8 Years manufacturer D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory for Brisbane
1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade...
In the past few years, our company absorbed and digested advanced technologies both at home and abroad. Meanwhile, our company staffs a team of experts devoted to the development of 8 Years manufacturer D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory for Brisbane, Please send us your specifications and requirements, or feel free to contact us with any questions or inquiries that you may have.
1. Relevant D2 Steel Specifications
|Standard||ASTM A681||DIN EN ISO 4957||JIS G4404|
2. D2 Tool Steel Chemical Composition
|DIN ISO 4957||C||Mn||P||S||Si||Cr||V||Mo|
3. AISI Grade D2 Steel Mechanical Properties
|Hardness, Knoop (converted from Rockwell C hardness)||769||769|
|Hardness, Rockwell C||62||62|
|Izod impact unnotched||77.0 J||56.8 ft-lb|
|Elastic modulus||190-210 GPa||27557-30457 ksi|
|Thermal expansion||10.4 x 10-6/ºC||20-100||
4. AISI/ASTM A681 D2 Grade Steel Forging
Heating for forging of AISI D2 tool steel should
be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
should always be annealed after forging.
5. D2 Tool Steel Heat Treatment
ASTM D2 steels alloy should be preheated very slowly to 815oC (1500oF) and then temperature can be increased to 1010oC (1850oF). They are then held at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).
Annealing of D2 tool steels material should be done at 871 to 898oC (1600 to 1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or less.after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.
When desirable to relieve the strains of machining, heat D2 grade steel slowly to 1050°-1250°F, allow to equalize, and then cool in still air (Strain Relieving).
Preheat Prior To Hardening
Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.
After thorough preheating, heat to 1800°-1850°F. Hold the work piece at the hardening temperature until it is completely and uniformly heated.
AISI D2 steel tool material is an air hardening steel and will develop hardness on cooling in still air. To avoid scaling and prevent decarburization of the work piece surface, controlled atmosphere or vacuum furnaces are recommended. If these furnaces are not available, pack hardening, salt baths or wrapping the piece in stainless steel foil will provide some degree of surface protection in the hardening process. Parts should be allowed to cool to 150F, or to where they can be held in the bare hand, and then temper immediately.
The tempering temperature on material D2 steel may be varied according to the desired hardness. D2 steels can be tempered at 204oC (400oF) for achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell C hardness of 54.
6. D2 Tool Steel Material Application
AISI grade D2 tool steels are used for long run tooling applications, where wear resistance is important, such as blanking or forming dies and thread rolling dies.
Some main applications for D2 tool steel are as below:
Blanking Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls, Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear Parts.
We usually hold D2 tool steel on sale activities, and you would have our price on regular schedule. Contact us and sign in our newsletter to have D2 tool steel materials price list and commercial quote today.
Click on the link below to view my latest video on TIG Welding Mild Steel:
In this video I am going to be discussing and demonstrating TIG welding on Mild Steel.
I hope you will enjoy the video, and if so, please hit the “Like” button after watching. Also, don’t forget to subscribe to my YouTube Channel so you can be updated whenever I post a new video.
Also, please visit my website at www.weldfever.com.
Tool Steel Service
Tool Steel Service provides services and products to customers throughout the US, Canada and Mexico. We have manufacturing and warehousing facilities
throughout North America.
tool steel, alloy steel, carbon steel, powdered metal, stainless steel, precision ground flat stock, drill rod, stripper plate and others in the following surface conditions: hot roll plate, decarb free bar, round bar, precision ground flat stock and drill rod.
O1 tool steel, A2 tool steel, D2 tool steel, S7 tool steel, H13 tool steel, 4140 alloy steel, 4142 alloy steel, 4130 alloy steel, 4152 alloy steel, A36 carbon steel, 1018 carbon steel, 1020 carbon steel, AR400 carbon steel, P20 mold steel, P20 High Hard, Nak 55 mold steel, A11 powdered metal, M4 powdered metal, M2 high speed steel, M4 high speed steel, T1 high speed steel, T15 high speed steel
We can handle YOUR MATERIAL
40 Ton Crane Capacity
Cut to Length – Large Steel Cutting Steel Grinding – Steel Milling – Steel Storage
All within our 70,000 sq. ft. facitily located in the Chicago metropolitan area