Factory Outlets ASTM 52100 Bearing Steel | 1.3505 | 100Cr6 | SUJ2 | EN31 Wholesale to Moldova
ASTM A295 is specification which covers 52100 high carbon bearing quality steelto be used in the manufacture of anti-friction bearings. And 52100 bearing steel is the most common steel grade in ASTM A295 standard for high-carbon anti-friction bearing steel. What is 52100 bearing steel? AISI/ASTM 52100 bearing steel is a high carbon, chromium containing low alloysteel that is through hardening and noted in particular for use asbearings. 52100 bearing steel is one kind of special steel with ...
We have a highly efficient team to deal with inquiries from customers. Our goal is "100% customer satisfaction by our product quality, price & our team service" and enjoy a good reputation among clients. With many factories, we can provide a wide range of Factory Outlets ASTM 52100 Bearing Steel | 1.3505 | 100Cr6 | SUJ2 | EN31 Wholesale to Moldova, We welcome new and old customers from all walks of life to contact us for future business relationships and mutual success!
is specification which covers 52100 high carbon bearing quality steel
to be used in the manufacture of anti-friction bearings. And is the most common steel grade in ASTM A295 standard for high-carbon anti-friction bearing steel.
What is 52100 bearing steel?
52100 bearing steel is a high carbon, chromium containing low alloy
steel that is through hardening and noted in particular for use as
52100 bearing steel is one kind of special steel with features of
high wear resistance and rolling fatigue strength. High-carbon chromium
bearing steel, engineering steel and some types of stainless steel and
heat resistant steel are used as materials of bearings and for other
Advantages of Chrome Bearing Steel 52100:
Superior hardness, 60-67 on Rockwell hardness scale (Rc) at room temperature
High carbon chrome alloy steel
Operates continually at temperatures up to 120°C
Used to produce precision ball bearings and roller bearings
Long working life
1. Relevant Steel Specification of ASTM 52100 Bearing Steel
|Standard||ASTM A295||DIN 17230|
2. Chemical Composition of 52100 Bearing Steel and Equivalents
3. Mechanical Properties of ASTM A295 52100 Bearing Steel
|Bulk modulus (typical for steel)||140 GPa||20300 ksi|
|Shear modulus (typical for steel)||80 GPa||11600 ksi|
|Elastic modulus||190-210 GPa||27557-30458 ksi|
|Hardness, Knoop (converted from Rockwell C hardness)||875||875|
|Hardness, Rockwell C (quenched in oil from 150°C tempered)||62||62|
|Hardness, Rockwell C (quenched in water from 150°C tempered)||64||64|
|Hardness, Rockwell C (quenched in oil)||64||64|
|Hardness, Rockwell C (quenched in water)||66||66|
|Hardness, Vickers (converted from Rockwell C hardness)||848||848|
|Machinability (spheroidized annealed and cold drawn. Based on 100 machinability for AISI 1212 steel)||40||40|
52100 Steel Physical Properties
|Density||7.81 g/cm3||0.282 lb/in³|
52100 Alloy Steel Thermal Properties
|Thermal expansion co-efficient (@ 23-280°C/73.4- 36°F, annealed)||11.9 µm/m°C||6.61 µin/in°F|
|Thermal conductivity (typical steel)||46.6 W/mK||323 BTU in/hr.ft².°F|
4. Forging of A295 52100 Bearing Steel
52100 alloy steel is forged at 927 to 1205°C, and should not be forged
below 925ºC. A post-forge equalization treatment is recommended at 745ºC
for 4-6 hours followed by air cooling for SAE/AISI 52100 steel.
6. Heat Treatment for ASTM 52100 Bearing Steel
52100 alloy bearing steel is heated at 816°C followed by quenching in
oil. Before performing this process, it is subjected to normalizing heat
treatment at 872°C followed by slowly cooling in order to reduce the
AISI 52100 bearing steels alloy can be hot worked at 205 to 538°C.
AISI 52100 bearing steel can be cold worked using conventional techniques in the annealed or normalized conditions.
For spheroidize anneale, the following isothermal anneal is recommended:
1500ºF (815ºC) for 3 hours
1350ºF (735ºC) for 4 hours
1250ºF (675ºC) for 3 hours
Slow cool to 1000ºF (540ºC) then air cool.
AISI 52100 alloy bearing steel could be hardened by quenching in water from 801-829 degree or quench in oil from 816-842 degree.
Temper to desired hardness as indicated by tempering curves after water or oil quench.
5. Applications of 52100 Bearing Steel
steel 52100 grade bearing steel is mainly used for the manufacture of
aircraft bearings and other highly stressed parts. This steel grade
52100 steel is preferably vacuum arc re-melted to give optimum
Typical applications: Bearing Manufacture, CV joints, ball screws, gauges, knife etc.
Citric acid can be bought from drugstore (they use it in jelly or such to adjust acidity) but it is very expensive there. Therefore Finnish rodders buy it from some agriculture-store. It is not expensive. Officially it is used as pigs obstruent! I dipped those parts in citric acid for overnight, next day brushed it with wirebrush and flushed it with water. Then again back to citric acid over night and wirebrushed + flushed it next day.
Flushing is important, you’ll want to get all acid away, otherwise steel will turn to yellow.
You can’t use this method on all parts because of hydrogen embrittlement. So no pedals, frames, brake drums, engine blocks or such to citric acid!!! And yeah, parts should be clean -I’ve cleaned ‘em with fuel- because grease will neutralize acid. Ratio was 3%
Parts must be dried soon as you get them flushed, I quess you guys know why…
Music on the background:
Junior Brown; “Sugarfoot Rag”
Possibilities to comment this video was removed because answers to most of those questions can be found from this description. Been copy-pasting that text above too many times…
Also, too many people don’t seem to understand that there are other methods than just media/sand blasting…
Shanghai Bozhong Metallic Group was established in 2006, with 31 million registered fund, It is the main integrated operator of modern-day provider market for specialty stainless steel.It is the main building business of the Shanghai steel modern-day provider in depth pilot spot, which was set up by nation’s commerce ministry and Shanghai government.