owing to good service, a variety of high quality products, competitive prices and efficient delivery, we enjoy a good reputation among our customers. We are an energetic company with wide market for Factory Price For AISI 8620 Steel | 1.6523 | 21NiCrMo2 | SNCM220 Wholesale to Milan, Welcome to build the well and long standing business relationships with our company to create a glorious future together .customers' satisfaction is our eternal pursuit

AISI 8620 Steel

is a low alloy nickel, chromium, molybdenum case hardening steel,
generally supplied in the as rolled condition with a maximum hardness HB

255max. SAE steel 8620 offers high external strength and good internal
strength, making it highly wear resistant. AISI 8620 steel has a higher
core strength than grades 8615 and 8617.

SAE 8620 alloy steel is
flexible during hardening treatments, thus enabling improvement of
case/core properties. Pre hardened and tempered (uncarburized) 8620 can
be further surface hardened by nitriding but will not respond
satisfactorily to flame or induction hardening due to its low carbon
content.

Steel 8620 is suited for applications which require a
combination of toughness and wear resistance. This grade is commonly
supplied in round bar.

1. AISI 8620 Steel Supply Range

8620 Round Bar: diameter 80mm – 1200mm
8620 Steel Plate: thickness 10mm – 1500mm x width 200mm – 3000mm
8620 Square Bar: 140mm – 460mm
8620 tubes are also available against your detailed request.
Surface Finish: Black, Rough Machined, Turned or as per given requirements.

2. SAE 8620 Steel Specification and Relevant Standards

3. ASTM 8620 Steels & Equilvalents Chemical Composition

4. AISI 8620 Steel Mechanical Properties

• 8620 Physical Properties:

Density (lb / cu. in.) 0.283
Specific Gravity 7.8
Specific Heat (Btu/lb/Deg F – [32-212 Deg F]) 0.1
Melting Point (Deg F) 2600
Thermal Conductivity 26
Mean Coeff Thermal Expansion 6.6
Modulus of Elasticity Tension 31

• 8620 Steel Mechanical Properties

5. Forging of Material 8620 Steel

AISI

8620 alloy steel is forged at a start temperature of around 2250ºF
(1230ºC) down to approximately 1700ºF(925ºC.) prior to the hardening
heat treatment or carburizing. The alloy is air cooled after forging.

6. ASTM 8620 Steel Heat Treatment

• Annealing

AISI

8620 steel may be given a full anneal by heat to 820℃ – 850℃, and hold
until temperature is uniform throughout the section and cool in furnace
or air cooled.

• Tempering

Tempering

of heat treated and water quenched parts of 8620 steels (not
carburized) is done at 400 F to 1300 F to improve case toughness with
minimal effect on its hardness. This will also reduce the possibility of

grinding cracks.

• Hardening

The

AISI steel 8620 will be austenitized at around 840°C – 870°C, and oil
or water quenched depending upon section size and intricacy. Cool in Air

or Oil required.

• Normalizing

1675ºF

(910ºC) and air cool. This is another method of improving machinability

in 8620 material; normalizing might also be used prior to case
hardening.

7. Machinability of SAE 8620 Steel

The

8620 alloy steel is readily machined after heat treatment and/or
carburizing, should be at a minimum so as not to impair the hardened
case of the part. Machining may be done by conventional means prior to
heat treatment – after carburizing machining is usually limited to
grinding.

8. Welding of 8620 Materials

The
alloy 8620 may be welded as rolled condition by conventional methods,
usually gas or arc welding. Preheating at 400 F is beneficial and
subsequent heating after welding is recommended – consult the approved
weld procedure for the method used. However, welding in the case
hardened or through hardened condition is not recommended

9. Application of ASTM 8620 Steel

AISI

8620 steel material is used extensively by all industry sectors for
light to medium stressed components and shafts requiring high surface
wear resistance with reasonable core strength and impact properties.

Typical

applications are: Arbors, Bearings, Bushings, Cam Shafts, Differential
Pinions, Guide Pins, King Pins, Pistons Pins, Gears, Splined Shafts,
Ratchets, Sleeves and other applications where it is helpful to have a
steel that can be readily machined and carburized to controlled case
depths.