29 Years Factory L6 Tool Steel | 1.2714 | 55NiCrMoV7 | SKT4 | BH224/5 Factory in Oman

29 Years Factory
 L6 Tool Steel | 1.2714 | 55NiCrMoV7 | SKT4 | BH224/5 Factory in Oman

Short Description:

In ASTM A681 standard, L6 steel grade is in L-type for special purpose tool steels. AISI L6 tool steel is in the general class of alloy, oil-hardening tool steel that is characterized by good toughness. ASTM L6 tool steel is suitable for use as tools, dies, and machine parts, which require a good combination of hardness and toughness. Due to its lower carbon content and relatively high nickel content, L6 tool steel has slightly better shock-resistance than more highly alloyed types and shoul...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    Our team through professional training. Skilled professional knowledge, strong sense of service, to meet the service needs of customers for 29 Years Factory L6 Tool Steel | 1.2714 | 55NiCrMoV7 | SKT4 | BH224/5 Factory in Oman, We are confident to make great achievements in the future. We are looking forward to becoming one of your most reliable suppliers.


    In ASTM A681 standard, L6 steel grade is in L-type for special purpose tool steels. AISI L6 tool steel
    is in the general class of alloy, oil-hardening tool steel that is
    characterized by good toughness. ASTM L6 tool steel is suitable for use
    as tools, dies, and machine parts, which require a good combination of
    hardness and toughness.

    Due to its lower carbon content and
    relatively high nickel content, L6 tool steel has slightly better
    shock-resistance than more highly alloyed types and should be used where
    some wear-resistance can be sacrificed for increased toughness.

    1. Relevant Steel Specification of L6 Tool Steel

    Country USA German Japan British
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404 BS 4659
    Grades L6/T61206 1.2714/55NiCrMoV7 SKT4 BH224/5

    2. AISI L6 Steel Chemical Composition and Steel Equivalents

    ASTM A681 C Mn P S Si Cr V Mo Ni
    L6/T61206 0.65 0.75 0.25 0.80 0.03 0.03 0.10 0.50 0.60 1.20 . . . . . . . . . 0.50 1.25 2.00
    DIN ISO 4957 C Mn P S Si Cr V Mo Ni
    1.2714/55NiCrMoV7 0.50 0.60 0.60 0.90 0.03 0.02 0.10 0.40 0.80 1.20 0.05 0.15 0.35 0.55 1.50 1.80
    JIS G4404 C Mn P S Si Cr V Mo Ni
    SKT4 0.50 0.60 0.60 0.90 0.03 0.02 0.10 0.40 0.80 1.20 0.05 0.15 0.35 0.55 1.50 1.80
    BS 4659 C Mn P S Si Cr V Mo Ni
    BH224/5 0.49 0.57 0.70 1.00 0.03 0.025 . . . 0.35 0.70 1.10 . . . . . . 0.25 0.40 1.25 1.80

    3. ASTM L6 Tool Steel Mechanical Properties

    Steel L6 Physical Properties

    • Modulus of elasticity [103 x N/mm2]: 215

    • Density [g/cm3]: 7.84

    • Thermal conductivity [W/m.K]: 36.0

    • Electric resistivity [Ohm mm2/m]: 0.30

    • Specific heat capacity[J/g.K]: 0.46

    Mechanical Properties of L6 Steels

    Properties Metric Imperial
    Poisson’s ratio 0.27- 0.30 0.27- 0.30
    Elastic modulus 190-210 GPa 27557-30457 ksi

    4. Forging of L6 Tool Steel

    Forge at 1079°C (1975 F) down to 871°C (1600 F). Do not forge below 843°C (1550 F).

    5. AISI L6 Tool Steel Heat Treatment

    Hardening

    Preheating:
    Heat steel L6 at a rate not exceeding 204°C (400°F) per hour (222°C per
    hour) to 621-677°C (1150-1250°F) and equalize. Soak for 30 minutes for
    the first inch (25.4 mm) of thickness, plus 15 minutes for each
    additional inch (25.4 mm).

