17 Years Factory H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel Wholesale to Roman

17 Years Factory
 H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel Wholesale to Roman

Short Description:

H13 Tool Steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications. H13 tool steel is classified as group H steels by the AISI classification system. This series of steels start from H1 to H19. AISI H-13 tool steel is characterized by: Good resistance to abrasion at both low and high temperatures High level of toughness and ductility Uniform and high level of machinability and polishability Good high-temperature strength and resistance to t...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    We have a highly efficient team to deal with inquiries from customers. Our goal is "100% customer satisfaction by our product quality, price & our team service" and enjoy a good reputation among clients. With many factories, we can provide a wide range of 17 Years Factory H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel Wholesale to Roman, If you have any comments about our company or products, please feel free to contact us, your coming mail will be highly appreciated.


    H13 Tool Steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications. H13 tool steel is classified as group H steels by the AISI classification system. This series of steels start from H1 to H19.

    AISI H-13 tool steel is characterized by:

    • Good resistance to abrasion at both low and high temperatures

    • High level of toughness and ductility

    • Uniform and high level of machinability and polishability

    • Good high-temperature strength and resistance to thermal fatigue

    • Excellent through-hardening properties

    • Very limited distortion during hardening

    In
    steel H13, the molybdenum and vanadium act as strengthening agents. The
    chromium content assists die steel H-13 to resist softening when used
    at high temperatures. H-13 die steels offers an excellent combination of
    shock and abrasion resistance, and possesses good red hardness. It is
    capable of withstanding rapid cooling and resists premature heat
    checking. Tool Steel H13 has good machinability, good weldability, good
    ductility, and can be formed by conventional means.

    Due to H13
    tool steel excellent combination of high toughness and fatigue
    resistance, AISI H13 hot work tool steel is used more than any other
    tool steel in tooling applications.

    1. Common H13 Tool Steel Related Specifications

    Country USA German Japan
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404
    Grades H13 1.2344/X40CrMoV5-1 SKD61

    2. H13 Tool Steel Chemical Composition

    ASTM A681 C Mn P S Si Cr V Mo
    H13 0.32 0.45 0.2 0.6 0.03 0.03 0.8 1.25 4.75 5.5 0.8 1.2 1.1 1.75
    DIN ISO 4957 C Mn P S Si Cr V Mo
    1.2344 /X40CrMoV5-1 0.35 0.42 0.25 0.5 0.03 0.02 0.8 1.2 4.8 5.5 0.85 1.15 1.1 1.5
    JIS G4404 C Mn P S Si Cr V Mo
    SKD61 0.35 0.42 0.25 0.5 0.03 0.02 0.8 1.2 4.8 5.5 0.8 1.15 1.0 1.5

    3. AISI H13 Steel Mechanical Properties

    Properties

    Metric Imperial
    Tensile strength, ultimate (@20°C/68°F, varies with heat treatment) 1200 – 1590 MPa 174000 – 231000 psi
    Tensile strength, yield (@20°C/68°F, varies with heat treatment) 1000 – 1380 MPa 145000 – 200000 psi
    Reduction of area (@20°C/68°F) 50.00% 50.00%
    Modulus of elasticity (@20°C/68°F) 215 GPa 31200 ksi
    Poisson’s ratio 0.27-0.30 0.27-0.30

    4. Forging of H13 Tool Steel
    Heating for forging must be done slowly and uniformly. Soak through at
    1900°-2000°F and reheat as often as necessary, stopping work when the
    temperature drops below 1650°F. After forging, cool slowly in lime,
    mica, dry ashes or furnace. H-13 should always be annealed after
    forging.

    5. Heat Treatment for H13 Tool Steels

    • Annealing

    Heat
    slowly to 1550°-1650°F, hold until entire mass is heated through, and
    cool slowly in the furnace (40F per hour) to about 1000°F, after which
    cooling rate may be increased. Suitable precautions must be taken to
    prevent excessive carburization or decarburization.

    • Stress Relieving

    When
    desirable to relieve the strains of machining, heat slowly to
    1050°-1250°F, allow to equalize, and then cool in still air (Strain
    Relieving). Â

    • Preheat Prior to Hardening

    Warm slightly before charging into the preheat furnace, which should be operating at 1400°-1500°F.

    • Hardening

    H13
    tool steel is a steel having very high hardenability and should be
    hardened by cooling in still air. The use of a salt bath or controlled
    atmosphere furnace is desirable to minimize decarburization, and if not
    available, pack hardening in spent pitch coke is suggested. The
    temperature employed is usually 1800°-1850°F, depending on size section.

    • Quenching

    Quench
    in still air or dry air blast. If complicated forms are to be hardened,
    an interrupted oil quench can be used. Quench part in oil and remove
    from bath when it just loses its color (1000°-1100°F). Finish cooling to
    below 150°-125°F in air, then temper immediately.

    • Tempering

    Tempering
    practice may vary with size and application, but is usually performed
    in the range of maximum secondary hardness or higher. Double tempering
    is recommended. The results below is H13 that was air quenched from
    1800°F and tempered for 4 hours at various temperatures. The results may
    be used as a guide, keeping in mind that parts of heavy section or mass
    may be several points lower in hardness.

