20 Years manufacturer AISI 1053 Carbon Steel (UNS G10530) in Iran

20 Years manufacturer
 AISI 1053 Carbon Steel (UNS G10530) in Iran

Short Description:

Chemical Composition The chemical composition of AISI 1053 carbon steel is outlined in the following table. Element Content (%) Iron, Fe 98.36-98.82 Manganese, Mn 0.7-1.0 Carbon, C 0.48-0.55 Sulfur, S 0.05 Phosphorous, P 0.04 Physical Properties The physical properties of AISI 1053 carbon steel are tabulated below. Properties Metric Imperial Density 7.7-8.03 g/cm3 0.278-0.290 l...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    Our company puts emphasis on the management, the introduction of talented personnel, and the construction of staff building, trying hard to improve the quality and liability consciousness of staff members. Our company successfully attained IS9001 Certification and European CE Certification of 20 Years manufacturer AISI 1053 Carbon Steel (UNS G10530) in Iran, We welcome new and old customers from all walks of life to contact us for future business relationships and mutual success!


    Chemical Composition

    The chemical composition of AISI 1053 carbon steel is outlined in the following table.

    Element Content (%)
    Iron, Fe 98.36-98.82
    Manganese, Mn 0.7-1.0
    Carbon, C 0.48-0.55
    Sulfur, S 0.05
    Phosphorous, P 0.04

    Physical Properties

    The physical properties of AISI 1053 carbon steel are tabulated below.

    Properties Metric Imperial
    Density 7.7-8.03 g/cm3 0.278-0.290 lb/in3

    Mechanical Properties

    The following table shows mechanical properties of AISI 1053 carbon steel.

    Properties Metric Imperial
    Elastic modulus 190-210 GPa 29700-30458 ksi
    Poisson’s ratio 0.27-0.30 0.27-0.30

  • Previous:
  • Next:



  • I edited this video to cut down the time by removing parts where I just stand there like an idiot. There were two problems with this bend. 1) This was the end of my work out and I was exhausted and 2) I was trying to beat the storm that was coming my way. These two things led to horrible form making this bend a lot harder than it had to be. I was still pleased with my training today.



    Listing Site: Property Site: http://tour.circlepix.com/home/5TMGAE/7625-E-CAMELBACK-Road-A344-Scottsdale-AZ-5553994 Furnished Rental just in time for …

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Heart

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Cup