Chemical Composition of Stainless Steel 304 Table 1. Chemical composition for 304 stainless steel alloys % 304 304L 304H C 0.0 – 0.07 0.0 – 0.03 0.04 – 0.08 Mn 0.0 – 2.0 0.0 – 2.00 0.0 – 2.0 Si 0.0 – 1.00 0.0 – 1.00 0.0 – 1.0 P 0.0 – 0.05 0.0 – 0.05 0.0 – 0.04 S 0.0 – 0.03 0.0 – 0.02 0.0 – 0.02 Cr 17.50 – 19.50 17.50 – 19.50 ...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    Our company since its inception, always regards product quality as enterprise life, continuously improve production technology, improve product quality and continuously strengthen enterprise total quality management, in strict accordance with the national standard ISO 9001:2000 for China Factory for AISI304| SUS304| EN1.4948 Factory for Czech Republic, We sincerely look forward to hearing from you. Give us a chance to show you our professionalism and passion.


    Chemical Composition of Stainless Steel 304

    Table 1. Chemical composition for 304 stainless steel alloys

    %

    304

    304L

    304H

    C

    0.0 – 0.07

    0.0 – 0.03

    0.04 – 0.08

    Mn

    0.0 – 2.0

    0.0 – 2.00

    0.0 – 2.0

    Si

    0.0 – 1.00

    0.0 – 1.00

    0.0 – 1.0

    P

    0.0 – 0.05

    0.0 – 0.05

    0.0 – 0.04

    S

    0.0 – 0.03

    0.0 – 0.02

    0.0 – 0.02

    Cr

    17.50 – 19.50

    17.50 – 19.50

    17.00 – 19.00

    Ni

    8.00 – 10.50

    8.00 – 10.50

    8.00 – 11.00

    Fe

    Balance

    Balance

    Balance

    N

    0.0-0.11

    0.0-0.11

    0.0 – 0.10

    Properties of Stainless Steel 304

    Mechanical Properties of Stainless Steel 304

    Table 2a. Mechanical properties for 304 stainless steel alloys – sheet up to 8 mm thick

    Grade

    304

    304L

    304H

    Tensile Strength (MPa)

    540 – 750

    520 – 700

    -

    Proof Stress (MPa)

    230 Min

    220 Min

    -

    Elongation A50 mm

    45 Min %

    45 Min %

    -


    Table 2b. Mechanical properties for 304 stainless steel alloys – plate from 8 – 75 mm thick

    Grade

    304

    304L

    304H

    Tensile Strength (MPa)

    520 – 720

    500 – 700

    -

    Proof Stress (MPa)

    210 Min

    200 Min

    -

    Elongation A5

    45 Min %

    45 Min %

    -


    Table 2c. Mechanical properties for 304 stainless steel alloys – bar and section up to 160 mm diameter / thickness

    Grade

    304

    304L

    304H

    Tensile Strength (MPa)

    500 – 700

    500 – 700

    500 – 700

    Proof Stress (MPa)

    190

    175 Min

    185 Min

    Elongation A50 mm

    45 Min %

    45 Min %

    40 Min %

    Hardness Brinell

    215 Max HB

    215 Max HB

    -

    Physical Properties of Stainless Steel 304

    Table 3. Physical properties for 304 stainless steel alloys

    Property

    Value

    Density

    8.00 g/cm3

    Melting Point

    1450 °C

    Modulus of Elasticity

    193 GPa

    Electrical Resistivity

    0.072 x 10-6 Ω.m

    Thermal Conductivity

    16.2 W/m.K

    Thermal Expansion

    17.2 x 10-6 /K

    Alloy Designations

    Stainless steel 304 also corresponds to the following standard designations and specifications:

    Euronorm

    UNS

    BS

    En

    Grade

    1.4301

    S30400

    304S15

    304S16

    304S31

    58E

    304

    1.4306

    S30403

    304S11

    -

    304L

    1.4307

    -

    304S11

    -

    304L

    1.4311

    -

    304S11

    -

    304L

    1.4948

    S30409

    304S51

    -

    304H

    Corrosion Resistance of Stainless Steel 304

    Stainless steel 304
    has excellent corrosion resistance in a wide variety of environments
    and when in contact with different corrosive media. Pitting and crevice
    corrosion can occur in environments containing chlorides. Stress
    corrosion cracking can occur at temperatures over 60°C.

