factory wholesale good quality AISI 4340 Steel | 36CrNiMo4 | 1.6511 | EN24 | 817M40 | SNCM439 Wholesale to Chicago

factory wholesale good quality
 AISI 4340 Steel | 36CrNiMo4 | 1.6511 | EN24 | 817M40 | SNCM439 Wholesale to Chicago

Short Description:

AISI 4340 steel is a medium carbon, low alloy steel known for its toughness andstrength in relatively large sections. AISI 4340 is also one kind ofnickel chromium molybdenum steels. 4340 alloy steel is generallysupplied hardened and tempered in the tensile range of 930 – 1080 Mpa.Pre hardened and tempered 4340 steels can be further surface hardened by flame or induction hardening and by nitriding. The 4340 steel has goodshock and impact resistance as well as wear and abrasion resistanc...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    The company keeps to the operation concept "scientific management, high quality and efficiency primacy, customer supreme for factory wholesale good quality AISI 4340 Steel | 36CrNiMo4 | 1.6511 | EN24 | 817M40 | SNCM439 Wholesale to Chicago, We welcome you to inquire us by call or mail and hope to build a successful and cooperative relationship.


    AISI 4340 steel
    is a medium carbon, low alloy steel known for its toughness and
    strength in relatively large sections. AISI 4340 is also one kind of
    nickel chromium molybdenum steels. 4340 alloy steel is generally
    supplied hardened and tempered in the tensile range of 930 – 1080 Mpa.
    Pre hardened and tempered 4340 steels can be further surface hardened by
    flame or induction hardening and by nitriding. The 4340 steel has good
    shock and impact resistance as well as wear and abrasion resistance in
    the hardened condition. AISI 4340 steel properties offer good ductility
    in the annealed condition, allowing it to be bent or formed. Fusion and
    resistance welding is also possible with our 4340 alloy steel. ASTM 4340
    material is often utilized where other alloy steels do not have the
    hardenability to give the strength required. For highly stressed parts
    it is excellent choice. AISI 4340 alloy steel can also be machined by
    all customary methods.

    Due to availability the ASTM 4340 grade steel is often substituted
    with European based standards 817M40/EN24 and 1.6511/36CrNiMo4 or Japan
    based SNCM439 steel. You have the detailed data of 4340 steel below.

    1. AISI 4340 Steel Specification and Relevant Standards

    Country USA Britain Britain Japan
    Standard ASTM A29 EN 10250 BS 970 JIS G4103
    Grades 4340 36CrNiMo4/
    1.6511
    EN24/817M40 SNCM 439/SNCM8

    2. ASTM 4340 Steels And Equilvalents Chemical Composition

    Standard Grade C Mn P S Si Ni Cr Mo
    ASTM A29 4340 0.38-0.43 0.60-0.80 0.035 0.040 0.15-0.35 1.65-2.00 0.70-0.90 0.20-0.30
    EN 10250 36CrNiMo4/
    1.6511
    0.32-0.40 0.50-0.80 0.035 0.035 ≦0.40 0.90-1.20 0.90-1.2 0.15-0.30
    BS 970 EN24/817M40 0.36-0.44 0.45-0.70 0.035 0.040 0.1-0.40 1.00-1.40 0.20-0.35
    JIS G4103 SNCM 439/SNCM8 0.36-0.43 0.60-0.90 0.030 0.030 0.15-0.35 1.60-2.00 0.60-1.00 0.15-0.30

    3. AISI Alloy 4140 Steel Mechanical Properties

    Mechannical Properties

    (Heat Treated Condition )

    Condition Ruling section
    mm
    Tensile Strength MPa Yield Strength
    MPa
    Elong.
    %
    Izod Impact
    J
    Brinell
    Hardness
    T 250 850-1000 635 13 40 248-302
    T 150 850-1000 665 13 54 248-302
    U 100 930-1080 740 12 47 269-331
    V 63 1000-1150 835 12 47 293-352
    W 30 1080-1230 925 11 41 311-375
    X 30 1150-1300 1005 10 34 341-401
    Y 30 1230-1380 1080 10 24 363-429
    Z 30 1555- 1125 5 10 444-

