5 Years manufacturer C45 Round Bar | AISI 1045 | DIN 1.1191 | JIS S45C Factory for Slovenia
Steel C45 Round Bar is an unalloyed medium carbon steel, which is also a general carbon engineering steel. C45 is a medium strength steel with good machinability and excellent tensile properties. C45 round steel is generally supplied in the black hot rolled or occasionally in the normalised condition, with a typical tensile strength range 570 – 700 Mpa and Brinell hardness range 170 – 210 in either condition. It does not however respond satisfactorily to nitriding due to a lack of suita...
Our team through professional training. Skilled professional knowledge, strong sense of service, to meet the service needs of customers for 5 Years manufacturer C45 Round Bar | AISI 1045 | DIN 1.1191 | JIS S45C Factory for Slovenia, Please send us your specifications and requirements, or feel free to contact us with any questions or inquiries that you may have.
an unalloyed medium carbon steel, which is also a general carbon
engineering steel. C45 is a medium strength steel with good
machinability and excellent tensile properties. C45 round steel is
generally supplied in the black hot rolled or occasionally in the
normalised condition, with a typical tensile strength range 570 – 700
Mpa and Brinell hardness range 170 – 210 in either condition. It does
not however respond satisfactorily to nitriding due to a lack of
suitable alloying elements.
C45 round bar steel is equivalent to
Steel C45 bar or plate is suitable for the manufacture of parts such as
gears, bolts, general-purpose axles and shafts, keys and studs.
1. Supply Range of Steel C45 Round Bar
C45 Steel Round Bar: diameter 8mm – 3000mm
C45 Steel Plate: thickness 10mm – 1500mm x width 200mm – 3000mm
C45 Steel Flat Bar: 200mm – 1000mm
Square C45 Steel: 20mm-800mm
Surface Finish: Black, Rough Machined, Turned or as per given requirements.
2. Common C45 Steel Specifications
|Standard||EN 10083-2||AS 1442|
3. C45 Round Bar Steel Chemical Composition Properties
4. Mechanical Properties of C45 Round Bar Steel Material
Mechanical Properties in Quenched+Tempered Condition
|Diameter d (mm)||Thickness t (mm)||0.2 % proof stress (N/mm2)||Tensile strength (N/mm2)||Elongation A5 (%)||Reduction Z (%)|
|<16||<8||min. 490||700-850||min. 14||min. 35|
|<17-40||<8<=20||min. 430||650-800||min. 16||min. 40|
|<41-100||<20<=60||min. 370||630-780||min. 17||min. 45|
Mechanical Properties in Normalized Condition
|Diameter d (mm)||Thickness t (mm)||0.2 % proof stress (N/mm2)||Tensile strength (N/mm2)||Elongation A5(%)|
|<16||<16||min. 390||min. 620||min. 14|
|<17-100||<16<=100||min. 305||min. 305||min. 16|
|<101-250||<100<250||min. 275||min. 560||min. 16|
5. Forging of Carbon Steel C45 Round Bar
Hot forming temperature: 850-1200oC.
heat to 750 oC – 800 oC, then continue heating to 1100 oC – 1200 oC
maximum, hold until temperature is uniform throughout the section and
commence forging immediately. Forging is not workable below 850 oC.
Finished forgings could be air cooled.
We are strong on forged steel C45 round bar. Welcome enquiry of C45 steel materials.
6. DIN C45 Round Bar Steel Grade Heat Treatment
|Forging or hot rolling:||1100 – 850°C|
|Normalising:||840 – 880°C/air|
|Soft annealing:||680 – 710°C/furnace|
|Hardening:||820 – 860°C/water, oil|
|Tempering:||550 – 660°C/air|
7. Hardening of DIN C45 Steel Hardening
Harden from a temperature of 820-860oC followed by water or oil quenching.
to 820 oC – 850 oC hold until temperature is uniform throughout the
section, soak for 10 – 15 minutes per 25mm of section, and quench in
water or brine. Or,
Heat to 830 oC – 860 oC soak as above and quench in oil.Temper immediately while still hand warm.
Surface hardness for C45 special steel round bar after flame or induction hardning:
Steel Name Steel number Surface Harndess
C45 1.1191 min. 55 HRC
8. Application of DIN Carbon Steel C45 Round Bar
C45 round bar steel material and steel plate C45, flats are widely used
in all industry for uses which require more strength and wear
resistance than the low carbon mild steel.
subsequently tempered steel for C45 steel grade round bar, steel plate,
flat and square is used for axles, bolts, forged connecting rods,
crankshafts, torsion bars, light gears, guide rods, screws, forgings,
wheel tyres, shafts, sickles, axes, knives, wood working drills,
Welcome customers to inquiry DIN C45 round bar,
CK45/1.1191 steel plate, flat steel for C45 steel price. We are
professional supplier and exporter for more than 20 years. We offer you
worldwide solution for C45 round bar steel.
Shop Whiteline Front Adjustable Anti-dive Kit: http://muscle.am/2iloDpw
Reduced Chassis Flex. The Whiteline Adjustable Front Strut Tower Brace is designed to reduce chassis flex for better handling on 2005-2010 Mustang GTs and V6 models. The heavy-duty construction incorporates a dual-tube design for maximum strength and rigidity. The best part about this kit is the adjustable nature of the front strut tower brace, allowing you to use this even on supercharged Mustangs. It is designed to clear the stock factory hood while still giving you enough clearance to install this kit over your supercharged engine using the unique eccentric mounting points.
High-Quality Construction. This Whiteline Adjustable Front Tower Brace for 2005-2010 Mustangs is constructed from high-quality 4130 chromoly steel which is lightweight and has excellent tensile strength. The strut tower brace incorporates a dual-tube design to further increase chassis rigidity and reduce flex. The tower brace is then sprayed with a matte black powder coat finish that resists corrosion and wear while adding a bit of style under the hood.
Complete Bolt-on Installation. The Whiteline Adjustable Front Tower Brace is a complete bolt-on kit. Simply remove the pair of inner bolts of the shock tower, slide this kit into place, reinstall the bolts and tighten firmly. No further modifications or specialty tools are required. The adjustable design is perfect for Mustangs equipped with aftermarket superchargers.
The carbon content affects the properties of the iron, we have pure iron, low carbon steel(mild steel), medium carbon steel, high carbon steel and Cast iron, the low-carbon is soft and easily scratched the high-carbon is much harder so high carbon steel can cut low carbon steel.