Bottom price for EN DIN 34CrNiMo6 | 1.6582 | 4337 Engineering Steel in Spain
EN 34CrNiMo6 Steel is an important alloy engineering steel grade as per BS EN10083-3:2006. 34CrNim06 steel has high strength, high toughness and good hardenability. EN / DIN 34CrNiMo6 alloy steel has the stability ofresistance to overheating, but the white sensitivity of 34CrNiM06 ishigh. It also has the temper brittleness, so the weldability of34CrNiMo6 material is poor. The steel 34CrNiMo6 needs the hightemperature preheating before welding in order to eliminate the stressafter welding pr...
Dedicated to strict quality control and thoughtful customer service, our experienced staff members are always available to discuss your requirements and ensure full customer satisfaction for Bottom price for EN DIN 34CrNiMo6 | 1.6582 | 4337 Engineering Steel in Spain, sincerely look forward to serving you in the near future. You are sincerely welcome to visit our company to talk business face to face with each other and establish long-term co-operation with us!
is an important alloy engineering steel grade as per BS EN
10083-3:2006. 34CrNim06 steel has high strength, high toughness and good
hardenability. EN / DIN 34CrNiMo6 alloy steel has the stability of
resistance to overheating, but the white sensitivity of 34CrNiM06 is
high. It also has the temper brittleness, so the weldability of
34CrNiMo6 material is poor. The steel 34CrNiMo6 needs the high
temperature preheating before welding in order to eliminate the stress
after welding processing.
1.EN Steel 34CrNiMo6 Supply Range
Round Steel Bar Sizes: diameter 80mm – 1200mm
Other steel shape and sizes available according to your requirements.
Surface finish: Black, machined, peeled, turned or according to other customers’ pecial requirements.
2.EN 34CrNiMo6 Steel Standards And Equivalents
|BS EN 10083 -3: 2006||34CrNiMo6 / 1.6582||: 2004||4337|
|BS EN 10250 – 3: 2000|
3. EN/DIN 34CrNiMo6 Steel Chemical Composition Properties
|BS EN 10083 – 3:2006||34CrNiMo6
|0.30-0.38||0.5-0.8||0.40 max||0.025 max||0.035 max||1.3-1.7||0.15-0.30||1.3-1.7|
|BS EN 10250-3:2000||C||Mn||Si||P||S||Cr||Mo||Ni|
|0.30-0.38||0.5-0.8||0.40 max||0.035 max||0.035 max||1.3-1.7||0.15-0.30||1.3-1.7|
|ASTM A29: 2004||4337||C||Mn||Si||P||S||Cr||Mo||Ni|
|0.30-0.40||0.6-0.8||0.20-0.35||0.035 max||0.040 max||0.70-0.90||0.20-0.30||1.65-2.00|
4.Mechanical Properties of EN/DIN 34CrNiM06 / 1.6582 Alloy Steel
|Properties||< 16||>16 – 40||>40 – 100||>100 – 160||>160 – 250|
|Thickness t [mm]||< 8||8<t<20||20<t<60||60<t<100||100<t<160|
|Yield strength Re [N/mm²]||min. 1000||min. 900||min. 800||min. 700||min. 600|
|Tensile strength Rm [N/mm2]||1200 – 1400||1100 – 1300||1000 – 1200||900 – 1100||800 – 950|
|Elongation A [%]||min. 9||min. 10||min. 11||min. 12||min. 13|
|Reduction of area Z [%]||min. 40||min. 45||min. 50||min. 55||min. 55|
|Toughness CVN [J]||min. 35||min. 45||min. 45||min. 45||min. 45|
5.Heat Treatment of 34CrNiMo6 Engineering Steel
Quenched and Tempered (Q+T) of 34CrNiMo6 Steel
Heat 34CrNiMo6 round steel slowly to the temperature of 850°C;
Soak at this hardening temperature quench in oil;
Temper as soon as 34CrNiMo6 steels reach room temperature.
Heat uniformly to the suitable temperature;
Withdraw from the furnace and cool in the air.
The usual tempering temperature is 600°C which depending on the actual requirements.
6.Forging of DIN 34CrNiMo6 / 1.6582 Steel
Hot forming temperature: 1100-900oC.
7.Machinability of Steel 34CrNiMo6
is best done with this 1.6582 alloy steel in the annealed or normalized
and tempered condition. It can be machined by all conventional methods.
alloy materials can be fusion or resistance welded. Preheat and post
heat weld procedures should be followed when welding this alloy by
34CrNiMo6 steel is used to make tools which demands good plasticity and
high strength. It is usually selected to make the big size and important
parts, such as heavy machinery axle,turbine shaft blade, high load of
transmission parts, fasteners, crank shafts, gears, as well as heavily
loaded parts for motor construction etc.
Otai Steel is reliable to
supply engineering 34CrNiMo6 steels / 1.6582 engineering alloy steels.
Please tell us your detailed requirements and have the best offer soon.
http://briarwood-ford.com/ Call or visit for a test drive of this vehicle today! Phone: 877-560-3859 Year: 2010 Make: Jeep Model: Patriot Trim: Sport Engine: 2.0L …
Ball Pen Extruder (50mm)
The major extruder getting fifty mm SCREW built of EN forty one B sequence nitride steel getting I.d ratio 28:1 duly ground and polished
Designed of nitride steel getting ID fifty mm duly honed
H2o Cooling Furnished to the barrel at the feeding part.
Ac Motor will be of a reputed make Hindustan motor consisting of ten HP 1500 rpm
Helical Gear Box
Helical Gear Box will be of reputed Company P.G. Gear getting ration 16:1
Ceramic band heaters for economical heating.