China Wholesale for AISI 4340 Steel | 36CrNiMo4 | 1.6511 | EN24 | 817M40 | SNCM439 Factory for Gabon
AISI 4340 steel is a medium carbon, low alloy steel known for its toughness andstrength in relatively large sections. AISI 4340 is also one kind ofnickel chromium molybdenum steels. 4340 alloy steel is generallysupplied hardened and tempered in the tensile range of 930 – 1080 Mpa.Pre hardened and tempered 4340 steels can be further surface hardened by flame or induction hardening and by nitriding. The 4340 steel has goodshock and impact resistance as well as wear and abrasion resistanc...
The customer satisfaction is our primary target. We uphold a consistent level of professionalism, quality, credibility and service for
China Wholesale for AISI 4340 Steel | 36CrNiMo4 | 1.6511 | EN24 | 817M40 | SNCM439 Factory for Gabon, We sincerely welcome both foreign and domestic business partners, and hope to work with you in the near future!
is a medium carbon, low alloy steel known for its toughness and
strength in relatively large sections. AISI 4340 is also one kind of
nickel chromium molybdenum steels. 4340 alloy steel is generally
supplied hardened and tempered in the tensile range of 930 – 1080 Mpa.
Pre hardened and tempered 4340 steels can be further surface hardened by
flame or induction hardening and by nitriding. The 4340 steel has good
shock and impact resistance as well as wear and abrasion resistance in
the hardened condition. AISI 4340 steel properties offer good ductility
in the annealed condition, allowing it to be bent or formed. Fusion and
resistance welding is also possible with our 4340 alloy steel. ASTM 4340
material is often utilized where other alloy steels do not have the
hardenability to give the strength required. For highly stressed parts
it is excellent choice. AISI 4340 alloy steel can also be machined by
all customary methods.
Due to availability the ASTM 4340 grade steel is often substituted
with European based standards 817M40/EN24 and 1.6511/36CrNiMo4 or Japan
based SNCM439 steel. You have the detailed data of 4340 steel below.
1. AISI 4340 Steel Specification and Relevant Standards
|Standard||EN 10250||JIS G4103|
2. ASTM 4340 Steels And Equilvalents Chemical Composition
|JIS G4103||SNCM 439/SNCM8||0.36-0.43||0.60-0.90||0.030||0.030||0.15-0.35||1.60-2.00||0.60-1.00||0.15-0.30|
3. AISI Alloy 4140 Steel Mechanical Properties
(Heat Treated Condition )
|Tensile Strength MPa||Yield Strength
|Thermal expansion co-efficient (20°C/68°F, specimen oil hardened, 600°C (1110°F) temper||12.3 µm/m°C||6.83 µin/in°F|
|Thermal conductivity (typical steel)||44.5 W/mK||309 BTU in/hr.ft².°F|
4. Forging of 4340 Alloy Steel
the steel 4340 first, heat up to 1150°C – 1200°C maximum for forging,
hold until temperature is uniform throughout the section.
Do not forge
below 850 °C. 4340 has good forging characteristics but care must be
taken when cooling as the steel shows susceptibility to cracking.
Following forging operation the work piece should be cooled as slowly as
possible. And cooling in in sand or dry lime is recommended etc.
5. AISI 4340 Steel Grade Heat Treatment
pre-hardened steel stress relieving is achieved by heating steel 4340
to between 500 to 550°C. Heat to 600 °C – 650 °C, hold until temperature
is uniform throughout the section, soak for 1 hour per 25 mm section,
and cool in still air.
full anneal may be done at 844°C (1550 F) followed by controlled
(furnace) cooling at a rate not faster than 10°C (50 F) per hour down to
315°C (600 F). From 315°C 600 F it may be air cooled.
4340 alloy steel should be in the heat treated or normalized and heat
treated condition before tempering. The tempering temperature for
depends upon the strength level desired. For strength levels in the 260 –
280 ksi range temper at 232°C (450 F). For strength in the 125 – 200
ksi range temper at 510°C (950 F). And don’t temper the 4340 steels if
it is in the 220 – 260 ksi strength range as tempering can result in
degradation of impact resistance for this level of strength.
