Discount wholesale ASTM 52100 Bearing Steel | 1.3505 | 100Cr6 | SUJ2 | EN31 in Palestine
ASTM A295 is specification which covers 52100 high carbon bearing quality steelto be used in the manufacture of anti-friction bearings. And 52100 bearing steel is the most common steel grade in ASTM A295 standard for high-carbon anti-friction bearing steel. What is 52100 bearing steel? AISI/ASTM 52100 bearing steel is a high carbon, chromium containing low alloysteel that is through hardening and noted in particular for use asbearings. 52100 bearing steel is one kind of special steel with ...
We depend on sturdy technical force and continually create sophisticated technologies to meet the demand of Discount wholesale ASTM 52100 Bearing Steel | 1.3505 | 100Cr6 | SUJ2 | EN31 in Palestine, We welcome customers, business associations and friends from all parts of the world to contact us and seek cooperation for mutual benefits.
is specification which covers 52100 high carbon bearing quality steel
to be used in the manufacture of anti-friction bearings. And is the most common steel grade in ASTM A295 standard for high-carbon anti-friction bearing steel.
What is 52100 bearing steel?
52100 bearing steel is a high carbon, chromium containing low alloy
steel that is through hardening and noted in particular for use as
52100 bearing steel is one kind of special steel with features of
high wear resistance and rolling fatigue strength. High-carbon chromium
bearing steel, engineering steel and some types of stainless steel and
heat resistant steel are used as materials of bearings and for other
Advantages of Chrome Bearing Steel 52100:
Superior hardness, 60-67 on Rockwell hardness scale (Rc) at room temperature
High carbon chrome alloy steel
Operates continually at temperatures up to 120°C
Used to produce precision ball bearings and roller bearings
Long working life
1. Relevant Steel Specification of ASTM 52100 Bearing Steel
|Standard||ASTM A295||DIN 17230|
2. Chemical Composition of 52100 Bearing Steel and Equivalents
3. Mechanical Properties of ASTM A295 52100 Bearing Steel
|Bulk modulus (typical for steel)||140 GPa||20300 ksi|
|Shear modulus (typical for steel)||80 GPa||11600 ksi|
|Elastic modulus||190-210 GPa||27557-30458 ksi|
|Hardness, Knoop (converted from Rockwell C hardness)||875||875|
|Hardness, Rockwell C (quenched in oil from 150°C tempered)||62||62|
|Hardness, Rockwell C (quenched in water from 150°C tempered)||64||64|
|Hardness, Rockwell C (quenched in oil)||64||64|
|Hardness, Rockwell C (quenched in water)||66||66|
|Hardness, Vickers (converted from Rockwell C hardness)||848||848|
|Machinability (spheroidized annealed and cold drawn. Based on 100 machinability for AISI 1212 steel)||40||40|
52100 Steel Physical Properties
|Density||7.81 g/cm3||0.282 lb/in³|
52100 Alloy Steel Thermal Properties
|Thermal expansion co-efficient (@ 23-280°C/73.4- 36°F, annealed)||11.9 µm/m°C||6.61 µin/in°F|
|Thermal conductivity (typical steel)||46.6 W/mK||323 BTU in/hr.ft².°F|
4. Forging of A295 52100 Bearing Steel
52100 alloy steel is forged at 927 to 1205°C, and should not be forged
below 925ºC. A post-forge equalization treatment is recommended at 745ºC
for 4-6 hours followed by air cooling for SAE/AISI 52100 steel.
6. Heat Treatment for ASTM 52100 Bearing Steel
52100 alloy bearing steel is heated at 816°C followed by quenching in
oil. Before performing this process, it is subjected to normalizing heat
treatment at 872°C followed by slowly cooling in order to reduce the
AISI 52100 bearing steels alloy can be hot worked at 205 to 538°C.
AISI 52100 bearing steel can be cold worked using conventional techniques in the annealed or normalized conditions.
For spheroidize anneale, the following isothermal anneal is recommended:
1500ºF (815ºC) for 3 hours
1350ºF (735ºC) for 4 hours
1250ºF (675ºC) for 3 hours
Slow cool to 1000ºF (540ºC) then air cool.
AISI 52100 alloy bearing steel could be hardened by quenching in water from 801-829 degree or quench in oil from 816-842 degree.
Temper to desired hardness as indicated by tempering curves after water or oil quench.
5. Applications of 52100 Bearing Steel
steel 52100 grade bearing steel is mainly used for the manufacture of
aircraft bearings and other highly stressed parts. This steel grade
52100 steel is preferably vacuum arc re-melted to give optimum
Typical applications: Bearing Manufacture, CV joints, ball screws, gauges, knife etc.
To come across out more about this assets click: http://fjlord.co.british isles/FJL035900643 or call Chiswick on 020 8747 8601 or E-Mail: email@example.com isles This great …
Shower Grates Benalla – The future of Plumbing and Stainless Grates!
Our Website: http://www.paigestainless.com.au/click-drain/
Google Business Page: https://plus.google.com/+PaigestainlessAustralia
See our product at 0:59
CLICK DRAIN™ developed using PAIGE STAINLESS HEELGUARD® has developed a full stainless steel drainage system using this centuries technology for ease of onsite fitting.
This patented product enables both builders and plumbers to basically style the drain on site as required, its clever and unique `click` together system has out let sections, joiner sections, change of direction sections and stop ends to create a drain for all site requirements.”
No one else has actually manufactured Heelguard to the Architectural Market for over Twenty Years to the Australian Design Requirement.
Monday-Friday: 9:00am – 5:00pm
YOU COULD REACH US THROUGH:
27 Cessna Drive, Caboolture QLD 4510, Australia
Tel: + 61 7 5499 1511
Fax: +617 5499 0741
Linear Surface Water Drainage
Platforms and Decks
FULL CUSTOM SYSTEMS ARE OUR SPECIALTY.