Discount wholesale D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory for Birmingham
1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade...
We are experienced manufacturer. Wining the majority of the crucial certifications of its market for Discount wholesale D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory for Birmingham, As we are moving forward, we keep an eye on our ever-expanding product range and make improvement to our services.
1. Relevant D2 Steel Specifications
|Standard||ASTM A681||DIN EN ISO 4957||JIS G4404|
2. D2 Tool Steel Chemical Composition
|DIN ISO 4957||C||Mn||P||S||Si||Cr||V||Mo|
3. AISI Grade D2 Steel Mechanical Properties
|Hardness, Knoop (converted from Rockwell C hardness)||769||769|
|Hardness, Rockwell C||62||62|
|Izod impact unnotched||77.0 J||56.8 ft-lb|
|Elastic modulus||190-210 GPa||27557-30457 ksi|
|Thermal expansion||10.4 x 10-6/ºC||20-100||
4. AISI/ASTM A681 D2 Grade Steel Forging
Heating for forging of AISI D2 tool steel should
be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
should always be annealed after forging.
5. D2 Tool Steel Heat Treatment
ASTM D2 steels alloy should be preheated very slowly to 815oC (1500oF) and then temperature can be increased to 1010oC (1850oF). They are then held at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).
Annealing of D2 tool steels material should be done at 871 to 898oC (1600 to 1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or less.after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.
When desirable to relieve the strains of machining, heat D2 grade steel slowly to 1050°-1250°F, allow to equalize, and then cool in still air (Strain Relieving).
Preheat Prior To Hardening
Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.
After thorough preheating, heat to 1800°-1850°F. Hold the work piece at the hardening temperature until it is completely and uniformly heated.
AISI D2 steel tool material is an air hardening steel and will develop hardness on cooling in still air. To avoid scaling and prevent decarburization of the work piece surface, controlled atmosphere or vacuum furnaces are recommended. If these furnaces are not available, pack hardening, salt baths or wrapping the piece in stainless steel foil will provide some degree of surface protection in the hardening process. Parts should be allowed to cool to 150F, or to where they can be held in the bare hand, and then temper immediately.
The tempering temperature on material D2 steel may be varied according to the desired hardness. D2 steels can be tempered at 204oC (400oF) for achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell C hardness of 54.
6. D2 Tool Steel Material Application
AISI grade D2 tool steels are used for long run tooling applications, where wear resistance is important, such as blanking or forming dies and thread rolling dies.
Some main applications for D2 tool steel are as below:
Blanking Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls, Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear Parts.
We usually hold D2 tool steel on sale activities, and you would have our price on regular schedule. Contact us and sign in our newsletter to have D2 tool steel materials price list and commercial quote today.
Qual-Fab, Inc., located in Avon, OH, fabricates personalized welded constructions for the metal processing and other industries. Normally meant for use in large temperature, corrosive environments, the weldments made at Qual-Fab are normally made from stainless and nickel alloys. Making top top quality welds is a sizeable aim for Gary Vanek, President and Matt Schatz, Welding Supervisor, CWI. Applying pulse Waveform Command Technology modes exclusively intended for each material, thickness, wire alloy, wire diameter and shielding gas, Qual-Fab is able to transfer item by way of the plant speedier and with higher top quality.
Yantai Haige Equipment Tools Co., Ltd, we are qualified company of metal round bar / wire rod floor finishing tools. We have more than 10 yrs seasoned in this industry.
Our products and solutions have been exported to Russia, India, North Korea, South Korea, Vietnam, Pakistan, Taiwan,and many others.
Our major products and solutions:
metal bar / seamless tube cnc peeling machine
metal bar / seamless tube semi-automated peeling machine
2-roll precision straightener for bright bar
2-roll prestraightener for black bar
bright metal automated creation line
wire rod -bar creation line
wire rod – wire rod creation line
merged drawing machine
abrasive belt grinder for metal bar
centerless grinder & loader and unloader
multi-roll straightening machine for part bar
skiving & roller burnishing machine for inside cylinder tube
piston rod polishing machine
electrical plating machine,
absolutely free forging machine, and many others.
Far more information and facts, please feel absolutely free to get in touch with us.