    Quenching

    Quench L6 tool steel in oil to 66-51°C (150-125°F).

    Tempering

    Temper
    L6 steels immediately after quenching. Hold at temperature for 1 hour
    per inch (25.4 mm) of thickness when tempering at 204°C (400°F), 4 hours
    minimum, then air cool to ambient temperature.
    However, where increased toughness is desired, at a sacrifice of some hardness, higher tempering temperatures are often used.

    AISI L6 steel does not become brittle, as many other die steels do, when tempered in the range of 232°C to 426°C (450 to 800°F).

    To
    minimize the possibility of cracking, the steel should be tempered
    immediately after hardening and should be heated slowly to the desired
    tempering temperature.

    Annealing

    Annealing of steel L6 must be performed after hot working and before re-hardening.

    Heat
    to 760°C (1400°F) and hold one hour per inch of maximum thickness. Then
    cool slowly with the furnace at a rate not exceeding 28°C per hour(50°F
    per hour) to 538°C (1000°F). Continue cooling to ambient temperature in
    the furnace or in air.

    For improved machinability, hold at 760°C
    (1400°F) for 1 hour per inch (25.4mm) of maximum thickness; 2 hours
    minimum. Then cool slowly with the furnace cool from 677°C (1250°F) to
    760°C (1400°F), hold for 8 hours, then air cool to ambient temperature.

    Because of its air-hardening ability, steel L6 should not be normalized.

    6. Machinability of Steel L6

    Machinability
    of tool steel L6 is very good. It rates 90% of the machinability of the
    W-group water hardening low alloy steels rated 100% as a baseline.

    7. Applications of ASTM A681 L6 Tool Steel

    AISI
    L6 cold working tool steel is for general purpose tools and dies where
    greater toughness is required, but with some sacrifice of
    abrasion-resistance.

    Typically used below applications:

    • spindles,

    • forming rolls,

    • punches,

    • blanking and forming dies,

    • trimmer dies,

    • clutch parts,

    • pawls,

    • bearings,

    • chucks parts,

    • rollers,

    • knuckle pins,

    • clutch pins,

    • shear blades

  • Previous:
  • Next:



  • PRE-C427SS-TK1- Super Street Series 427 Stroker SBC, Dart Block, 4340 Forged steel crank, Forged H beam rods W/ARP cap screws,AFR CNC Aluminum Heads, Scorpion Roller rockers and tie bar mechanical lifters, Edelbrock Vr. Jr intake manifold, Cast Aluminum valve covers, 7 qt. oil pan and braided dipstick. Dyno tested, 575HP/525TQ.
    TURN KEY OPTIONS INCLUDED
    Quick Fuel Q 750 Carb, MSD Pro billet distributor, Custom fit wires and looms, MSD Ignition package with coil and small hardware finishing kit.
    OPTIONS INCLUDE
    MARCH PERFORMANCE PULLEY KIT
    For More Information on our Custom Engines and or VEHICLE SERVICES please feel free to visit us at

    http://www.prestigemoto.com

    OR
    For CHEVY ENGINES only http://prestigemoto.com/chevy_sb_index
    For FORD ENGINES only http://prestigemoto.com/ford_sb_index
    For MOPAR ENGINES only http://prestigemoto.com/mopar-index
    For MARINE ENGINES only http://prestigemoto.com/marine-index
    For SUPERCHARGED AND TURBO ENGINES only http://www.prestigemoto.com/supercharged-index
    We Offer Complete Restorations from partials to completes along with ONE OFF CUSTOMS

    http://prestigemoto.com/build-your-dream

    You can also just simply CONTACT US via email at http://prestigemoto.com/contact



    internet site:http://www.steelsino.com
    Shanghai Bozhong Metal Group was launched in 2006, with 31 million registered fund, It is the main integrated operator of contemporary provider market for specialty stainless metal.It is the main development firm of the Shanghai metal contemporary provider extensive pilot location, which was set up by nation’s commerce ministry and Shanghai government.

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the House

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Plane