In ASTM A681 standard, L6 steel grade is in L-type for special purpose tool steels. AISI L6 tool steel is in the general class of alloy, oil-hardening tool steel that is characterized by good toughness. ASTM L6 tool steel is suitable for use as tools, dies, and machine parts, which require a good combination of hardness and toughness. Due to its lower carbon content and relatively high nickel content, L6 tool steel has slightly better shock-resistance than more highly alloyed types and shoul...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    To constantly improve the management system by virtue of the rule of "sincerely, good faith and quality are the base of enterprise development", we widely absorb the essence of related products internationally, and constantly develop new products to meet the demands of customers for 9 Years manufacturer L6 Tool Steel | 1.2714 | 55NiCrMoV7 | SKT4 | BH224/5 in Chicago, We will wholeheartedly welcome all clients in the industry both at home and abroad to cooperate hand in hand, and create a bright future together.


    In ASTM A681 standard, L6 steel grade is in L-type for special purpose tool steels. AISI L6 tool steel
    is in the general class of alloy, oil-hardening tool steel that is
    characterized by good toughness. ASTM L6 tool steel is suitable for use
    as tools, dies, and machine parts, which require a good combination of
    hardness and toughness.

    Due to its lower carbon content and
    relatively high nickel content, L6 tool steel has slightly better
    shock-resistance than more highly alloyed types and should be used where
    some wear-resistance can be sacrificed for increased toughness.

    1. Relevant Steel Specification of L6 Tool Steel

    Country USA German Japan British
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404 BS 4659
    Grades L6/T61206 1.2714/55NiCrMoV7 SKT4 BH224/5

    2. AISI L6 Steel Chemical Composition and Steel Equivalents

    ASTM A681 C Mn P S Si Cr V Mo Ni
    L6/T61206 0.65 0.75 0.25 0.80 0.03 0.03 0.10 0.50 0.60 1.20 . . . . . . . . . 0.50 1.25 2.00
    DIN ISO 4957 C Mn P S Si Cr V Mo Ni
    1.2714/55NiCrMoV7 0.50 0.60 0.60 0.90 0.03 0.02 0.10 0.40 0.80 1.20 0.05 0.15 0.35 0.55 1.50 1.80
    JIS G4404 C Mn P S Si Cr V Mo Ni
    SKT4 0.50 0.60 0.60 0.90 0.03 0.02 0.10 0.40 0.80 1.20 0.05 0.15 0.35 0.55 1.50 1.80
    BS 4659 C Mn P S Si Cr V Mo Ni
    BH224/5 0.49 0.57 0.70 1.00 0.03 0.025 . . . 0.35 0.70 1.10 . . . . . . 0.25 0.40 1.25 1.80

    3. ASTM L6 Tool Steel Mechanical Properties

    Steel L6 Physical Properties

    • Modulus of elasticity [103 x N/mm2]: 215

    • Density [g/cm3]: 7.84

    • Thermal conductivity [W/m.K]: 36.0

    • Electric resistivity [Ohm mm2/m]: 0.30

    • Specific heat capacity[J/g.K]: 0.46

    Mechanical Properties of L6 Steels

    Properties Metric Imperial
    Poisson’s ratio 0.27- 0.30 0.27- 0.30
    Elastic modulus 190-210 GPa 27557-30457 ksi

    4. Forging of L6 Tool Steel

    Forge at 1079°C (1975 F) down to 871°C (1600 F). Do not forge below 843°C (1550 F).

    5. AISI L6 Tool Steel Heat Treatment

    Hardening

    Preheating:
    Heat steel L6 at a rate not exceeding 204°C (400°F) per hour (222°C per
    hour) to 621-677°C (1150-1250°F) and equalize. Soak for 30 minutes for
    the first inch (25.4 mm) of thickness, plus 15 minutes for each
    additional inch (25.4 mm).

    Quenching

    Quench L6 tool steel in oil to 66-51°C (150-125°F).

    Tempering

    Temper
    L6 steels immediately after quenching. Hold at temperature for 1 hour
    per inch (25.4 mm) of thickness when tempering at 204°C (400°F), 4 hours
    minimum, then air cool to ambient temperature.
    However, where increased toughness is desired, at a sacrifice of some hardness, higher tempering temperatures are often used.

    AISI L6 steel does not become brittle, as many other die steels do, when tempered in the range of 232°C to 426°C (450 to 800°F).

    To
    minimize the possibility of cracking, the steel should be tempered
    immediately after hardening and should be heated slowly to the desired
    tempering temperature.

    Annealing

    Annealing of steel L6 must be performed after hot working and before re-hardening.

    Heat
    to 760°C (1400°F) and hold one hour per inch of maximum thickness. Then
    cool slowly with the furnace at a rate not exceeding 28°C per hour(50°F
    per hour) to 538°C (1000°F). Continue cooling to ambient temperature in
    the furnace or in air.