Tempering should be avoided if possible within the range 250 °C – 450 °C due to temper brittleness.
Flame or Induction Hardening
As mentioned above, pre-hardened and tempered 4340 steel bars or plates can be further surface hardened by either the flame or induction hardening
methods resulting in a case hardness in excess of Rc 50. AISI 4340
steel parts should be heated as quickly as possible to the austenitic
temperature range (830 °C – 860 °C) and required case depth followed by
an immediate oil or water quenching, depending upon hardness required,
workpiece size/shape and quenching arrangements.
quenching to hand warm, tempering at 150°C – 200°C will reduce stresses
in the case with minimal effect on its hardness.
All de-carburised surface material must first be removed to ensure best results.
and tempered 4340 alloy steel can also be nitrided, giving a surface
hardness of up to Rc 60. Heat to 500°C – 530°C and hold for sufficient
time (from 10 to 60 hours) to develop the depth of case. Nitriding
should be followed by slow cooling (no quench) reducing the problem of
distortion. The nitrided grade 4340 materials can therefore be machined
to near final size, leaving a small grinding allowance only. The tensile
strength of the 4340 steel material core is usually not affected since
the nitriding temperature range is generally below the original
tempering temperature employed.
Surface hardness achievable is 600 to 650HV.
is best done with the alloy steel 4340 in the annealed or normalized
and tempered condition. It can be readily machined by all conventional
methods such as sawing, turning, drilling etc. However in the high
strength conditions of 200 ksi or greater the machinability is only from
25% to 10% that of the alloy in the annealed condition.
of steel 4340 in the hardened and tempered condition (as normally
supplied), is not recommended and should be avoided if at all possible,
because of the danger of quench cracking, as the mechanical properties
will be altered within the weld heat affected zone.
must be carried out, pre-heat to 200 to 300°C and maintain this while
welding. Immediately after welding stress relieve at 550 to 650°C, prior
to hardening and tempering.
If welding in the hardened and
tempered condition is really necessary, then the work piece, immediately
on cooling to hand warm, should be if possible stress relieved at 15 °C
below the original tempering temperature.
8. Application of 4340 Steel
4340 steel is used in most industry sectors for applications requiring
higher tensile/yield strength than 4140 steel can provide.
Some typical applications such as:
Aircraft Landing Gear
Oil and Gas Drilling,
Warm and Cold Forming,
Transfer Systems, like power transmission gears and shafts.
engineering industries and structural use applications, such as: heavy
duty shafts, gears, axles, spindles, couplings, pins, chucks, molds etc.
TCM BALER：http://www.tcmbaler.com/ a professional manufacturer, specialize in hydraulic compressing machine/ baling press compactor/pressing baler for more than 15years, Our products are applicable for waste cardboard/ cardbox, OCC, plastic bottles ,fiber, rags,wipers,used clothes/clothing,textiles, cotton, newspaper, kraft paper, scrap metal, mattress spring, scrap car body, heavy steel etc. plays a big role in recycling industry, welcomed by domestic and national customers.
