Competitive Price for ASTM 52100 Bearing Steel | 1.3505 | 100Cr6 | SUJ2 | EN31 Wholesale to Lebanon

Competitive Price for
 ASTM 52100 Bearing Steel | 1.3505 | 100Cr6 | SUJ2 | EN31 Wholesale to Lebanon

Short Description:

ASTM A295 is specification which covers 52100 high carbon bearing quality steelto be used in the manufacture of anti-friction bearings. And 52100 bearing steel is the most common steel grade in ASTM A295 standard for high-carbon anti-friction bearing steel. What is 52100 bearing steel? AISI/ASTM 52100 bearing steel is a high carbon, chromium containing low alloysteel that is through hardening and noted in particular for use asbearings. 52100 bearing steel is one kind of special steel with ...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    The company keeps to the operation concept "scientific management, high quality and efficiency primacy, customer supreme for Competitive Price for ASTM 52100 Bearing Steel | 1.3505 | 100Cr6 | SUJ2 | EN31 Wholesale to Lebanon, items won certifications with the regional and international primary authorities. For far more detailed information, please contact us!


    ASTM A295
    is specification which covers 52100 high carbon bearing quality steel
    to be used in the manufacture of anti-friction bearings. And 52100 bearing steel is the most common steel grade in ASTM A295 standard for high-carbon anti-friction bearing steel.

    What is 52100 bearing steel?

    AISI/ASTM
    52100 bearing steel is a high carbon, chromium containing low alloy
    steel that is through hardening and noted in particular for use as
    bearings.

    52100 bearing steel is one kind of special steel with features of
    high wear resistance and rolling fatigue strength. High-carbon chromium
    bearing steel, engineering steel and some types of stainless steel and
    heat resistant steel are used as materials of bearings and for other
    purposes.

    Advantages of Chrome Bearing Steel 52100:

    • Superior hardness, 60-67 on Rockwell hardness scale (Rc) at room temperature

    • High carbon chrome alloy steel

    • Operates continually at temperatures up to 120°C

    • Used to produce precision ball bearings and roller bearings

    • Cost-effective

    • Long working life

    1. Relevant Steel Specification of ASTM 52100 Bearing Steel

    Country USA German Japan British
    Standard ASTM A295 DIN 17230 JIS G4805 BS 970
    Grades 52100 100Cr6/1.3505 SUJ2 535A99/EN31

    2. Chemical Composition of 52100 Bearing Steel and Equivalents

    Standard Grade C Mn P S Si Ni Cr Cu Mo
    ASTM A295 52100 0.93-1.05 0.25-0.45 0.025 0.015 0.15-0.35 0.25 1.35-1.60 0.30 0.10
    DIN 17230 100Cr6/1.3505 0.90-1.05 0.25-0.45 0.030 0.025 0.15-0.35 0.30 1.35-1.65 0.30
    JIS G4805 SUJ2 0.95-1.10 0.50 0.025 0.025 0.15-0.35 1.30-1.60
    BS 970 535A99/EN31 0.95-1.10 0.40-0.70 0.10-0.35 1.20-1.60

    3. Mechanical Properties of ASTM A295 52100 Bearing Steel

    Properties Metric Imperial
    Bulk modulus (typical for steel) 140 GPa 20300 ksi
    Shear modulus (typical for steel) 80 GPa 11600 ksi
    Elastic modulus 190-210 GPa 27557-30458 ksi
    Poisson’s ratio 0.27-0.30 0.27-0.30
    Hardness, Brinell
    Hardness, Knoop (converted from Rockwell C hardness) 875 875
    Hardness, Rockwell C (quenched in oil from 150°C tempered) 62 62
    Hardness, Rockwell C (quenched in water from 150°C tempered) 64 64
    Hardness, Rockwell C (quenched in oil) 64 64
    Hardness, Rockwell C (quenched in water) 66 66
    Hardness, Vickers (converted from Rockwell C hardness) 848 848
    Machinability (spheroidized annealed and cold drawn. Based on 100 machinability for AISI 1212 steel) 40 40
    • 52100 Steel Physical Properties

    Properties Metric Imperial
    Density 7.81 g/cm3 0.282 lb/in³
    Melting point 1424°C 2595°F
    • 52100 Alloy Steel Thermal Properties

    Properties Metric Imperial
    Thermal expansion co-efficient (@ 23-280°C/73.4- 36°F, annealed) 11.9 µm/m°C 6.61 µin/in°F
    Thermal conductivity (typical steel) 46.6 W/mK 323 BTU in/hr.ft².°F

    4. Forging of A295 52100 Bearing Steel

    AISI
    52100 alloy steel is forged at 927 to 1205°C, and should not be forged
    below 925ºC. A post-forge equalization treatment is recommended at 745ºC
    for 4-6 hours followed by air cooling for SAE/AISI 52100 steel.