    Thermal Properties

    Properties Metric Imperial
    Thermal expansion co-efficient (20°C/68°F, specimen oil hardened, 600°C (1110°F) temper 12.3 µm/m°C 6.83 µin/in°F
    Thermal conductivity (typical steel) 44.5 W/mK 309 BTU in/hr.ft².°F

    4. Forging of 4340 Alloy Steel

    Preheat
    the steel 4340 first, heat up to 1150°C – 1200°C maximum for forging,
    hold until temperature is uniform throughout the section.

    Do not forge
    below 850 °C. 4340 has good forging characteristics but care must be
    taken when cooling as the steel shows susceptibility to cracking.
    Following forging operation the work piece should be cooled as slowly as
    possible. And cooling in in sand or dry lime is recommended etc.

    5. AISI 4340 Steel Grade Heat Treatment

    • Stress Relieving

    For
    pre-hardened steel stress relieving is achieved by heating steel 4340
    to between 500 to 550°C. Heat to 600 °C – 650 °C, hold until temperature
    is uniform throughout the section, soak for 1 hour per 25 mm section,
    and cool in still air.

    • Annealing

    A
    full anneal may be done at 844°C (1550 F) followed by controlled
    (furnace) cooling at a rate not faster than 10°C (50 F) per hour down to
    315°C (600 F). From 315°C 600 F it may be air cooled.

    • Tempering

    AISI
    4340 alloy steel should be in the heat treated or normalized and heat
    treated condition before tempering. The tempering temperature for
    depends upon the strength level desired. For strength levels in the 260 –
    280 ksi range temper at 232°C (450 F). For strength in the 125 – 200
    ksi range temper at 510°C (950 F). And don’t temper the 4340 steels if
    it is in the 220 – 260 ksi strength range as tempering can result in
    degradation of impact resistance for this level of strength.

    Tempering should be avoided if possible within the range 250 °C – 450 °C due to temper brittleness.

    • Flame or Induction Hardening

    As mentioned above, pre-hardened and tempered 4340 steel bars or plates can be further surface hardened by either the flame or induction hardening
    methods resulting in a case hardness in excess of Rc 50. AISI 4340
    steel parts should be heated as quickly as possible to the austenitic
    temperature range (830 °C – 860 °C) and required case depth followed by
    an immediate oil or water quenching, depending upon hardness required,
    workpiece size/shape and quenching arrangements.

    Following
    quenching to hand warm, tempering at 150°C – 200°C will reduce stresses
    in the case with minimal effect on its hardness.

    All de-carburised surface material must first be removed to ensure best results.

    • Nitriding

    Hardened
    and tempered 4340 alloy steel can also be nitrided, giving a surface
    hardness of up to Rc 60. Heat to 500°C – 530°C and hold for sufficient
    time (from 10 to 60 hours) to develop the depth of case. Nitriding
    should be followed by slow cooling (no quench) reducing the problem of
    distortion. The nitrided grade 4340 materials can therefore be machined
    to near final size, leaving a small grinding allowance only. The tensile
    strength of the 4340 steel material core is usually not affected since
    the nitriding temperature range is generally below the original
    tempering temperature employed.

    Surface hardness achievable is 600 to 650HV.

    6. Machinability

    Machining
    is best done with the alloy steel 4340 in the annealed or normalized
    and tempered condition. It can be readily machined by all conventional
    methods such as sawing, turning, drilling etc. However in the high
    strength conditions of 200 ksi or greater the machinability is only from
    25% to 10% that of the alloy in the annealed condition.

    7. Welding

    Welding
    of steel 4340 in the hardened and tempered condition (as normally
    supplied), is not recommended and should be avoided if at all possible,
    because of the danger of quench cracking, as the mechanical properties
    will be altered within the weld heat affected zone.

    If welding
    must be carried out, pre-heat to 200 to 300°C and maintain this while
    welding. Immediately after welding stress relieve at 550 to 650°C, prior
    to hardening and tempering.