    Heat Resistance of Stainless Steel 304

    Stainless steel 304 has
    good resistance to oxidation in intermittent service up to 870°C and in
    continuous service to 925°C. However, continuous use at 425-860°C is
    not recommended if corrosion resistance in water is required. In this
    instance 304L is recommended due to its resistance to carbide
    precipitation.

    Where high strength is required at temperatures above 500°C and up to
    800°C, grade 304H is recommended. This material will retain aqueous
    corrosion resistance.

    Fabrication of Stainless Steel 304

    Fabrication of all stainless steels should
    be done only with tools dedicated to stainless steel materials. Tooling
    and work surfaces must be thoroughly cleaned before use. These
    precautions are necessary to avoid cross contamination of stainless steel by easily corroded metals that may discolour the surface of the fabricated product.

    Cold Working of Stainless Steel 304

    Stainless steel 304 readily
    work hardens. Fabrication methods involving cold working may require an
    intermediate annealing stage to alleviate work hardening and avoid
    tearing or cracking. At the completion of fabrication a full annealing
    operation should be employed to reduce internal stresses and optimise
    corrosion resistance.

    Hot Working of Stainless Steel 304

    Fabrication methods, like forging, that involve hot working should
    occur after uniform heating to 1149-1260°C. The fabricated components
    should then be rapidly cooled to ensure maximum corrosion resistance.

    Heat Treatment of Stainless Steel 304

    Stainless steel 304 cannot be hardened by heat treatment.

    Solution treatment or annealing can be done by rapid cooling after heating to 1010-1120°C.

    Machinability

    Stainless steel 304 has good machinability. Machining can be enhanced by using the following rules:

    • Cutting edges must be kept sharp. Dull edges cause excess work hardening.

    • Cuts should be light but deep enough to prevent work hardening by riding on the surface of the material.

    • Chip breakers should be employed to assist in ensuring swarf remains clear of the work

    • Low thermal conductivity of austenitic alloys results in heat
      concentrating at the cutting edges. This means coolants and lubricants
      are necessary and must be used in large quantities.

    Welding of Stainless Steel 304

    Fusion welding performance for Stainless steel 304 is excellent both with and without fillers. Recommended filler rods and electrodes for stainless steel 304 is grade 308 stainless steel.
    For 304L the recommended filler is 308L. Heavy welded sections may
    require post-weld annealing. This step is not required for 304L. Grade
    321 may be used if post-weld heat treatment is not possible.

    Applications of Stainless Steel 304

    Stainless steel 304 is typically used in:

    • Sinks and splashbacks

    • Saucepans

    • Cutlery and flatware

    • Architectural panelling

    • Sanitaryware and troughs

    • Tubing

    • Brewery, dairy, food and pharmaceutical production equipment

    • Springs, nuts, bolts and screws

  • Previous:
  • Next:



  • In this video I show you the Online Shopping for Kitchen Utensils amp; Gadgets from a great selection at everyday low prices.. For more details please visit: http://po.st/g8ibHZ Thank You!

    Great King International Stainless Steel Spice Box wit Review
    King International Stainless Steel Spice Box wit Test
    King International Stainless Steel Spice Box wit Unboxing
    Review King International Stainless Steel Spice Box wit Hands-on

    https://www.youtube.com/watch?v=I_QNbDLG3Fc



    THIS PROCESS CAN BE DANGEROUS! WEAR GAUNTLETS, SAFETY GOGGLES AND AN APRON AT ALL TIMES!

    Heat-treating a knife blade is actually quite simple, if you just follow ‘the recipe’. There’s lots of overly-complicated recipes floating around, so I thought I would show you a method that I’ve used and proven for O1 tool steel.

    Here’s a list of tools that you’ll need:

    O1 Tool Steel: http://amzn.to/1vF0nSo
    Channel Locks: http://amzn.to/1DiN9vw
    Bernzomatic MAPP torch: http://amzn.to/1wiHkvS
    Canola Oil (get 3 or 4): http://amzn.to/1tzQGEF
    Quenching container: http://amzn.to/1sXnsNX
    Leather gloves: http://amzn.to/1wdYb0R
    Safety goggles: http://amzn.to/1FcU7UA

    2 Brick forge instructions: http://www.bladeforums.com/forums/showthread.php/920120-Virtual-BBQ-2-Brick-Forge-WIP
    (K23 firebricks for 2 brick forge, you can get these cheaper locally): http://amzn.to/1waUvhl

    PLEASE NOTE: Doing things of this nature can be extremely dangerous. Use common sense and take every safety precaution to make sure you’re not injured.

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Car

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Cup