1250°F, allow to equalize, and then cool in still air (Strain Relieving).
Preheat Prior To Hardening
Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.
After thorough preheating, heat to 1800°-1850°F. Hold the work piece at the hardening temperature until it is completely and uniformly heated.
AISI D2 steel tool material is an air hardening steel and will develop hardness on cooling in still air. To avoid scaling and prevent decarburization of the work piece surface, controlled atmosphere or vacuum furnaces are recommended. If these furnaces are not available, pack hardening, salt baths or wrapping the piece in stainless steel foil will provide some degree of surface protection in the hardening process. Parts should be allowed to cool to 150F, or to where they can be held in the bare hand, and then temper immediately.
The tempering temperature on material D2 steel may be varied according to the desired hardness. D2 steels can be tempered at 204oC (400oF) for achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell C hardness of 54.
6. D2 Tool Steel Material Application
AISI grade D2 tool steels are used for long run tooling applications, where wear resistance is important, such as blanking or forming dies and thread rolling dies.
Some main applications for D2 tool steel are as below:
Blanking Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls, Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear Parts.
We usually hold D2 tool steel on sale activities, and you would have our price on regular schedule. Contact us and sign in our newsletter to have D2 tool steel materials price list and commercial quote today.
The Musashi forge is identified for continually generating useful and elegant katana swords with an remarkable worth mixed with spectacular overall performance.
Our new Folded Elite series carries on to increase the bar by providing differentially hardened folded metal blades mixed with special fittings. Wholly handmade with shut supervision and consideration to detail, these swords are designed to be collection and dojo centre parts.
Both of those 1045 and 1060 high carbon metal are fastened alongside one another and folded eleven times resulting in 4096 levels. The metal is then formed into the blade geometry and clay tempered to produce differential hardness and a genuine hamon line. The temper procedure also creates an edge hardness of 58RC. Now in its last stage of output, the blade is hand honed for an impressively sharp edge, really polished, inspected and coated with protecting oil.
The hamon line detail is on the multi-metal layered blade. The hamon line distinguishes in between the more difficult edge metal and the additional versatile spine metal, marking in which the metallic variations its hardness. The levels of metal are designed noticeable along the hamon line, resulting in a wonderful and special layered wave hamon.
Merchandise Technical specs:
Fully useful samurai sword function of art.
Stunning workmanship and consideration to detail.
Folded high carbon metal Damascus blade with 4096 levels.
Clay tempering procedure with h2o quench.
58 RC edge (HA) hardness, 42 RC spine (MUNE) hardness.
Hamon and hardness designed with temper procedure.
Serious hamon, not wire brushed or printed.
Serious ray skin with cotton/nylon twine wrapped grip.
Brass Tsuba, Fuchi and Kashira.
Incredibly sharp hand honed edge.
Highly polished blade.
Hardwood tackle with dual bamboo pegs.
Hardwood scabbard with high excellent piano paint complete.
forty.five in. in general, 27.five in. blade, 11 in. tackle.
Arrives serialized with Certification of Authenticity.
Contains hardwood situation, black sword bag and cleaning kit.