    If welding in the hardened and
    tempered condition is really necessary, then the work piece, immediately
    on cooling to hand warm, should be if possible stress relieved at 15 °C
    below the original tempering temperature.

    8. Application of 4340 Steel

    AISI
    4340 steel is used in most industry sectors for applications requiring
    higher tensile/yield strength than 4140 steel can provide.

    Some typical applications such as:

    • Aircraft Landing Gear

    • Automotive,

    • Oil and Gas Drilling,

    • Forging,

    • Warm and Cold Forming,

    • Machine Building,

    • Transfer Systems, like power transmission gears and shafts.

    • General
      engineering industries and structural use applications, such as: heavy
      duty shafts, gears, axles, spindles, couplings, pins, chucks, molds etc.

  • Previous:
  • Next:



  • TCM BALER:http://www.tcmbaler.com/ a professional manufacturer, specialize in hydraulic compressing machine/ baling press compactor/pressing baler for more than 15years, Our products are applicable for waste cardboard/ cardbox, OCC, plastic bottles ,fiber, rags,wipers,used clothes/clothing,textiles, cotton, newspaper, kraft paper, scrap metal, mattress spring, scrap car body, heavy steel etc. plays a big role in recycling industry, welcomed by domestic and national customers.

    Main products:
    1.Fully automatic horizontal baling press
    2.Semi-automatic horizontal baling press
    3.vertical baling press baler
    4.wipers/rags bagging press baler
    5.scrap metal baling compactor
    6.shearing baler machine
    7.container shear
    8.movable scrap metal baler compactor
    9.single shaft shredder
    10.double shaft shredder

    http://www.tcmbaler.com/

    Tel: 0086 -21-61522014
    Fax: 0086-21-61522018
    Email: machineinchina@hotmail.com

    Hydraulic Metal Baler, Scrap Baling Press, Aluminum Can Baler Australia, Metal Cans Baler, 14 rowsHydraulic metal baler can be driven by diesel engine for alternative. Hydraulic Metal Baler Application 1. such as scrap steel, aluminum, and copper, hydraulic automatic can baler, Metal Scrap Aluminum Can Baler, Metal Scrap Belarus, pop can baler, Metal Scrap Aluminum Can Baler, Wholesale Various High Quality Metal Scrap Aluminum Can Baler Products from Global Metal Scrap Aluminum Can Baler Suppliers and Metal, metal baler automatic, Scrap Metal Copper Baler Aluminum Recycling Machinery Switzerland, Metal Baling Machine, Scrap metal copper baler aluminum recycling machinery aluminum medicine plate recycling machine. FOB Reference Price, Hydraulic Metal Balers, SMB C40 Cans Baler. 9, Scrap Metal Balers Equipment Colombia, Scrap Metal Sheet Baler, SMB C40 Cans Metal Balers Equipment in 9, Jiangsu, Nantong, Steel Cans And Aluminum Cans Compressing Baler, SMB C40 Cans Baler Overview, , Factory Direct Sale Jpy81 Series Hydraulic Metal Scrap Iron Baler, Balers, Recycling Equipment, Colmar Equipment Ecuador, Copper Waste Metal Scraps Horizontal Hydraulic Baler For Sale, Colmar Balers are used as compactors in the Scrap Metal Industry for the Recycling Equipment. Shear Balers. or in the recycling of aluminum cans or other, Waste Scrap Metal Compressor, Aluminum Can Balers, Steel Can Baler, Drink Container El Salvador, Y81 Metal Scrap, Aluminum Alloy Frame, Aluminum Can, Animal Fiber View more PROSINO aluminum scrap shredders for further size PET bottle baler and aluminum can, Hydraulic Scrap Metal Pressure Baler Sale, Steel Can Baler, Aluminum Can Baler, Used Beverage Finland, 250t Iron Compress Machine, steel can baler machine, aluminum can Used Beverage Containers Aluminum or Steel Can Baler UBC Used Beverage Containers Aluminum or Steel Can, Metal Scrap Iron Baler, Scrap Metal Balers Australian Recycling Equipment Ghana, scrap metal baler compactor, lid baler, triple compression baler, aluminium baler, light scrap baler. Australian Recycling Equipment offers a comprehensive aluminum, zinc, steel., used metal baler, Aluminum Can Baler YouTube Greece, Mobile Baler, Aluminum cans scrap metal balers. Aluminum cans scrap metal balers. Categories: Scrap Metal Balers: Place of Origin: Jiangsu, China: Brand Name: Wanshida:, Hms Scrap Press Baler, Aluminum cans scrap metal balers for sale of ec91133190 Guatemala, Scrap Metal Briquette Machine, scrap metal aluminum can baler machine . The scrap metal aluminum can baler machine is suitable for compressing pop cans, oil drums, paint buckets, scrap, Automatic Hydraulic Secondary Metals Baler, scrap metal aluminum can baler machine, View scrap metal Honduras, metal scrap baler y83 250, Scrap balers and scrap shears by GPS the leading manufacturer of scrap processing equipment and This means that whichever scrap metal recycling machine you, 200 tons steel baler, Homemade aluminum can Baler YouTube Haiti, Hydraulic Steel Baler Manufacture, Lefort Scrap Baler with Bronneberg Guillotine. No price Helmond, Netherlands Recently Added. 1978 specifications: light aluminum cans, shredded cans, , Aluminium Scrap Baling Machine, Scrap Metal Recycling Equipment, Scrap Balers, Scrap Indonesia, Best selling Metal Scrap Baler Manufacture, Metal Balers Products Directory, Equipment Suppliers, Metal Balers Sellers Directory. waste copper aluminum, waste stainless steel, scrap, Recycling Equipment, Used Scrap Balers for sale. Taurus and more. Kazakhstan, Scrap Metal Recycling, McIntyre is a JMC Recycling Systems company and a manufacturer of recycling machinery including, metal balers, equipment for the scrap metal and recycling, Automatic Waste Metal Baler, Metal Hydraulic Baling Press Machine, Metal Copper Scrap Baler ,



