AISI M2 Tool Steel is molybdenum based high-speed steel in tungsten–molybdenum series. HSS grade steel M2 is a medium alloyed high speed steel which has good machinability. The H-SS M2 chemical composition gives a good combination of well-balanced toughness, wear resistance and red hardness properties. Widely used for cutting tools such as twist drills, taps, milling cutters, saws, knives etc. Also commonly used in cold work punches and dies and cutting applications involving high speed...
We insist on the principle of development of 'High quality, Efficiency, Sincerity and Down-to-earth working approach' to provide you with excellent service of processing for 20 Years Factory M2 Tool Steel | 1.3343 | HS-6-5-2C| SKH51 Wholesale to Luxembourg, Let's cooperate hand in hand to jointly make a beautiful future. We sincerely welcome you to visit our company or contact us for cooperation!
is a medium alloyed high speed steel which has good machinability. The
H-SS M2 chemical composition gives a good combination of well-balanced
toughness, wear resistance and red hardness properties. Widely used for
cutting tools such as twist drills, taps, milling cutters, saws, knives
etc. Also commonly used in cold work punches and dies and cutting
applications involving high speed and light cuts.
Grade M2 High Speed Steel is by far the most popular high speed steel replacing high speed steel gradein most applications because of its superior properties and relative economy.
1. Common M2 Tool Steel Related Specifications and Equivalents
2. ASTM M2 Tool Steel Chemical Composition Properties
|M2 regular C||0.78||0.88||0.15||0.40||0.03||0.03||0.20||0.45||3.75||4.50||1.75||2.20||4.50||5.50||5.50||6.75|
|DIN ISO 4957||C||Mn||P||S||Si||Cr||V||Mo||W|
3. AISI HSS M2 Tool Steel Mechanical Properties
Physical Properties of HSS M2 Material
|Density||0.294 lb/in3 (8138 kg/m3)|
|Modulus of Elasticity||0.294 lb/in3 (8138 kg/m3)|
|Thermal conductivity||24 Btu/ft/hr/°F 41.5 W/m/°K|
|Machinability||65% of a 1% carbon steel|
AISI M2 Tool Steels Properties Mechanical
|Hardness, Rockwell C (tempered at 1150°F, quenched at 2200°F)||62||62|
|Hardness, Rockwell C (as hardened, quenched at 2200°F)||65||65|
|Compressive yield strength (when tempered at 300°F)||3250 MPa||471000 psi|
|Izod impact unnotched (when tempered at 300°F)||67 J||49.4 ft-lb|
|Abrasion (loss in mm3, as-hardened; ASTM G65)||25.8||25.8|
|Abrasion (loss in mm3, tempered at 1275°F; ASTM G65)||77.7||77.7|
|Elastic modulus||190-210 GPa||27557-30458 ksi|
M2 Steels Thermal Properties
|CTE, linear (@20.0 – 100°C/ 68.0 – 212°F)||10 μm/m°C||5.56 μin/in°F|
|CTE, linear (@20.0 – 500°C/68.0 – 932°F)||12.2 μm/m°C||6.78 μin/in°F|
|CTE, linear (@20.0 – 850°C/68.0 – 1560°F)||12.6 μm/m°C||7 μin/in°F|
4. Forging of AISI M2 High Speed Steel
heat M2 HSS steel slowly and uniformly to 850-900°C. The heat should
then be increased more quickly to the forging temperature of
1050-1150°C. If during the forging
the temperature of the M2 high speed tool steel material drops below
880-900°C, re-heating will be necessary. Cool the M2 steel component
very slowly after forging.
5. Heat Treatment of M2 Steel HSS
to 1600° F, soak thoroughly at heat. Furnace cool 25° F per hour to
900° F, air cool to room temperature. Approximate annealed hardness 241
Stress Relief of Unhardened Material: Heat slowly
to 1200 to 1250° F. Soak for two hours per inch of thickness at heat.
Slow cool (furnace cool if possible) to room temperature.
Preheat: Heat slowly to 1550° F, soak thoroughly, heat to 1850° F, soak thoroughly.
time in the furnace varies from a few minutes to a 15 minutes,
depending tool size, heat capacity of the furnace, and the size of the
charge. – Heat to 2150 to 2200° F for max. toughness and minimum
distortion. – Heat to 2250 to 2275° F for max. hardness and abrasion
hardness, oil quench to 150-200° F. Air quench to 150° F. When quenching
in hot salt maintain the quench just above the Ms temperature. After
equalizing withdraw parts from the hot salt and air cooled to 150° F.
temper is mandatory, three tempers are sometimes preferred. Soak for 2
hours per inch of thickness. Air cool to room temperature between
tempers. The best tempering range for hardness, strength and toughness
is 1000 to 1050° F.
|Temper° F||Rockwell “C”||Temper° F||Rockwell “C”|
6. Machinability of AISI M2 Tool Steel H-SS
of HSS M2 tool steels can be carried out using grinding methods.
However, they have poor grinding capability and hence they are regarded
as “medium” machinability tool steel under annealed conditions. The
machinability of these tool steels M2 is only 50% of that of the easily
machinable W group or water hardening tool steels.
7. M2 Tool Steel Applications
The main use of high-speed steels continues to be in the manufacture of various cutting tools.
applications for M2 high speed steel are twist drills, reamers,
broaching tools, taps, milling tools, metal saws. M2 is suitable for
cold forming tools such as extrusion rams and dies, also widely used in
all kinds of cutting tools, knife and punches and die applications,
plastic moulds with elevated wear resistance and screws.
Drilling mild steel angle iron is easy – short movie from
www.ttp-hard-drills.net. Easily drill holes in steel using TTP Hard
Drills – these cobalt drills with added cobalt and molybdenum come
with a 135 degree split point – maximum cutting action in minimum time
- suitable for drilling harder steel and alloys.
Using a hand drill the TTP cobalt drills 135 degrees split point ensures less wander when starting the drill and reduces the ‘drag’ in the centre of the drill.
TOO HIGH DRILL SPEED
TOO MUCH PRESSURE
TOO MUCH HEAT
Avoid these mistakes and you can cut the steel easily with our TTP drills.
When cutting, start slowly to find the chip and keeping the drill
cutting not rubbing. Be sure to keep it cool. Apply a cooling aid
frequently. See TTP cut it as a convenient cooling paste which is
perfect for hand drilling away from the bench.
The Superior Hardness of our products due to Tungsten and Molybdenum
base and High Temperature Resistance due to addition of Cobalt mean
that steel can be cut efficiently without the need to make mistakes.
Available in USA and Europe
This Drill on Amazon: