Factory Price For H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel Factory from Myanmar

Factory Price For
 H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel Factory from Myanmar

Short Description:

H13 Tool Steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications. H13 tool steel is classified as group H steels by the AISI classification system. This series of steels start from H1 to H19. AISI H-13 tool steel is characterized by: Good resistance to abrasion at both low and high temperatures High level of toughness and ductility Uniform and high level of machinability and polishability Good high-temperature strength and resistance to t...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    In the past few years, our company absorbed and digested advanced technologies both at home and abroad. Meanwhile, our company staffs a team of experts devoted to the development of Factory Price For H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel Factory from Myanmar, We sincerely welcome overseas customers to consult for the long-term cooperation and the mutual development.We strongly believe that we can do better and better.


    H13 Tool Steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications. H13 tool steel is classified as group H steels by the AISI classification system. This series of steels start from H1 to H19.

    AISI H-13 tool steel is characterized by:

    • Good resistance to abrasion at both low and high temperatures

    • High level of toughness and ductility

    • Uniform and high level of machinability and polishability

    • Good high-temperature strength and resistance to thermal fatigue

    • Excellent through-hardening properties

    • Very limited distortion during hardening

    In
    steel H13, the molybdenum and vanadium act as strengthening agents. The
    chromium content assists die steel H-13 to resist softening when used
    at high temperatures. H-13 die steels offers an excellent combination of
    shock and abrasion resistance, and possesses good red hardness. It is
    capable of withstanding rapid cooling and resists premature heat
    checking. Tool Steel H13 has good machinability, good weldability, good
    ductility, and can be formed by conventional means.

    Due to H13
    tool steel excellent combination of high toughness and fatigue
    resistance, AISI H13 hot work tool steel is used more than any other
    tool steel in tooling applications.

    1. Common H13 Tool Steel Related Specifications

    Country USA German Japan
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404
    Grades H13 1.2344/X40CrMoV5-1 SKD61

    2. H13 Tool Steel Chemical Composition

    ASTM A681 C Mn P S Si Cr V Mo
    H13 0.32 0.45 0.2 0.6 0.03 0.03 0.8 1.25 4.75 5.5 0.8 1.2 1.1 1.75
    DIN ISO 4957 C Mn P S Si Cr V Mo
    1.2344 /X40CrMoV5-1 0.35 0.42 0.25 0.5 0.03 0.02 0.8 1.2 4.8 5.5 0.85 1.15 1.1 1.5
    JIS G4404 C Mn P S Si Cr V Mo
    SKD61 0.35 0.42 0.25 0.5 0.03 0.02 0.8 1.2 4.8 5.5 0.8 1.15 1.0 1.5

    3. AISI H13 Steel Mechanical Properties

    Properties

    Metric Imperial
    Tensile strength, ultimate (@20°C/68°F, varies with heat treatment) 1200 – 1590 MPa 174000 – 231000 psi
    Tensile strength, yield (@20°C/68°F, varies with heat treatment) 1000 – 1380 MPa 145000 – 200000 psi
    Reduction of area (@20°C/68°F) 50.00% 50.00%
    Modulus of elasticity (@20°C/68°F) 215 GPa 31200 ksi
    Poisson’s ratio 0.27-0.30 0.27-0.30

    4. Forging of H13 Tool Steel
    Heating for forging must be done slowly and uniformly. Soak through at
    1900°-2000°F and reheat as often as necessary, stopping work when the
    temperature drops below 1650°F. After forging, cool slowly in lime,
    mica, dry ashes or furnace. H-13 should always be annealed after
    forging.

    5. Heat Treatment for H13 Tool Steels

    • Annealing

    Heat
    slowly to 1550°-1650°F, hold until entire mass is heated through, and
    cool slowly in the furnace (40F per hour) to about 1000°F, after which
    cooling rate may be increased. Suitable precautions must be taken to
    prevent excessive carburization or decarburization.

    • Stress Relieving

    When
    desirable to relieve the strains of machining, heat slowly to
    1050°-1250°F, allow to equalize, and then cool in still air (Strain
    Relieving). Â

    • Preheat Prior to Hardening

    Warm slightly before charging into the preheat furnace, which should be operating at 1400°-1500°F.

    • Hardening

    H13
    tool steel is a steel having very high hardenability and should be
    hardened by cooling in still air. The use of a salt bath or controlled
    atmosphere furnace is desirable to minimize decarburization, and if not
    available, pack hardening in spent pitch coke is suggested. The
    temperature employed is usually 1800°-1850°F, depending on size section.

    • Quenching

    Quench
    in still air or dry air blast. If complicated forms are to be hardened,
    an interrupted oil quench can be used. Quench part in oil and remove
    from bath when it just loses its color (1000°-1100°F). Finish cooling to
    below 150°-125°F in air, then temper immediately.

    • Tempering

    Tempering
    practice may vary with size and application, but is usually performed
    in the range of maximum secondary hardness or higher. Double tempering
    is recommended. The results below is H13 that was air quenched from
    1800°F and tempered for 4 hours at various temperatures. The results may
    be used as a guide, keeping in mind that parts of heavy section or mass
    may be several points lower in hardness.

