Chinese wholesale D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Wholesale to Rotterdam

Chinese wholesale
 D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Wholesale to Rotterdam

Short Description:

1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    Our products are widely recognized and trusted by users and can meet continuously developing economic and social needs for Chinese wholesale D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Wholesale to Rotterdam, winning customers' trust is the gold key to our success! If you are interested in our products, please feel free to visit our web site or contact us.


    1. Relevant D2 Steel Specifications

    Country USA German Japan
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404
    Grades D2 1.2379/X153CrMo12 SKD11

    2. D2 Tool Steel Chemical Composition

    ASTM A681 C Mn P S Si Cr V Mo
    D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2
    DIN ISO 4957 C Mn P S Si Cr V Mo
    1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1
    JIS G4404 C Mn P S Si Cr V Mo
    SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2

    3. AISI Grade D2 Steel Mechanical Properties

    Mechanical Properties Metric Imperial
    Hardness, Knoop (converted from Rockwell C hardness) 769 769
    Hardness, Rockwell C 62 62
    Hardness, Vickers 748 748
    Izod impact unnotched 77.0 J 56.8 ft-lb
    Poisson’s ratio 0.27-0.30 0.27-0.30
    Elastic modulus 190-210 GPa 27557-30457 ksi

    Thermal Properties

    Properties

    Conditions

    T (°C)

    Treatment

    Thermal expansion 10.4 x 10-6/ºC 20-100

    4. AISI/ASTM A681 D2 Grade Steel Forging

    Heating for forging of AISI D2 tool steel should
    be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
    as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
    die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
    should always be annealed after forging.

    5. D2 Tool Steel Heat Treatment

    • Heat Treatment

    ASTM  D2 steels alloy should be preheated very slowly to 815oC (1500oF) and  then temperature can be increased to 1010oC (1850oF). They are then held  at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).

    • Annealing

    Annealing  of D2 tool steels material should be done at 871 to 898oC (1600 to  1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or  less.after which cooling rate may be increased. Suitable precautions  must be taken to prevent excessive carburization or decarburization.

    • Stress Relieving

    When  desirable to relieve the strains of machining, heat D2 grade steel  slowly to 1050°-1250°F, allow to equalize, and then cool in still air  (Strain Relieving).

    • Preheat Prior To Hardening

    Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.

    • Hardening

    After  thorough preheating, heat to 1800°-1850°F. Hold the work piece at the  hardening temperature until it is completely and uniformly heated.

    • Quenching

    AISI  D2 steel tool material is an air hardening steel and will develop  hardness on cooling in still air. To avoid scaling and prevent  decarburization of the work piece surface, controlled atmosphere or  vacuum furnaces are recommended. If these furnaces are not available,  pack hardening, salt baths or wrapping the piece in stainless steel foil  will provide some degree of surface protection in the hardening  process. Parts should be allowed to cool to 150F, or to where they can  be held in the bare hand, and then temper immediately.

    • Tempering

    The  tempering temperature on material D2 steel may be varied according to  the desired hardness. D2 steels can be tempered at 204oC (400oF) for  achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell  C hardness of 54.

    6. D2 Tool Steel Material Application
     AISI grade D2 tool steels are used for long run tooling applications,  where wear resistance is important, such as blanking or forming dies and  thread rolling dies.

    Some main applications for D2 tool steel are as below:

    Blanking  Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long  Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls,  Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread  Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear  Parts.

    We usually hold D2 tool  steel on sale activities, and you would have our price on regular  schedule. Contact us and sign in our newsletter to have D2 tool steel  materials price list and commercial quote today.

  • Previous:
  • Next:



  • A GEI típusú, kényszerlevegő ellátású gyújtóégő család azonos névleges hőteljesítményű, de különböző beépítési hosszúságú tagokból áll. Az általános felhasználású égőcsalád elsődleges alkalmazási területét az olajfinomítói csőkemencék jelentik.

    A gyújtóégő rendeltetése, alkalmazási területe

    A gyújtóégő különféle főégőkhöz rendelt, folyamatos üzemeltetésre is alkalmas gyújtóégő (őrlángégő funkció), mely a vonatkozó műszaki peremfeltételek között a főégőt

    - üzem indításkor begyújtja,
    - folyamatos üzemével elláthatja az égésbiztosítását.

    Általános alkalmazási területe ipari kazánok, egyéb hőhasznosítók, kemencék, kényszerlevegős vagy injektoros égői, melyek begyújtási feltételei megfelelnek a technológiai utasításoknak és az érvényes biztonságtechnikai előírásoknak egyaránt.
    A tüzelőanyaggal érintkező szerkezeti részek korrózióálló acélból, a gyújtóégő lángjával érintkező szerkezeti részek pedig hőálló acélból vannak kialakítva.

    The pilot burner household of forced air layout kind GEI is consisting of equivalent capacity,
    but of several size users. The principal scope of application of these pilot
    burners is the pipe-stills of oil refineries.

    Goal and field of application of the pilot burner
    The pilot burner is connected to several most important burners, in buy to be certain the functionality
    of ignition burner (pilot burner functionality) delivering beneath the presented technical
    ailments
    - start out-up of the ignition,
    - trying to keep-up as a result of its ongoing operation protected combustion.
    It can be used by industrial boilers, by warmth restoration amenities, furnaces forced-air
    or injector kind burners, by which the ignition ailments are in compliance with the
    legitimate protection specifications. The burner elements owning call with the gas, are
    made of stainless metal, the burner components making contact with the flame are designed of warmth
    resistant metal.



    The new 695 OS Iron is designed for the mid to low handicap players seeking a solid, clean look with the softer feel of a 8620 carbon steel form forged iron. The updated designs offer added weight to the lower heel and toe areas for lower CG and stability on off-centre hits. It has minimal offset and slightly rounded toe preferred by better players.

    The faces are skimmed-milled for flatness and scorelines are CNC-milled to exact specifications.

    The 695 OS Iron includes the innovative Hosel Weight Port System which is the cleanest most professional method for adding weight by using lead power or hosel weights

    Available in 4 Iron to Approach Wedge

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Plane

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Tree