1.Fully automatic horizontal baling press
2.Semi-automatic horizontal baling press
3.vertical baling press baler
4.wipers/rags bagging press baler
5.scrap metal baling compactor
6.shearing baler machine
8.movable scrap metal baler compactor
9.single shaft shredder
10.double shaft shredder
Tel: 0086 -21-61522014
Hydraulic Drive Baler, Hydraulic Drive Baler Suppliers and Armenia, Waste Metal Baler, Hydraulic Drive Baler, Wholesale Various High Quality Hydraulic Drive Baler Products from Global Hydraulic Drive Baler Suppliers and Hydraulic Drive Baler Factory, , Metal Baler Machine, Nice Hydraulic Plastic Plastic Baler Machine China Bulgaria, hydraulic metal baler y83 160, Nice Hydraulic Plastic Plastic Baler Machine China Supplier, Driven Type: Hydraulic, Hydraulic. High quality hydraulic scrap steel wire baler machine, Pine Straw Baler For Sale, Hydraulic waste copper wire baler scrap metal baler0086 Cameroon, Metal Scraps Horizontal Hydraulic Baler For Sale, Hydraulic waste copper wire baler scrap metal This machine mainly used in steel plants, recyling corportation Hydraulic drive for all machine types, , iron scrap baler, Hydraulic Baling Machine For Scrap Metal, Engineering Denmark, Hydraulic Metal Press Baler, Mixed Light Scrap Metals Scrap Aluminum Window Scrap Steel Wire Driven type system hydraulic drive Hydraulic scrap metal balers Y81 630, Hydraulic Scrap Metal Shear Baler Machine, paper compactor hydraulic driven baler Dominica, Scrap Steel Baler, Driven Type: Hydraulic, eliminating hydraulic material:steel wire, hydraulic baler straw hay press machine renewable building materials products coarse, Aluminum Can Press Machine, PC Series Auto Tie Horizontal Baler Marathon Ecuador, Mobile Scrap Metal Baler With Diesel Engine Power, PC Series Auto Tie Horizontal Baler positioners direct the wire through the tier. The gear driven twisters are driven by hydraulic motors. The chute type in, Scrapped Metal Baler, american hydraulic cardboard baler wire supplier, price of Spain, Metal Baler Manufacturer, hydraulic cardboard baler wire Specialized Rebar Tie Wire for Baling Rrced Steel Bar alabama wire, pp belt, etc Driven Type: Hydraulic, Scrap Stainless Baling Press, metal wire press baler manufacturer, price of metal wire Micronesia, metal scrap balers hc81f 2500, Metal, steel wire, rope, etc Type: Other Driven Type: Hydraulic baler by given weight Driven Type: Hydraulic Tags: Wire Steel Press Baler, metal scrap baler machine, Hydraulic Metal Baler. 9, Scrap Metal Balers Equipment Faroe Islands, scrap steel baler machine, such as cuboid type, Hydraulic metal baler can be applied in steel mills, Driven by hydraulic system, stable operation, , Scrap Metel Baler, Hydraulic Metal Baler Recycling Machines Britain, Scrap Material Baler Baling Machine, Hydraulic metal baler can be driven by diesel engine for Hydraulic metal baler can be applied in steel mills, Type of Bale Out of Hydraulic Metal Baler 1., Hydraulic Scrap Metal Baling Press Machine, hydraulic driven baler, price of hydraulic driven baler in Guynea, Scrap Metal Pressing Machine, hydraulic driven baler Manufacturers, Suppliers and Exporters. Hydraulic Baler, Hydraulic Baler Suppliers and Alibaba. Application:Waste Bandage Compress Baler, Cost Of Horizontal Metal Baler, Baler machine for used clothing Alibaba Greece, Hydraulic Automatic Scrap Baler, Baler machine for used clothing, US $ 3, 500 15, 000 Set, Driven Type: Hydraulic, Voltage: 380V, Power: Steel wire. etc. PET strap. Steel wire., Stainless Metal Baler, Car Tire Baler, Truck Tire Baling Press, Tyre Baler Machines Haiti, Steel Metal Baler For Recycling Plant, Standard Heavy Duty Baler for High Rebound Material eg. Tire Balers Steel Wire. SVB2 TB 1500 Hydraulic driven Chamber Door ensures operational safety and, Safe Tin Can Scrap Baler, Large Automatic Hydraulic Metal Shears, 400 1250 Ton India, Waste Manual Control Metal Tins cans Baler, Large Automatic Hydraulic Metal Shears, 400 scrap iron, wire steel, etc. Driven Type: Hydraulic. Voltage:, Scrap Tin Cans Baler, Quality Scrap Baler Machine Plastic Baling Machine Iran, Small Tin Can Baler, Scrap Baler Machine Plastic Baling Machine. Driven Type: Hydraulic, Voltage: 25 Mpa, Customized, Production
“FD Grip” The No.1 earthquake-resistant rebar coupler in Japan, the highest seismic country,
for over 30 years.