7 Years manufacturer EN DIN 34CrNiMo6 | 1.6582 | 4337 Engineering Steel Factory from California
EN 34CrNiMo6 Steel is an important alloy engineering steel grade as per BS EN10083-3:2006. 34CrNim06 steel has high strength, high toughness and good hardenability. EN / DIN 34CrNiMo6 alloy steel has the stability ofresistance to overheating, but the white sensitivity of 34CrNiM06 ishigh. It also has the temper brittleness, so the weldability of34CrNiMo6 material is poor. The steel 34CrNiMo6 needs the hightemperature preheating before welding in order to eliminate the stressafter welding pr...
We keep improving and perfecting our products and service. At the same time, we work actively to do research and development for 7 Years manufacturer EN DIN 34CrNiMo6 | 1.6582 | 4337 Engineering Steel Factory from California, We sincerely welcome overseas customers to consult for the long-term cooperation and the mutual development.We strongly believe that we can do better and better.
is an important alloy engineering steel grade as per BS EN
10083-3:2006. 34CrNim06 steel has high strength, high toughness and good
hardenability. EN / DIN 34CrNiMo6 alloy steel has the stability of
resistance to overheating, but the white sensitivity of 34CrNiM06 is
high. It also has the temper brittleness, so the weldability of
34CrNiMo6 material is poor. The steel 34CrNiMo6 needs the high
temperature preheating before welding in order to eliminate the stress
after welding processing.
1.EN Steel 34CrNiMo6 Supply Range
Round Steel Bar Sizes: diameter 80mm – 1200mm
Other steel shape and sizes available according to your requirements.
Surface finish: Black, machined, peeled, turned or according to other customers’ pecial requirements.
2.EN 34CrNiMo6 Steel Standards And Equivalents
|BS EN 10083 -3: 2006||34CrNiMo6 / 1.6582||: 2004||4337|
|BS EN 10250 – 3: 2000|
3. EN/DIN 34CrNiMo6 Steel Chemical Composition Properties
|BS EN 10083 – 3:2006||34CrNiMo6
|0.30-0.38||0.5-0.8||0.40 max||0.025 max||0.035 max||1.3-1.7||0.15-0.30||1.3-1.7|
|BS EN 10250-3:2000||C||Mn||Si||P||S||Cr||Mo||Ni|
|0.30-0.38||0.5-0.8||0.40 max||0.035 max||0.035 max||1.3-1.7||0.15-0.30||1.3-1.7|
|ASTM A29: 2004||4337||C||Mn||Si||P||S||Cr||Mo||Ni|
|0.30-0.40||0.6-0.8||0.20-0.35||0.035 max||0.040 max||0.70-0.90||0.20-0.30||1.65-2.00|
4.Mechanical Properties of EN/DIN 34CrNiM06 / 1.6582 Alloy Steel
|Properties||< 16||>16 – 40||>40 – 100||>100 – 160||>160 – 250|
|Thickness t [mm]||< 8||8<t<20||20<t<60||60<t<100||100<t<160|
|Yield strength Re [N/mm²]||min. 1000||min. 900||min. 800||min. 700||min. 600|
|Tensile strength Rm [N/mm2]||1200 – 1400||1100 – 1300||1000 – 1200||900 – 1100||800 – 950|
|Elongation A [%]||min. 9||min. 10||min. 11||min. 12||min. 13|
|Reduction of area Z [%]||min. 40||min. 45||min. 50||min. 55||min. 55|
|Toughness CVN [J]||min. 35||min. 45||min. 45||min. 45||min. 45|
5.Heat Treatment of 34CrNiMo6 Engineering Steel
Quenched and Tempered (Q+T) of 34CrNiMo6 Steel
Heat 34CrNiMo6 round steel slowly to the temperature of 850°C;
Soak at this hardening temperature quench in oil;
Temper as soon as 34CrNiMo6 steels reach room temperature.
Heat uniformly to the suitable temperature;
Withdraw from the furnace and cool in the air.
The usual tempering temperature is 600°C which depending on the actual requirements.
6.Forging of DIN 34CrNiMo6 / 1.6582 Steel
Hot forming temperature: 1100-900oC.
7.Machinability of Steel 34CrNiMo6
is best done with this 1.6582 alloy steel in the annealed or normalized
and tempered condition. It can be machined by all conventional methods.
alloy materials can be fusion or resistance welded. Preheat and post
heat weld procedures should be followed when welding this alloy by
34CrNiMo6 steel is used to make tools which demands good plasticity and
high strength. It is usually selected to make the big size and important
parts, such as heavy machinery axle,turbine shaft blade, high load of
transmission parts, fasteners, crank shafts, gears, as well as heavily
loaded parts for motor construction etc.
Otai Steel is reliable to
supply engineering 34CrNiMo6 steels / 1.6582 engineering alloy steels.
Please tell us your detailed requirements and have the best offer soon.
see a more detailed article http://goo.gl/KnjkTi or visit the store here http://goo.gl/mJkDww Tig welding stainless to cabon steel and high strength A572 grade 50 steel using 309 filler rod. 309 is the industry standard for welding carbon to stainless. 309 stainless tig rods have lots of applications and one of the biggest ones is for maintenance type welding where metal cant be completely clean or when the grade of steel is unknown…It can also be used to weld 400 series stainless steels in certain applications.
In this video filmed at the Walter Tosto SpA in Chieti, Italy (part of the AMW consortium, with Ansaldo Nucleare S.p.A and Mangiarotti S.p.A) a stainless steel plate for the ITER vacuum vessel is pressed into the required shape through an open die hot forming process. (Published with the authorization of Walter Tosto SpA.)