19 Years manufacturer D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Manufacturer in Bolivia

19 Years manufacturer
 D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Manufacturer in Bolivia

Short Description:

1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    We depend on sturdy technical force and continually create sophisticated technologies to meet the demand of 19 Years manufacturer D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Manufacturer in Bolivia, "Passion, Honesty, Sound service, Keen cooperation and Development" are our goals. We are here expecting friends all over the world!


    1. Relevant D2 Steel Specifications

    Country USA German Japan
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404
    Grades D2 1.2379/X153CrMo12 SKD11

    2. D2 Tool Steel Chemical Composition

    ASTM A681 C Mn P S Si Cr V Mo
    D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2
    DIN ISO 4957 C Mn P S Si Cr V Mo
    1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1
    JIS G4404 C Mn P S Si Cr V Mo
    SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2

    3. AISI Grade D2 Steel Mechanical Properties

    Mechanical Properties Metric Imperial
    Hardness, Knoop (converted from Rockwell C hardness) 769 769
    Hardness, Rockwell C 62 62
    Hardness, Vickers 748 748
    Izod impact unnotched 77.0 J 56.8 ft-lb
    Poisson’s ratio 0.27-0.30 0.27-0.30
    Elastic modulus 190-210 GPa 27557-30457 ksi

    Thermal Properties

    Properties

    Conditions

    T (°C)

    Treatment

    Thermal expansion 10.4 x 10-6/ºC 20-100

    4. AISI/ASTM A681 D2 Grade Steel Forging

    Heating for forging of AISI D2 tool steel should
    be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
    as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
    die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
    should always be annealed after forging.

    5. D2 Tool Steel Heat Treatment

    • Heat Treatment

    ASTM  D2 steels alloy should be preheated very slowly to 815oC (1500oF) and  then temperature can be increased to 1010oC (1850oF). They are then held  at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).

    • Annealing

    Annealing  of D2 tool steels material should be done at 871 to 898oC (1600 to  1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or  less.after which cooling rate may be increased. Suitable precautions  must be taken to prevent excessive carburization or decarburization.

    • Stress Relieving

    When  desirable to relieve the strains of machining, heat D2 grade steel  slowly to 1050°-1250°F, allow to equalize, and then cool in still air  (Strain Relieving).

    • Preheat Prior To Hardening

    Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.

    • Hardening

    After  thorough preheating, heat to 1800°-1850°F. Hold the work piece at the  hardening temperature until it is completely and uniformly heated.

    • Quenching

    AISI  D2 steel tool material is an air hardening steel and will develop  hardness on cooling in still air. To avoid scaling and prevent  decarburization of the work piece surface, controlled atmosphere or  vacuum furnaces are recommended. If these furnaces are not available,  pack hardening, salt baths or wrapping the piece in stainless steel foil  will provide some degree of surface protection in the hardening  process. Parts should be allowed to cool to 150F, or to where they can  be held in the bare hand, and then temper immediately.

    • Tempering

    The  tempering temperature on material D2 steel may be varied according to  the desired hardness. D2 steels can be tempered at 204oC (400oF) for  achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell  C hardness of 54.

    6. D2 Tool Steel Material Application
     AISI grade D2 tool steels are used for long run tooling applications,  where wear resistance is important, such as blanking or forming dies and  thread rolling dies.

    Some main applications for D2 tool steel are as below:

    Blanking  Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long  Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls,  Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread  Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear  Parts.

    We usually hold D2 tool  steel on sale activities, and you would have our price on regular  schedule. Contact us and sign in our newsletter to have D2 tool steel  materials price list and commercial quote today.

  • Previous:
  • Next:



  • TRAFITAL spa http://trafital.paginegialle.it/produzione-acciai-trafilati-rettificati.html 301, v. Colombo Tel 0331 368900 Fax 0331 368940 Since 1953 we have been manufacturing drawn bars in carbon and alloy steel in the following sections: flats up to 500x40mm, squares up to 150x150mm, hexagons up to 100mm, angles up to 100x100x10mm, T-sections, splined shafts, cold-drawn special section bars to customer’s design. Peeled-reeled and ground bars: rounds up to 160mm. TRAFITAL spa – certified to ISO 9000 by IGQ since 1994 – was the first Italian firm to specialize in a wide range of large- and special-size bars off the shelf ; radial-edged flat and square drawn bars to customer’s design; drawn steel sections for racks; narrow tolerances on ground bars up to h6 and tolerances on cold-drawn bars, including h9 tolerances for feather keys; fixed or precision length up to ± 1mm. – http://www.paginegialle.it/trafital



    Find these LED off-road lights and many more listed here:

    https://headlightrevolution.com/off-road-lights/led-pod-lights/

    Our Dually vs. Optimus + Vision X Light Cannon video has been wanting to be made for quite a long time and we finally got it out here on Youtube. We are going head to head with Rigid Industries very popular “Dually” LED off road light and comparing it against the Vision X’s “Optimus” series. We will be using our new test field to demonstrate the type of beam pattern and intensity of each Light. Stay tuned and you can see the brand new (as of 2013) Vision X Light Cannon! That thing is an amazing LED Light!

    For anymore questions about these awesome lights leave a comment or message us here on Youtube and we will get back to you!

    Want to get more reviews and updates on the latest in lighting technology subscribe to this Youtube channel and Like us on Facebook!

    https://www.facebook.com/HeadlightRevolution

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Cup

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Heart