High Quality EN DIN 34CrNiMo6 | 1.6582 | 4337 Engineering Steel Factory in Sweden

High Quality EN DIN 34CrNiMo6 | 1.6582 | 4337 Engineering Steel Factory in Sweden

Short Description:

EN 34CrNiMo6 Steel is an important alloy engineering steel grade as per BS EN10083-3:2006. 34CrNim06 steel has high strength, high toughness and good hardenability. EN / DIN 34CrNiMo6 alloy steel has the stability ofresistance to overheating, but the white sensitivity of 34CrNiM06 ishigh. It also has the temper brittleness, so the weldability of34CrNiMo6 material is poor. The steel 34CrNiMo6 needs the hightemperature preheating before welding in order to eliminate the stressafter welding proc...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    Our products are widely recognized and trusted by users and can meet continuously changing economic and social needs of High Quality EN DIN 34CrNiMo6 | 1.6582 | 4337 Engineering Steel Factory in Sweden, sincerely look forward to serving you in the near future. You are sincerely welcome to visit our company to talk business face to face with each other and establish long-term co-operation with us!


    EN 34CrNiMo6 Steel

    is an important alloy engineering steel grade as per BS EN
    10083-3:2006. 34CrNim06 steel has high strength, high toughness and good

    hardenability. EN / DIN 34CrNiMo6 alloy steel has the stability of
    resistance to overheating, but the white sensitivity of 34CrNiM06 is
    high. It also has the temper brittleness, so the weldability of
    34CrNiMo6 material is poor. The steel 34CrNiMo6 needs the high
    temperature preheating before welding in order to eliminate the stress
    after welding processing.


    1.EN Steel 34CrNiMo6 Supply Range

    Round Steel Bar Sizes: diameter 80mm – 1200mm
    Other steel shape and sizes available according to your requirements.

    Surface finish: Black, machined, peeled, turned or according to other customers’ pecial requirements.

    2.EN 34CrNiMo6 Steel Standards And Equivalents

    BS EN 10083 -3: 2006 34CrNiMo6 / 1.6582 ASTM A29: 2004 4337
    BS EN 10250 – 3: 2000

    3. EN/DIN 34CrNiMo6 Steel Chemical Composition Properties

    BS EN 10083 – 3:2006 34CrNiMo6
    /1.6582
    C Mn Si P S Cr Mo Ni
    0.30-0.38 0.5-0.8 0.40 max 0.025 max 0.035 max 1.3-1.7 0.15-0.30 1.3-1.7
    BS EN 10250-3:2000 C Mn Si P S Cr Mo Ni
    0.30-0.38 0.5-0.8 0.40 max 0.035 max 0.035 max 1.3-1.7 0.15-0.30 1.3-1.7
    ASTM A29: 2004 4337 C Mn Si P S Cr Mo Ni
    0.30-0.40 0.6-0.8 0.20-0.35 0.035 max 0.040 max 0.70-0.90 0.20-0.30 1.65-2.00

    4.Mechanical Properties of EN/DIN 34CrNiM06 / 1.6582 Alloy Steel

    Properties < 16 >16 – 40 >40 – 100 >100 – 160 >160 – 250
    Thickness t [mm] < 8 8<t<20 20<t<60 60<t<100 100<t<160
    Yield strength Re [N/mm2] min. 1000 min. 900 min. 800 min. 700 min. 600
    Tensile strength Rm [N/mm2] 1200 – 1400 1100 – 1300 1000 – 1200 900 – 1100 800 – 950
    Elongation A [%] min. 9 min. 10 min. 11 min. 12 min. 13
    Reduction of area Z [%] min. 40 min. 45 min. 50 min. 55 min. 55
    Toughness CVN [J] min. 35 min. 45 min. 45 min. 45 min. 45

    5.Heat Treatment of 34CrNiMo6 Engineering Steel

    Quenched and Tempered (Q+T) of 34CrNiMo6 Steel

      Heat 34CrNiMo6 round steel slowly to the temperature of 850°C;

      Soak at this hardening temperature quench in oil;

      Temper as soon as 34CrNiMo6 steels reach room temperature.

      Heat uniformly to the suitable temperature;

      Withdraw from the furnace and cool in the air.

      The usual tempering temperature is 600°C which depending on the actual requirements.

      6.Forging of DIN 34CrNiMo6 / 1.6582 Steel

      Hot forming temperature: 1100-900oC.

      7.Machinability of Steel34CrNiMo6

      Machining

      is best done with this 1.6582 alloy steel in the annealed or normalized

      and tempered condition. It can be machined by all conventional methods.

      8.Welding

      The

      alloy materials can be fusion or resistance welded. Preheat and post
      heat weld procedures should be followed when welding this alloy by
      established methods.

      9.Application

      EN DIN
      34CrNiMo6 steel is used to make tools which demands good plasticity and
      high strength. It is usually selected to make the big size and important

      parts, such as heavy machinery axle,turbine shaft blade, high load of
      transmission parts, fasteners, crank shafts, gears, as well as heavily
      loaded parts for motor construction etc.

      Otai Steel is reliable to

      supply engineering 34CrNiMo6 steels / 1.6582 engineering alloy steels.
      Please tell us your detailed requirements and have the best offer soon.

    • Previous:
    • Next:



  • Designer Mariëlle Leenders has experimented with fabric that features shape memory wire either woven into the material or added later as one or more lines of stitching. Her Moving Textiles (2000) react to differences in temperature by shrinking, creasing, changing structure or rolling up. Lines of stitching added to the basic material in certain places cause the fabric to creep up when temperatures rise.

    Fabrics incorporating wire containing shape memory alloys (SMA) vary in form according to changes in temperature. The thin wire is made of an alloy based on nickel and titanium. This metallic material belongs to a group of related substances referred to as shape memory alloys (SMA). They possess the ability to return to some previously defined shape or size when subjected to the appropriate thermal procedure. Generally, the materials can be plastically deformed at some relatively low temperature, after which -upon exposure to some higher or lower temperature they revert to their original shapes. The temperature at which the material changes in form can be programmed precisely at any desired temperature between -50° and + 100°C. Materials that exhibit shape memory only upon heating have a one-way shape memory. A shape memory alloy deformed at a temperature slightly above its transformation temperature has a high degree of elasticity.
    When a similar heating process is applied to Moving Textiles, a material that features shape memory wire, the fabric reacts to later changes in temperature (of more than 2.5°C) by shrinking, creasing, changing structure or rolling up. Normal fluctuations in body temperature, therefore, cause no reaction. But clothing made of Moving Textiles can be programmed to respond to the transition from outdoor temperatures to heated indoor spaces. Examples are sleeves that automatically roll up and down, a jacket that opens and closes on its own, and a shirt that expands and contracts in both length and circumference. Other possibilities are blinds that descend when exposed to warm sunlight and roll back up when the temperature drops, moving lampshades, etc. Moving Textiles can be used for both decorative and functional purposes.

    For more information:
    www.shapememorytextiles.com
    www.marielleleenders.nl



    Machining of a heat-resistant steel turbine housing on a G550 with the GROB feed-out spindle.

    Turbinengehäuse aus hitzebeständigem Stahl – Bearbeitung mit der GROB-Motorspindel mit Planzugeinrichtung auf einer G550.

    For further information please visit our website http://www.grobgroup.com or contact us at info@de.grobgroup.com.

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Truck

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Heart