    The Cold Steel Company prides itself on using traditional parts and fittings for its swords forged by traditional Eastern swordsmiths. This dedication to authenticity along with the sheer power and strength of their blades makes Cold Steel swords extremely desirable to collectors.Cold Steel swords and knives are known for their toughness. For instance, a knife in their Tanto series has been tested by being repeatedly thrust through a car door with no damage suffered by the tip of the blade. To achieve this power without breaking or marring Cold Steel uses a steel lamination process known as San Mai III. “San Mai” means, “three layers” and refers to the fact that laminated sword construction can allow various grades (or layers) of steel to be combined in a single blade. Combining layers in this way allows for maximum flexibility (on outside layers of the blade so it won’t shatter when struck in battle) with strength (at the blade’s core with a higher carbon steel).Many Cold Steel blades are also made from Carbon V, a high carbon, low alloy cutlery grade steel. The quality of Carbon V makes it extremely strong due to a smelting process which involves Cold Steel metallurgists maintaining an exact microstructure of the steel. After smelting, every shipment is checked for structural quality, cleanliness and chemical content before being optimized for grain flow along the length of the blade. Finally, a unique heat treating process (a highly guarded trade secret) is applied to every blade, ensuring a durability and beauty unmatched in many of Cold Steel’s rivals.Cold Steel swords are very popular for functional purposes (in the dojo) or for test cutting (an ancient practice known as tamashigeri where a sword’s quality was tested by cutting the bodies of corpses or criminals—straw mats or bamboo are used today). The quality of the steel in their blades denotes a high carbon content (as in the Tanto series) versus stainless steel which can be attractive to look at but does not have the durability needed to withstand the rigors of battle.

    88BOK
    Weight: 48 oz.
    Blade Thick: 5/16″
    Blade Length: 36″
    Handle: 13″ Samé (Ray Skin). black braid cord with brass Menuki
    Steel: 1055 Carbon
    Overall Length: 49″
    Sheath: Black Lacquered Wood w/blue violet cover bag

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Heart

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Key