China Cheap price D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory in Qatar

China Cheap price
 D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory in Qatar

Short Description:

1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    abide by the contract", conforms to the market requirement, joins in the market competition by its high quality as well as provides more comprehensive and excellent service for clients to let them become big winner. The pursue of the company, is the clients' satisfaction for China Cheap price D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory in Qatar, We sincerely welcome domestic and foreign merchants who calls, letters asking, or to plants to negotiate, we will offer you quality products and the most enthusiastic service,We look forward to your visit and your cooperation.


    1. Relevant D2 Steel Specifications

    Country USA German Japan
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404
    Grades D2 1.2379/X153CrMo12 SKD11

    2. D2 Tool Steel Chemical Composition

    ASTM A681 C Mn P S Si Cr V Mo
    D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2
    DIN ISO 4957 C Mn P S Si Cr V Mo
    1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1
    JIS G4404 C Mn P S Si Cr V Mo
    SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2

    3. AISI Grade D2 Steel Mechanical Properties

    Mechanical Properties Metric Imperial
    Hardness, Knoop (converted from Rockwell C hardness) 769 769
    Hardness, Rockwell C 62 62
    Hardness, Vickers 748 748
    Izod impact unnotched 77.0 J 56.8 ft-lb
    Poisson’s ratio 0.27-0.30 0.27-0.30
    Elastic modulus 190-210 GPa 27557-30457 ksi

    Thermal Properties

    Properties

    Conditions

    T (°C)

    Treatment

    Thermal expansion 10.4 x 10-6/ºC 20-100

    4. AISI/ASTM A681 D2 Grade Steel Forging

    Heating for forging of AISI D2 tool steel should
    be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
    as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
    die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
    should always be annealed after forging.

    5. D2 Tool Steel Heat Treatment

    • Heat Treatment

    ASTM  D2 steels alloy should be preheated very slowly to 815oC (1500oF) and  then temperature can be increased to 1010oC (1850oF). They are then held  at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).

    • Annealing

    Annealing  of D2 tool steels material should be done at 871 to 898oC (1600 to  1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or  less.after which cooling rate may be increased. Suitable precautions  must be taken to prevent excessive carburization or decarburization.

    • Stress Relieving

    When  desirable to relieve the strains of machining, heat D2 grade steel  slowly to 1050°-1250°F, allow to equalize, and then cool in still air  (Strain Relieving).

    • Preheat Prior To Hardening

    Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.

    • Hardening

    After  thorough preheating, heat to 1800°-1850°F. Hold the work piece at the  hardening temperature until it is completely and uniformly heated.

    • Quenching

    AISI  D2 steel tool material is an air hardening steel and will develop  hardness on cooling in still air. To avoid scaling and prevent  decarburization of the work piece surface, controlled atmosphere or  vacuum furnaces are recommended. If these furnaces are not available,  pack hardening, salt baths or wrapping the piece in stainless steel foil  will provide some degree of surface protection in the hardening  process. Parts should be allowed to cool to 150F, or to where they can  be held in the bare hand, and then temper immediately.

    • Tempering

    The  tempering temperature on material D2 steel may be varied according to  the desired hardness. D2 steels can be tempered at 204oC (400oF) for  achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell  C hardness of 54.

    6. D2 Tool Steel Material Application
     AISI grade D2 tool steels are used for long run tooling applications,  where wear resistance is important, such as blanking or forming dies and  thread rolling dies.

    Some main applications for D2 tool steel are as below:

    Blanking  Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long  Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls,  Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread  Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear  Parts.

    We usually hold D2 tool  steel on sale activities, and you would have our price on regular  schedule. Contact us and sign in our newsletter to have D2 tool steel  materials price list and commercial quote today.

  • Previous:
  • Next:



  • A look at the open die forging process in action, as custom open die forging company Great Lakes Forge produces a forged rectangle, and a forged steel round.

    The super heated steel is pulled from the industrial oven and put onto the open die forge where it is positioned and forged into shape. Unlike closed die forging the metal is not confined on the sides by dies during the forging process. With open die forging you are able to create almost any shape desired and almost unlimited sizes, anything from small parts and blocks to massive shafts weighing in the tons. Open die forging is commonly used in the forging of shafts and crankshafts — it’s possible to forge a shaft over 100 feet long via open die forging.

    The open die forging process allows for far greater strength and toughness in parts compared to cast or machined parts, making open die forged steel the material of choice for any application requiring strength and longer part lifespans. Open die forgings are commonly used in the oil & gas industry, aerospace, pumps, printing, and almost any custom parts.

    For more information on open die forging see: http://www.glforge.com/custom-open-die-forgings.html



    Steel is a material that is 100% recyclable. This saves resources and energy when producing it. At Uddeholm, we work hard to make our production ever more environmental friendly and efficient, for instance by improving processes, using LNG instead of petroleum products, reusing waste products, reducing emissions and more. For us, clean steel is green steel.

    In this movie, Cecilia Johnsson, Environmetal Manager at Uddeholms AB embodies this work. The movie was part of voestalpine AG’s brand campaign in january 2013.,

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Heart

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Heart