13 Years Factory H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel Supply to Palestine

13 Years Factory
 H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel Supply to Palestine

Short Description:

H13 Tool Steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications. H13 tool steel is classified as group H steels by the AISI classification system. This series of steels start from H1 to H19. AISI H-13 tool steel is characterized by: Good resistance to abrasion at both low and high temperatures High level of toughness and ductility Uniform and high level of machinability and polishability Good high-temperature strength and resistance to t...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    We stick to our enterprise spirit of "Quality, Efficiency, Innovation and Integrity". We aim to create more value for our customers with our rich resources, advanced machinery, experienced workers and excellent services for 13 Years Factory H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel Supply to Palestine, items won certifications with the regional and international primary authorities. For far more detailed information, please contact us!


    H13 Tool Steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications. H13 tool steel is classified as group H steels by the AISI classification system. This series of steels start from H1 to H19.

    AISI H-13 tool steel is characterized by:

    • Good resistance to abrasion at both low and high temperatures

    • High level of toughness and ductility

    • Uniform and high level of machinability and polishability

    • Good high-temperature strength and resistance to thermal fatigue

    • Excellent through-hardening properties

    • Very limited distortion during hardening

    In
    steel H13, the molybdenum and vanadium act as strengthening agents. The
    chromium content assists die steel H-13 to resist softening when used
    at high temperatures. H-13 die steels offers an excellent combination of
    shock and abrasion resistance, and possesses good red hardness. It is
    capable of withstanding rapid cooling and resists premature heat
    checking. Tool Steel H13 has good machinability, good weldability, good
    ductility, and can be formed by conventional means.

    Due to H13
    tool steel excellent combination of high toughness and fatigue
    resistance, AISI H13 hot work tool steel is used more than any other
    tool steel in tooling applications.

    1. Common H13 Tool Steel Related Specifications

    Country USA German Japan
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404
    Grades H13 1.2344/X40CrMoV5-1 SKD61

    2. H13 Tool Steel Chemical Composition

    ASTM A681 C Mn P S Si Cr V Mo
    H13 0.32 0.45 0.2 0.6 0.03 0.03 0.8 1.25 4.75 5.5 0.8 1.2 1.1 1.75
    DIN ISO 4957 C Mn P S Si Cr V Mo
    1.2344 /X40CrMoV5-1 0.35 0.42 0.25 0.5 0.03 0.02 0.8 1.2 4.8 5.5 0.85 1.15 1.1 1.5
    JIS G4404 C Mn P S Si Cr V Mo
    SKD61 0.35 0.42 0.25 0.5 0.03 0.02 0.8 1.2 4.8 5.5 0.8 1.15 1.0 1.5

    3. AISI H13 Steel Mechanical Properties

    Properties

    Metric Imperial
    Tensile strength, ultimate (@20°C/68°F, varies with heat treatment) 1200 – 1590 MPa 174000 – 231000 psi
    Tensile strength, yield (@20°C/68°F, varies with heat treatment) 1000 – 1380 MPa 145000 – 200000 psi
    Reduction of area (@20°C/68°F) 50.00% 50.00%
    Modulus of elasticity (@20°C/68°F) 215 GPa 31200 ksi
    Poisson’s ratio 0.27-0.30 0.27-0.30

    4. Forging of H13 Tool Steel
    Heating for forging must be done slowly and uniformly. Soak through at
    1900°-2000°F and reheat as often as necessary, stopping work when the
    temperature drops below 1650°F. After forging, cool slowly in lime,
    mica, dry ashes or furnace. H-13 should always be annealed after
    forging.

    5. Heat Treatment for H13 Tool Steels

    • Annealing

    Heat
    slowly to 1550°-1650°F, hold until entire mass is heated through, and
    cool slowly in the furnace (40F per hour) to about 1000°F, after which
    cooling rate may be increased. Suitable precautions must be taken to
    prevent excessive carburization or decarburization.

    • Stress Relieving

    When
    desirable to relieve the strains of machining, heat slowly to
    1050°-1250°F, allow to equalize, and then cool in still air (Strain
    Relieving). Â

    • Preheat Prior to Hardening

    Warm slightly before charging into the preheat furnace, which should be operating at 1400°-1500°F.

    • Hardening

    H13
    tool steel is a steel having very high hardenability and should be
    hardened by cooling in still air. The use of a salt bath or controlled
    atmosphere furnace is desirable to minimize decarburization, and if not
    available, pack hardening in spent pitch coke is suggested. The
    temperature employed is usually 1800°-1850°F, depending on size section.