    6. Application of AISI H13 Tool Steel

    • As Tools for Extrusion

    Part Aluminium, mag­nesium alloys, HRC Copper al­loys HRC Stainless steel HRC
    Dies, Backers, die-holders, liners, dummy blocks, stems 44-50 43-47 45-50
    41-50 40-48 40-48

    Austenitizing temperature

    1,870-1,885°F 1,900-1,920°F
    (1,020-1,030°C) (1,040-1,050°C)
    • As Plastic Molding Tool Steel

    Part Austenitizing temp. HRC
    Injection molds Compression/ transfer molds 1,870-1,885°F (1,020-1,030°C) 50-52
    Tempering 480°F (250°C)
    • Other Applications

    Applications Austenitizing temp HRC
    Severe cold punching, scrap shears 1,870-1,885°F 50-52
    (1,020-1,030°C)
    Tempering 480°F (250°C)
    Hot shearing 1,870-1,885°F
    (1,020-1,030°C) 50-52
    Tempering 480°F (250°C) or
    1,070-1,110°F 45-50
    (575-600°C)
    Shrink rings (e.g. for cemented carbide dies) 1,870-1,885°F 45-50
    (1,020-1,030°C)
    Tempering 1,070-1,110°F
    (575–600°C)
    Wear-resisting parts 1,870-1,885°F Core
    50-52
    Surface
    ~1000HV1
    (1,020-1,030°C)
    Tempering 1,070°F (575°C)
    nitrided

     

    If
    there are any queries about AISI H13 tool steel for hot working
    applications, please feel free to leave a comment below. And welcome
    enquiry of AISI H13 tool steel, we are professional and reliable
    supplier  for prime H13 tool steel materials.

  • Previous:
  • Next:



  • Single Layer Sheet Extrusion Line can make one color PP/PS/HIPS/PS sheet.

    Technical Parameter:
    Suitable Sheet: PP, PS
    Max. Sheet Width: 670mm
    Sheet Thickness Range: 0.3mm-2.0mm
    Screw rod Dia.: 110 mm
    Screw L/D ratio: 30:1
    Main Motor Power: 45kw
    Max. Output: 150kgs/hr -200kgs/hr
    Rated Power: 65kw
    Actual Power: 45kw
    Overall Diameter(long x width x high): 11000mm x 2000mm x 1800mm
    Weight: 5.8T
    Standard Power Supply: 380v/3phase/4lines/50hz

    Function:

    The extruder extrudes PP/PS sheet.
    The machine is composed of extruding, calendering and traction rolling. The main parts including screw rods, cylinder, die are made of high quality specially-treated alloys. It’s characterized by abrasion resistant, resistant to corrosion, high-temperature resistant, etc. The extruding channel is even in resistance force and has no retention, which have the sheets of thickness is in balance.

    a. EXTRUDER PART: 1 set
    Output: max. 150kg/h
    Screw dia.: 110mm Hopper: 1 set L/D: 30:1
    Screw & barrel material: 38 CrMoAlA after nitrogen treatment with optimum hardness, strong corrosion resistance and long service lifetime
    Screw rotate speed: 0-70r.p/min
    Main motor power: 45.0kw
    Heating way: aluminium-casted heater
    Heating power: 15.0kw

    b. DIE HEAD PART: 1 set
    Sheet structure: 1 layer
    T-die design: like cloth-hanger, enable the melting material be flowed evenly from the outlet.
    Die head Width: 730mm
    Finished sheet width: 670mm
    sheet thickness: 0.3mm-2mm.
    Heating way: Aluminum-casted heater
    FILTER PART: 1 set
    Worm-gear case: 1 pc
    Filter size: 300mm x 40 mm
    Net dia.: 3-3.5mm
    Heating power: 7.2kw
    Net change: by hydraulic system, it includes double filters.

    d. WINDING PART: 1 set
    Winding rubber roller: 1 pc
    Flat roller: 1 pc
    Finished roll max.dia. 760mm
    Double working stations for receiving sheet

    e. 3 ROLLERS PART: 1 set
    Roller dia.: 345mm
    Roller length: 770mm
    Roller no.: 3 pcs
    Rollers reach to ”mirror surface” standard
    Roller linear speed: 0-14m/min
    Drive motor: 4.0kw
    Roller part movement: by motor, 1.1kw
    Roller layout way: by level type, each roller arranged side by side
    The cooling way: It’s gyroidal way (not linear way) to cool each rollers as inside roller has many channel irons. In order to equably cool sheet, sheet thickness is same.

    f. TRACTION PART: 01 set
    Traction roller dia.: 160mm
    Traction roller length: 750mm
    Traction motor power: 2.2kw
    Speed adjustment: frequency inverter
    2 sets of device for receiving leftover.

    g. OTHERS:
    Machine size: 11m x 2m x 1.8m
    Machine weight: 5.8T
    Power supply: 380v/3phase/4lines/50hz
    ………
    More technical details with full quotation, pls contact chinathermoformer@hotmail.com

    Note: Youtube is prohibited in China, we can’t read any message. Please send your information to chinathermoformer@hotmail.com, thank you.



    Phone Michlin Metals 800.445.2125
    four hundred Series Stainless Metal – What is Martensitic Stainless Metal?
    four hundred series or martensitic stainless steel is magnetic and heat treatable. It is a unique crystal lattice structure than three hundred series and less corrosion resistant.

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Key

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Truck