    6. Application of AISI H13 Tool Steel

    • As Tools for Extrusion

    Part Aluminium, mag­nesium alloys, HRC Copper al­loys HRC Stainless steel HRC
    Dies, Backers, die-holders, liners, dummy blocks, stems 44-50 43-47 45-50
    41-50 40-48 40-48

    Austenitizing temperature

    1,870-1,885°F 1,900-1,920°F
    (1,020-1,030°C) (1,040-1,050°C)
    • As Plastic Molding Tool Steel

    Part Austenitizing temp. HRC
    Injection molds Compression/ transfer molds 1,870-1,885°F (1,020-1,030°C) 50-52
    Tempering 480°F (250°C)
    • Other Applications

    Applications Austenitizing temp HRC
    Severe cold punching, scrap shears 1,870-1,885°F 50-52
    (1,020-1,030°C)
    Tempering 480°F (250°C)
    Hot shearing 1,870-1,885°F
    (1,020-1,030°C) 50-52
    Tempering 480°F (250°C) or
    1,070-1,110°F 45-50
    (575-600°C)
    Shrink rings (e.g. for cemented carbide dies) 1,870-1,885°F 45-50
    (1,020-1,030°C)
    Tempering 1,070-1,110°F
    (575–600°C)
    Wear-resisting parts 1,870-1,885°F Core
    50-52
    Surface
    ~1000HV1
    (1,020-1,030°C)
    Tempering 1,070°F (575°C)
    nitrided

     

    If
    there are any queries about AISI H13 tool steel for hot working
    applications, please feel free to leave a comment below. And welcome
    enquiry of AISI H13 tool steel, we are professional and reliable
    supplier  for prime H13 tool steel materials.

  • Previous:
  • Next:



  • New Morning ชุดพิมพ์เค้ก 3 ขนาด242628cm – Black
    สั่งซื้อออนไลน์ : http://p2b.us/whl9g6

    คุณกำลังต้องการ New Morning ชุดพิมพ์เค้ก 3 ขนาด242628cm – Black เพื่อช่วยแก้ไขปัญหา อยูใช่หรือไม่ ถ้าใช่คุณมาถูกที่แล้ว เรามีสินค้า ที่ท่านต้องการแนะนำ พร้อมมีแหล่งซื้อ สินค้าราคาถูก แนะนำให้ท่าน New Morning ชุดพิมพ์เค้ก 3 ขนาด242628cm – Black ราคาถูกให้กับคุณ

    ซื้อของออนไลน์เก็บเงินปลายทาง ส่งฟรี ของแท้ ของดี ราคาถูก New Morning ชุดพิมพ์เค้ก 3 ขนาด242628cm – Black New Morning ชุดพิมพ์เค้ก 3 ขนาด – Black พิมพ์เค้ก Non stick spring-form ก้นถอดได้ Material : carbon steel Coating material : non-stick coating (Xinflon LFGB and FDA tested) Temperature resistance : from 1 degree celcius to 280 degree ในเซ็ทประกอบด้วย 3 ขนาด – 24 cm – 26 cm – 28 cm – ความสูง 7 cm ข้อมูลจำเพาะของ New Morning ชุดพิมพ์เค้ก 3 ขนาด242628cm – Black รายการสินค้าในกล่อง New Morning ชุดพิมพ์เค้ก 3 ขนาด – Black คุณสมบัติทั่วไปซื้อของออนไลน์เก็บเงินปลายทาง ส่งฟรี ของแท้ ของดี ราคาถูก NE949HLAJ96DANTH-910538 Care label For oven use only สี Black Main material Carbon steel โมเดล NS23 Size (cm) 28 x 28 x 6.5 Weight (kg) 0.96 Production country China Promotion Texts SHIPPED FROM Thailand ของแท้ ของดี ส่งฟรี เก็บเงินปลายทาง…

    หมวดหมู่ shop-bakeware
    ราคา 549 บาท ถูกที่สุด

    สั่งซื้อพร้อมส่วนลด เก็บเงินปลายทาง http://p2b.us/whl9g6
    ———————————————————————————-
    คำค้นหา : New, Morning, ชุด, พิมพ์, เค้ก, 3, ขนาด, 242628cm, Black, New Morning ชุดพิมพ์เค้ก 3 ขนาด242628cm – Black

    New #Morning #ชุด #พิมพ์ #เค้ก #3 #ขนาด #242628cm #Black #New Morning ชุดพิมพ์เค้ก 3 ขนาด242628cm – Black



    Zeitgeist: The Movie is a 2007 documentary film by Peter Joseph. This movie was first presented as a public performance and was later published online, along with a website:

    This version includes Peter Joseph’s 2010 updates.
    For more information (Director’s notes, sources and references), please refer to the companion source guide (PDF):

    http://tinyurl.com/zgcompanionguide

    http://www.zeitgeistmovie.com/

    Embedding & sharing is highly encouraged.

    Note: This LTI Repository location contains only “official”, fully proofread versions of the transcript & its derived translations. More translations will be added as they are completed.

    If your language is not yet represented here, consider helping these efforts by joining your language team at http://bit.ly/Zj0QWC (LTI Forum).

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Car

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Key