    • Quenching

    Quench
    in still air or dry air blast. If complicated forms are to be hardened,
    an interrupted oil quench can be used. Quench part in oil and remove
    from bath when it just loses its color (1000°-1100°F). Finish cooling to
    below 150°-125°F in air, then temper immediately.

    • Tempering

    Tempering
    practice may vary with size and application, but is usually performed
    in the range of maximum secondary hardness or higher. Double tempering
    is recommended. The results below is H13 that was air quenched from
    1800°F and tempered for 4 hours at various temperatures. The results may
    be used as a guide, keeping in mind that parts of heavy section or mass
    may be several points lower in hardness.

    6. Application of AISI H13 Tool Steel

    • As Tools for Extrusion

    Part Aluminium, mag­nesium alloys, HRC Copper al­loys HRC Stainless steel HRC
    Dies, Backers, die-holders, liners, dummy blocks, stems 44-50 43-47 45-50
    41-50 40-48 40-48

    Austenitizing temperature

    1,870-1,885°F 1,900-1,920°F
    (1,020-1,030°C) (1,040-1,050°C)
    • As Plastic Molding Tool Steel

    Part Austenitizing temp. HRC
    Injection molds Compression/ transfer molds 1,870-1,885°F (1,020-1,030°C) 50-52
    Tempering 480°F (250°C)
    • Other Applications

    Applications Austenitizing temp HRC
    Severe cold punching, scrap shears 1,870-1,885°F 50-52
    (1,020-1,030°C)
    Tempering 480°F (250°C)
    Hot shearing 1,870-1,885°F
    (1,020-1,030°C) 50-52
    Tempering 480°F (250°C) or
    1,070-1,110°F 45-50
    (575-600°C)
    Shrink rings (e.g. for cemented carbide dies) 1,870-1,885°F 45-50
    (1,020-1,030°C)
    Tempering 1,070-1,110°F
    (575–600°C)
    Wear-resisting parts 1,870-1,885°F Core
    50-52
    Surface
    ~1000HV1
    (1,020-1,030°C)
    Tempering 1,070°F (575°C)
    nitrided

     

    If
    there are any queries about AISI H13 tool steel for hot working
    applications, please feel free to leave a comment below. And welcome
    enquiry of AISI H13 tool steel, we are professional and reliable
    supplier  for prime H13 tool steel materials.

  • Previous:
  • Next:



  • E-mail: monica@wxtechwell.com
    Mobile/ Whatsapp:+86-18018304331
    Skype: monica198614
    www.wxtechwell.com
    www.cold-rollformingmachine.com
    www.roofrollformingmachine.com

    Steel Silo Stiffener Panel Roll Forming Machine, Grain Silo Stiffener Roll Forming Machine

    A. Work Flowing:

    Loading coil car – Un-coiler – guiding device – feeder – leveller – shear roll former – hydraulic press – curving -hydraulic cutting – stacker – PLC control

    B. Main Specification:

     Suitable material: Galvanized sheet, Zinc Alumina sheet
     Material yield strength: 310Mpa
     Material thickness: 2.5-4.0mm
     Max. Feeding coil width: 1250mm
     Machine working speed: 4-8m/min
     Forming station: approx 18 stations
     Size of roll shaft: Ф120mm
     Roller material: GCr15, quenching HRC 58-62 °
     Total power: approx 180KW
     Power supply: AC440V+/-10%, 50Hz, 3 Phase
     Whole line dimention: about 35M X 4.5M ( L X W )
     Installation height: 4.5m
     Total weith of machine: approx 70 tons

    Applications:

    Steel silo corrugated sheet, steel silo corrugated panel, silo wall sheet, silo corrugated wall sheet, silo wall panel, silo corrugated wall panel, silo side panel, steel corrugated sheet, steel corrugated wall panel, steel corrugated panel

    Any questions, please contact us:
    www.wxtechwell.com
    www.cold-rollformingmachine.com
    E-mail/Skype:china@wxtechwell.com
    Tel/ Whatsapp/IMO:+86-133-6565-3972



    Knives https://youtu.be/e1TkeGwk8zM
    School of Self Reliance reviews some good knives to have for Bugging Out, Survival, Camping, and woodworking.
    Find Us, Like Us, Follow Us, Share Us, & Donate to Help Us!

    PAYPAL: https://www.paypal.me/SchoolofSelfReliance

    PATREON: http://www.patreon.com/SchoolOfSelfReliance

    FACEBOOK: http://www.facebook.com/TheSchoolOfSelfReliance/

    TWITTER: http://twitter.com/SelfRelianceSch

    WORDPRESS: http://prepclub.wordpress.com/

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Cup

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Car