    For improved machinability, hold at 760°C
    (1400°F) for 1 hour per inch (25.4mm) of maximum thickness; 2 hours
    minimum. Then cool slowly with the furnace cool from 677°C (1250°F) to
    760°C (1400°F), hold for 8 hours, then air cool to ambient temperature.

    Because of its air-hardening ability, steel L6 should not be normalized.

    6. Machinability of Steel L6

    Machinability
    of tool steel L6 is very good. It rates 90% of the machinability of the
    W-group water hardening low alloy steels rated 100% as a baseline.

    7. Applications of ASTM A681 L6 Tool Steel

    AISI
    L6 cold working tool steel is for general purpose tools and dies where
    greater toughness is required, but with some sacrifice of
    abrasion-resistance.

    Typically used below applications:

    • spindles,

    • forming rolls,

    • punches,

    • blanking and forming dies,

    • trimmer dies,

    • clutch parts,

    • pawls,

    • bearings,

    • chucks parts,

    • rollers,

    • knuckle pins,

    • clutch pins,

    • shear blades

  • Previous:
  • Next:



  • 6 In 1 Multi Metal Mini Wood Lathe Motorized Jig-saw Grinder Driller
    แหล่งแนะนำ : http://p2b.us/18fshf

    คุณกำลังต้องการ 6 In 1 Multi Metal Mini Wood Lathe Motorized Jig-saw Grinder Driller เพื่อช่วยแก้ไขปัญหา อยูใช่หรือไม่ ถ้าใช่คุณมาถูกที่แล้ว เรามีสินค้า ที่ท่านต้องการแนะนำ พร้อมมีแหล่งซื้อ สินค้าราคาถูก แนะนำให้ท่าน 6 In 1 Multi Metal Mini Wood Lathe Motorized Jig-saw Grinder Driller ราคาถูกให้กับคุณ

    Product details of 6 In 1 Multi Metal Mini Wood Lathe Motorized Jig-saw Grinder Driller Introduction: 6 in 1 multi metal mini wood lathe Machine -enjoy the joy of creation with quotTransformerquot 6 in 1 multi metal mini wood lathe not only has single unit such as Jig-saw grinder Drillerwood lathe metal lathe Miller but also has the 6 in 1 combined set. Base is made of advanced aluminum alloy and it#039s durable and not deformed. This is really a good tool. 6 in 1 multi metal mini wood lathe can make up of : 1) Jig-saw 2) Grinder 3) Driller 4) Metal lathe 5)Wood lathe 6)Milling Specification: Material Carbon steel Aluminum ABS Headstock speed 2000rpm Motor input DC 12V Max. Cutting diameter 45mm(bigger diameter is possible with intermediatepiece) Center distance 135mm(with accessories extra long machine bed can longer to 360mm) Color Black Red Recommended types of wood Lim wood birch maple pear tree cherry tree (medium hard) beech tree oak (hard). Scope 1 Can process integrated circuit acrylics wood plastic gold silver copper steel aluminum and so on. 2 Every suitable chisel and gouge can be used Panel saws Technique Data: 1) Motor speed: 20000rpm 2) Headstock speed: 2000rpm 3) Support power: 14.5VDC/2A/29W Switching Adapter input 100V-240V 4) Table size: 90 x 90mm 5) Stroke of the jigsaw: 4mm 6) Material: Carbon steel Aluminum ABS 7) Max. thickness of cut: hardwood: 4mm plywood: 7mm softwood: 18mm sheet metal: 0.5mm plexi-glass: 2mm 8) Maximum measurements on 3D (L/W/H cm)…

    หมวดหมู่ shop-power-tools
    ราคา 4908 บาท ถูกที่สุด

    สั่งซื้อพร้อมส่วนลด เก็บเงินปลายทาง http://p2b.us/18fshf
    ———————————————————————————-
    คำค้นหา : 6, In, 1, Multi, Metal, Mini, Wood, Lathe, Motorized, Jigsaw, Grinder, Driller, 6 In 1 Multi Metal Mini Wood Lathe Motorized Jig-saw Grinder Driller

    6 #In #1 #Multi #Metal #Mini #Wood #Lathe #Motorized #Jigsaw #Grinder #Driller #6 In 1 Multi Metal Mini Wood Lathe Motorized Jig-saw Grinder Driller



    When you buy a new carbon steel wok, you need to season and condition the wok. Seasoning a new wok means you start making a hard, black patina finish. This surface is non sticky and will help sear the food. First clean the wok with steel wool and dishwashing soap. Rinse and dry the wok. Follow all the steps so you will get a hard, black cooking surface for your wok. A well seared wok helps sear and lock in the flavours of the food. Usually it takes about a year to season the surface of the wok, but follow my procedure so you can season the wok in about 3 months.

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Heart

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Tree