Europe style for D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Manufacturer in Turkey

Europe style for
 D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Manufacturer in Turkey

Short Description:

1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    We always believe that one's character decides products' quality, the details decides products' quality ,with the REALISTIC,EFFICIENT AND INNOVATIVE team spirit for Europe style for D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Manufacturer in Turkey, Competitive price with high quality and satisfying service make us earned more customers.we wish to work with you and seek common development.


    1. Relevant D2 Steel Specifications

    Country USA German Japan
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404
    Grades D2 1.2379/X153CrMo12 SKD11

    2. D2 Tool Steel Chemical Composition

    ASTM A681 C Mn P S Si Cr V Mo
    D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2
    DIN ISO 4957 C Mn P S Si Cr V Mo
    1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1
    JIS G4404 C Mn P S Si Cr V Mo
    SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2

    3. AISI Grade D2 Steel Mechanical Properties

    Mechanical Properties Metric Imperial
    Hardness, Knoop (converted from Rockwell C hardness) 769 769
    Hardness, Rockwell C 62 62
    Hardness, Vickers 748 748
    Izod impact unnotched 77.0 J 56.8 ft-lb
    Poisson’s ratio 0.27-0.30 0.27-0.30
    Elastic modulus 190-210 GPa 27557-30457 ksi

    Thermal Properties

    Properties

    Conditions

    T (°C)

    Treatment

    Thermal expansion 10.4 x 10-6/ºC 20-100

    4. AISI/ASTM A681 D2 Grade Steel Forging

    Heating for forging of AISI D2 tool steel should
    be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
    as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
    die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
    should always be annealed after forging.

    5. D2 Tool Steel Heat Treatment

    • Heat Treatment

    ASTM  D2 steels alloy should be preheated very slowly to 815oC (1500oF) and  then temperature can be increased to 1010oC (1850oF). They are then held  at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).

    • Annealing

    Annealing  of D2 tool steels material should be done at 871 to 898oC (1600 to  1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or  less.after which cooling rate may be increased. Suitable precautions  must be taken to prevent excessive carburization or decarburization.

    • Stress Relieving

    When  desirable to relieve the strains of machining, heat D2 grade steel  slowly to 1050°-1250°F, allow to equalize, and then cool in still air  (Strain Relieving).

    • Preheat Prior To Hardening

    Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.

    • Hardening

    After  thorough preheating, heat to 1800°-1850°F. Hold the work piece at the  hardening temperature until it is completely and uniformly heated.

    • Quenching

    AISI  D2 steel tool material is an air hardening steel and will develop  hardness on cooling in still air. To avoid scaling and prevent  decarburization of the work piece surface, controlled atmosphere or  vacuum furnaces are recommended. If these furnaces are not available,  pack hardening, salt baths or wrapping the piece in stainless steel foil  will provide some degree of surface protection in the hardening  process. Parts should be allowed to cool to 150F, or to where they can  be held in the bare hand, and then temper immediately.

    • Tempering

    The  tempering temperature on material D2 steel may be varied according to  the desired hardness. D2 steels can be tempered at 204oC (400oF) for  achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell  C hardness of 54.

    6. D2 Tool Steel Material Application
     AISI grade D2 tool steels are used for long run tooling applications,  where wear resistance is important, such as blanking or forming dies and  thread rolling dies.

    Some main applications for D2 tool steel are as below:

    Blanking  Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long  Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls,  Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread  Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear  Parts.

    We usually hold D2 tool  steel on sale activities, and you would have our price on regular  schedule. Contact us and sign in our newsletter to have D2 tool steel  materials price list and commercial quote today.

  • Previous:
  • Next:



  • The video demonstrates short-term oxidation improvement of 410 stainless steel at high temperature after coating with Minimox® Self-Protective Alloy Treatment. Long-term oxidation resistance has also been displayed. After coating and suitable oxidation, the surface of the stainless steel is a beneficial combination of chromium oxide and chromium-manganese-oxygen spinel, even though there is no chromium or manganese in the Minimox® solution. The driving forces for surface diffusion are radically changed by the presence of Minimox Self-Protective Alloy Treatment. The alloy has become self-protective. Several other examples are presented.

    SEE OUR WEBSITE: http://www.Minimox.com to learn the details of the new patented Minimox solution for improving self-protection of aluminum, stainless steel, nickel and superalloys in elevated temperature and corrosive applications. Reduce material scaling & corrosion with a water-based treatment that can be applied in the field and inside complicated geometries.

    Also visit http://www.materialinterface.com to see all of our services.



    This Steel Detailing project involved the modification and renovation of 3 Hangars to accommodate maintenance of a C130 Hercules Aircraft.

    The scope included a roof replacement on three hangar buildings, 6 new interior mezzanines with handrail & ladders, 6 new stair towers with pivoting walk bridges for aircraft access, plus 3 new 160′ foot long box trusses and supporting tower structures for the new MegaDoors.

    Embedded into this video is a rendered and animated portion of our sds/2 model showing the pivoting and articulating aircraft access platform.

    Steel Detailing: Yes
    Engineering: No

    Music by: Bensound
    Title: Dream ambient track
    Source: www.bensound.com

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Star

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Heart