H13 Tool Steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications. H13 tool steel is classified as group H steels by the AISI classification system. This series of steels start from H1 to H19. AISI H-13 tool steel is characterized by: Good resistance to abrasion at both low and high temperatures High level of toughness and ductility Uniform and high level of machinability and polishability Good high-temperature strength and resistance to t...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    We support our buyers with ideal high quality products and high level service. Becoming the specialist manufacturer in this sector, we have gained rich practical experience in producing and managing for 29 Years Factory H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel Wholesale to Bangkok, Welcome to build the well and long standing business relationships with our company to create a glorious future together .customers' satisfaction is our eternal pursuit


    H13 Tool Steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications. H13 tool steel is classified as group H steels by the AISI classification system. This series of steels start from H1 to H19.

    AISI H-13 tool steel is characterized by:

    • Good resistance to abrasion at both low and high temperatures

    • High level of toughness and ductility

    • Uniform and high level of machinability and polishability

    • Good high-temperature strength and resistance to thermal fatigue

    • Excellent through-hardening properties

    • Very limited distortion during hardening

    In
    steel H13, the molybdenum and vanadium act as strengthening agents. The
    chromium content assists die steel H-13 to resist softening when used
    at high temperatures. H-13 die steels offers an excellent combination of
    shock and abrasion resistance, and possesses good red hardness. It is
    capable of withstanding rapid cooling and resists premature heat
    checking. Tool Steel H13 has good machinability, good weldability, good
    ductility, and can be formed by conventional means.

    Due to H13
    tool steel excellent combination of high toughness and fatigue
    resistance, AISI H13 hot work tool steel is used more than any other
    tool steel in tooling applications.

    1. Common H13 Tool Steel Related Specifications

    Country USA German Japan
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404
    Grades H13 1.2344/X40CrMoV5-1 SKD61

    2. H13 Tool Steel Chemical Composition

    ASTM A681 C Mn P S Si Cr V Mo
    H13 0.32 0.45 0.2 0.6 0.03 0.03 0.8 1.25 4.75 5.5 0.8 1.2 1.1 1.75
    DIN ISO 4957 C Mn P S Si Cr V Mo
    1.2344 /X40CrMoV5-1 0.35 0.42 0.25 0.5 0.03 0.02 0.8 1.2 4.8 5.5 0.85 1.15 1.1 1.5
    JIS G4404 C Mn P S Si Cr V Mo
    SKD61 0.35 0.42 0.25 0.5 0.03 0.02 0.8 1.2 4.8 5.5 0.8 1.15 1.0 1.5

    3. AISI H13 Steel Mechanical Properties

    Properties

    Metric Imperial
    Tensile strength, ultimate (@20°C/68°F, varies with heat treatment) 1200 – 1590 MPa 174000 – 231000 psi
    Tensile strength, yield (@20°C/68°F, varies with heat treatment) 1000 – 1380 MPa 145000 – 200000 psi
    Reduction of area (@20°C/68°F) 50.00% 50.00%
    Modulus of elasticity (@20°C/68°F) 215 GPa 31200 ksi
    Poisson’s ratio 0.27-0.30 0.27-0.30

    4. Forging of H13 Tool Steel
    Heating for forging must be done slowly and uniformly. Soak through at
    1900°-2000°F and reheat as often as necessary, stopping work when the
    temperature drops below 1650°F. After forging, cool slowly in lime,
    mica, dry ashes or furnace. H-13 should always be annealed after
    forging.

    5. Heat Treatment for H13 Tool Steels

    • Annealing

    Heat
    slowly to 1550°-1650°F, hold until entire mass is heated through, and
    cool slowly in the furnace (40F per hour) to about 1000°F, after which
    cooling rate may be increased. Suitable precautions must be taken to
    prevent excessive carburization or decarburization.

    • Stress Relieving

    When
    desirable to relieve the strains of machining, heat slowly to
    1050°-1250°F, allow to equalize, and then cool in still air (Strain
    Relieving). Â

    • Preheat Prior to Hardening

    Warm slightly before charging into the preheat furnace, which should be operating at 1400°-1500°F.

    • Hardening

    H13
    tool steel is a steel having very high hardenability and should be
    hardened by cooling in still air. The use of a salt bath or controlled
    atmosphere furnace is desirable to minimize decarburization, and if not
    available, pack hardening in spent pitch coke is suggested. The
    temperature employed is usually 1800°-1850°F, depending on size section.

    • Quenching

    Quench
    in still air or dry air blast. If complicated forms are to be hardened,
    an interrupted oil quench can be used. Quench part in oil and remove
    from bath when it just loses its color (1000°-1100°F). Finish cooling to
    below 150°-125°F in air, then temper immediately.

    • Tempering

    Tempering
    practice may vary with size and application, but is usually performed
    in the range of maximum secondary hardness or higher. Double tempering
    is recommended. The results below is H13 that was air quenched from
    1800°F and tempered for 4 hours at various temperatures. The results may
    be used as a guide, keeping in mind that parts of heavy section or mass
    may be several points lower in hardness.

