13 Years manufacturer BS EN 42CrMo4 | 1.7225 Alloy Engineering Steel Factory for Sudan
BS EN 42crmo4 Alloy Steel is a common chromium-molybdenum steel that usually used after quenchedand tempered, with high intensity, high hardenability. BS EN 42CrMo4round steel has better performance than 34CrMo4 steel due to the carbonand chromium content is higher. 42CrMo4 alloy steel has higher strength and hardenability. The 42CrMo4 alloy material alsohas high fatigue strength and good low-temperature impact toughness. The temper brittleness is not obvious. Although 42CrMo4 steel is mo...
To constantly improve the management system by virtue of the rule of "sincerely, good faith and quality are the base of enterprise development", we widely absorb the essence of related products internationally, and constantly develop new products to meet the demands of customers for 13 Years manufacturer BS EN 42CrMo4 | 1.7225 Alloy Engineering Steel Factory for Sudan, We will wholeheartedly welcome all clients in the industry both at home and abroad to cooperate hand in hand, and create a bright future together.
BS ENAlloy Steel
is a common chromium-molybdenum steel that usually used after quenched
and tempered, with high intensity, high hardenability. BS EN 42CrMo4
round steel has better performance than 34CrMo4 steel due to the carbon
and chromium content is higher.
has higher strength and hardenability. The 42CrMo4 alloy material also
has high fatigue strength and good low-temperature impact toughness. The
temper brittleness is not obvious.
Although 42CrMo4 steel is more expensive than 41Cr4 steel, it is more
preferable in terms of material properties. EN 42CrMo4 alloy
engineering steel materials have been widely used in automotive driving
elements. Otai Steel is able to supply you prime quality of 42CrMo4
alloy steel materials with wide range.
1.42CrMo4 Alloy Steel Supply Range
42CrMo4 Round bar Sizes: 80mm – 1200mm
Steel 42CrMo4 Flat and Plate: 10mm-1500mm thickness x 200-3000mm width
Other steel shape and sizes available according to your requirements.
Surface condition: Black, rough machined, peeled, turned or other requirements according to your requirements.
2.BS EN 42CrMo4 Alloy Steel Relevant Specifications and Equivalents
|BS EN 10250||Material No.||DIN||-3-1991||BS 970-1955||AS 1444||AFNOR|
3.42CrMo4 Alloy Steel Chemical Composition
|0.38-0.45||0.60-0.90||0.40 max||0.035 max||0.035 max||0.90-1.20||0.15-0.30|
4. DIN 42CrMo4 Alloy Steel Mechanical Properties
|Size Ø mm||Yield stress
|Ultimate tensile Stress,
KV, Joule, min.
|<40||750||1000-1200||11||295-355||35 at 20ºC|
|40-95||650||900-1100||12||265-325||35 at 20ºC|
|>95||550||800-950||13||235-295||35 at 20ºC|
5. Heat Treatment of 42CrMo4 Steels
Annealing of 42CrMo4 Steels
Heat steel 42CrMo4 forged steel slowly and thoroughly to 800-850°C;
Cool slowly in the furnace to the temperature 480°;
Complete annealing the steel in the air.
Quenched and Tempered (Q+T)
Heat 42CrMo4 steel slowly to 880°C;
Soak at this temperature then quench in oil;
Temper as soon as 42CrMo4 steel reach room temperature (20°C);
Heat uniformly to the suitable temperature of 560°C;
Withdraw the 42CrMo4 material from the furnace and cool in the air.
6. Forging of 42CrMo4 Alloy Steel
Preheat 42CrMo4 engineering steel uniformly and slowly;
Increase the forging temperature up to 1150-1200°C.
Always keep the forging temperature above at least 850°C
steel 42CrMo4 has only limited weldability. Preheating to 200-300°C is
strongly recommended; the upper limit should not be exceeded because of
risk for deterioration of the chrome layer.
Alloy steel 42CrMo4
can be friction welded. However, precautions are necessary so as to
limit the formation of undesirable microstructures in the welded zone.
8.Application of 42CrMo4 Alloy Steels
42CrMo4 alloy steel is widely used for engineering steel purpose, such
as: making various kinds of machinery, automobile, mining spare part,
the gearwheel of the engine, the driving gear of supercharger, the
connecting rob, the pinchock under the high pressure, parts for power
train applications, cold formed fastener components, shafts, gears,
drill collars for the oil exploration, etc.
Overview on KARL DEUTSCH Ultrasonic Systems: ECHOGRAPH-STPS Ultrasonic Bar testing; ECHOGRAPH-HRP.S Ultrasonic testing of bright bars; ECHOGRAPH RTPS Ultrasonic testing portal for round bars; KNPS-Echograph Billet Testing; ECHOPRAPH ALPT / RPTS Ultrasonic testing of round billets; ECHOGRAPH TTPS Ultrasonic testing of round billet samples; ECHOGRAPH-HRP.R High speed seamless tube testing without rotation; RPS.R-Echograph Ultrasonic Tube Testing with Helical Feeding; ECHOGRAPH-RPT.R Phased Array Testing portal for seamless tubes; ECHOGRAPG Testing of welded pipes; ECHOGRAPH-BAPS+SNHF Online ultrasonic test of strips and ERW-pipes; ECHOGRAPH-SNHF bi-directional testing portal; SNUL-Echograph Weld Testing on LSAW-Pipes; SNUS-Echograph Weld Testing on HSAW-Pipes (Helical Weld); SCHN-ECHOGRAPH Ultrasonic Testing of Rails; STFL-ECHOGRAPH Ultrasonic Testing of Pressure Cylinders. More information can be found on the KARL DEUTSCH website: http://www.karldeutsch.de
In 1979, the U.S. Customs Service reported that 87% of all marijuana seizures in the U.S. were made in the South Florida area. Due to the region’s 5,000 miles of coast and coastal waterways and close proximity to the Caribbean and Latin America, South Florida was a pot smuggler’s paradise. In sharp contrast to the brazenly violent cocaine cowboys of the 1980s, Miami’s marijuana smugglers were cooler, calmer, and typically nonviolent. Square Grouper paints a vivid portrait of Miami’s pot smuggling culture in the ’70s and ’80s and its major players: the smuggling Black Tuna Gang, the pot dealing Ethiopian Zion Coptic Church and the tiny fishing village of Everglades City.
MPAA Rating: R