    6. Heat Treatment for ASTM 52100 Bearing Steel

    ASTM/AISI
    52100 alloy bearing steel is heated at 816°C followed by quenching in
    oil. Before performing this process, it is subjected to normalizing heat
    treatment at 872°C followed by slowly cooling in order to reduce the
    machining stress.

    Hot Working

    AISI 52100 bearing steels alloy can be hot worked at 205 to 538°C.

    Cold Working

    AISI 52100 bearing steel can be cold worked using conventional techniques in the annealed or normalized conditions.

    Annealing

    For spheroidize anneale, the following isothermal anneal is recommended:

    • 1500ºF (815ºC) for 3 hours

    • 1350ºF (735ºC) for 4 hours

    • 1250ºF (675ºC) for 3 hours

    • Slow cool to 1000ºF (540ºC) then air cool.

    Quenching

    AISI 52100 alloy bearing steel could be hardened by quenching in water from 801-829 degree or quench in oil from 816-842 degree.

    Tempering

    Temper to desired hardness as indicated by tempering curves after water or oil quench.

    5. Applications of 52100 Bearing Steel

    Alloy
    steel 52100 grade bearing steel is mainly used for the manufacture of
    aircraft bearings and other highly stressed parts. This steel grade
    52100 steel is preferably vacuum arc re-melted to give optimum
    performance.

    Typical applications: Bearing Manufacture, CV joints, ball screws, gauges, knife etc.

  • Previous:
  • Next:



  • Blacksmithing – Forging – How To Twist Metal Bars Using A Forge

    Modern Day Blacksmith

    Modern Day Blacksmith, Ryan Feeney, demonstrates how to do a fundamental metal working skill: a basic twist of metal bars using a forge.

    In this video you’ll learn:
    -What temperature you’ll need to heat the metal
    -How to twist and handle metals of different widths.
    -What tools you’ll need to twist metal bars

    Ryan also shows how to do two types of metal twists:
    -A tight twist
    -A long twist

    Both can be accomplished depending on tool placement, pressure and technique.

    This is the perfect introduction for people new to metal working that want to pick up new skills, or learn the fundamentals.

    Modern Day Blacksmith follows Ryan and Don through their daily production of custom furniture, statues, railings, tables, oven hoods, railings, bar stools, and any other project their clients come up with. Don is a master of all wood types, and prides himself on his production of custom furniture, while Ryan is the self proclaimed Master of Metal and prides himself on his production of statues and other works involving steel, bronze, aluminum or any other kind of metal.

    Both men pride themselves on their knowledge of beer consumption and ridiculing the other one.

    Modern Day Blacksmith features them making their projects, but it also gives helpful tips for other metal and wood workers in the industry. It also includes their antics around the shops whether it be making fun of the way they dress, settling their disagreements through “Skills Challenges”, or blowing up something with fire, guns or dynamite.

    All Productions TV Facebook

    https://www.facebook.com/allproductionstv/

    All Productions Instagram

    https://www.instagram.com/all_productions_indy/

    All Productions TV Youtube Channel

    https://www.youtube.com/channel/UCue4Rxm3kUocn4zYegR41Ag

    Around the Shop-Modern Day Blacksmith

    https://www.youtube.com/playlist?list=PLb1i7M44t3kwWs4H7XsSm1bCU6c2v0J7o

    How To Metal-Modern Day Blacksmith

    https://www.youtube.com/playlist?list=PLb1i7M44t3kxoMq32laN03WlsMYx70SXP



    site:http://www.steelsino.com
    Shanghai Bozhong Steel Team was established in 2006, with 31 million registered fund, It is the primary integrated operator of present day services business for specialty stainless metal.It is the core design corporation of the Shanghai metal present day services complete pilot space, which was established up by nation’s commerce ministry and Shanghai authorities.

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Car

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Truck