    6. Application of AISI H13 Tool Steel

    • As Tools for Extrusion

    Part Aluminium, mag­nesium alloys, HRC Copper al­loys HRC Stainless steel HRC
    Dies, Backers, die-holders, liners, dummy blocks, stems 44-50 43-47 45-50
    41-50 40-48 40-48

    Austenitizing temperature

    1,870-1,885°F 1,900-1,920°F
    (1,020-1,030°C) (1,040-1,050°C)
    • As Plastic Molding Tool Steel

    Part Austenitizing temp. HRC
    Injection molds Compression/ transfer molds 1,870-1,885°F (1,020-1,030°C) 50-52
    Tempering 480°F (250°C)
    • Other Applications

    Applications Austenitizing temp HRC
    Severe cold punching, scrap shears 1,870-1,885°F 50-52
    (1,020-1,030°C)
    Tempering 480°F (250°C)
    Hot shearing 1,870-1,885°F
    (1,020-1,030°C) 50-52
    Tempering 480°F (250°C) or
    1,070-1,110°F 45-50
    (575-600°C)
    Shrink rings (e.g. for cemented carbide dies) 1,870-1,885°F 45-50
    (1,020-1,030°C)
    Tempering 1,070-1,110°F
    (575–600°C)
    Wear-resisting parts 1,870-1,885°F Core
    50-52
    Surface
    ~1000HV1
    (1,020-1,030°C)
    Tempering 1,070°F (575°C)
    nitrided

     

    If
    there are any queries about AISI H13 tool steel for hot working
    applications, please feel free to leave a comment below. And welcome
    enquiry of AISI H13 tool steel, we are professional and reliable
    supplier  for prime H13 tool steel materials.

  • Previous:
  • Next:



  • Hello, here is a Beautiful Black 1994 BMW 325is (2 door) Auto Trans Very Cold AC! Car & Driver Magazine Named this BMW 325is series to its Top 10 List 23 TIMES in a Row! And for Good reason, its a Grand Affordable Sports car with a back Seat & trunk that gets great gas Mileage on the highway & Handles Amazing, Very Porsche Like! Located in Fort Lauderdale & Posted by Special Video Services Amazing New HD Auto-Video Selling Service in the Beautiful Fort Lauderdale South Florida area @ just $1,650 Inquire 4 details here via message or @ www.SpecialVideoServices.com & I will reply ASAP



    Copper Recycling Azusa http://smartrecycling.com/scrap-metal-recycling-azusa/

    We deliver the widest range of scrap metal recycling services and collection storage containers for recyclables in the Azusa area. From special equipment for reclamation, disassembly or collection, to distinguishing the aftermarket most beneficial to you, Smart Recycling’s professional knowledge and flexibility is second to none.
    Smart Recycling, Inc.’s extensive know-how in the metals business makes it possible for us to obtain extremely competitive prices for your metals:
    Fixed Broker Sales – Allow Smart Recycling, Inc. broker your metals to get the greatest possible profit.
    Post Reclamation Salvage – Our means to maximize sales of your goods is first rate.
    Direct Supplier to Foundries and Mills – Removing the middle-man makes it possible for us to spend “top-dollar” to our clients.
    We maintain a steel shredder at our premises – Our investment in capital equipment puts extra money in your pocket.

    ==========================
    Copper Recycling Azusa

    In 2010, U.S. nonferrous scrap recuperation included:

    Light weight aluminum Recycling

    Obtaining to acknowledge the significant kinds of scrap steel is an essential step in ending up being a successful scrap steel vendor.

    With a recovery of 4.6 million metric heaps annually in the U.S, more aluminum is recycled compared to any kind of other nonferrous metals. Light weight aluminum is light and normally easy to flex. It will not produce triggers on a grinding wheel, as well as is nonmagnetic, unlike similarly tinted metals such as steel. Although aluminum comes in different grades, it is hard to recognize in between them.

    Copper Recycling Azusa

    Similar to any type of metal, less contamination improves the value, such as dismantling equipment to divide different types of metal, or getting rid of various other contaminants such as covering with concrete or other product. Webbing and screws need to be removed from patio chair. Look for aluminum scrap in real estate and demolition projects, consisting of door and also window frameworks, rain gutters, exterior siding, and wire. In vehicle stores, aluminum can be located in transmission housings and pistons.

    Copper Recycling

    Copper is the 3rd most widely recycled nonferrous metal. Actually, over 80% of copper ever before generated still exists. It is easy to determine as a result of its distinct colour, as well as that it is nonmagnetic. When placed against a grinding wheel, copper will certainly not spark.

    Stainless-steel Recycling

    Stainless-steel is the second most frequently recycled nonferrous metal. It includes steel alloys that includes a minimal proportion of chromium. An additional steel frequently utilized as an alloy in stainless steel is nickel. Unlike various other nonferrous metals, stainless-steel could be magnetic, depending after nickel content. Extra nickel lowers the magnetic buildings of the stainless-steel. Stainless-steel will trigger in feedback to a grinding wheel.

    Brass Recycling

    Brass is an alloy of copper and also zinc, along with percentages of other metals including manganese, tin, iron or light weight aluminum. The color variety of brass consists of red, yellow, silver and gold. In terms of magnetic attraction, it could reveal from nonmagnetic to a little magnetic. On the grinding wheel it will range between no stimulating to brief red stimulates.

    Copper Recycling Azusa

    https://www.youtube.com/watch?v=bplCTC2YrqY

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the House

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Plane