11 Years manufacturer EN DIN 34CrNiMo6 | 1.6582 | 4337 Engineering Steel Factory for Cannes
EN 34CrNiMo6 Steel is an important alloy engineering steel grade as per BS EN10083-3:2006. 34CrNim06 steel has high strength, high toughness and good hardenability. EN / DIN 34CrNiMo6 alloy steel has the stability ofresistance to overheating, but the white sensitivity of 34CrNiM06 ishigh. It also has the temper brittleness, so the weldability of34CrNiMo6 material is poor. The steel 34CrNiMo6 needs the hightemperature preheating before welding in order to eliminate the stressafter welding pr...
Assume full responsibility to meet all demands of our clients; achieve continuous advancements by promoting the growth of our clients; become the final permanent cooperative partner of clients and maximize the interests of clients for 11 Years manufacturer EN DIN 34CrNiMo6 | 1.6582 | 4337 Engineering Steel Factory for Cannes, We cordially welcome customers from at home and abroad to join us and cooperate with us to enjoy a better future.
is an important alloy engineering steel grade as per BS EN
10083-3:2006. 34CrNim06 steel has high strength, high toughness and good
hardenability. EN / DIN 34CrNiMo6 alloy steel has the stability of
resistance to overheating, but the white sensitivity of 34CrNiM06 is
high. It also has the temper brittleness, so the weldability of
34CrNiMo6 material is poor. The steel 34CrNiMo6 needs the high
temperature preheating before welding in order to eliminate the stress
after welding processing.
1.EN Steel 34CrNiMo6 Supply Range
Round Steel Bar Sizes: diameter 80mm – 1200mm
Other steel shape and sizes available according to your requirements.
Surface finish: Black, machined, peeled, turned or according to other customers’ pecial requirements.
2.EN 34CrNiMo6 Steel Standards And Equivalents
|BS EN 10083 -3: 2006||34CrNiMo6 / 1.6582||: 2004||4337|
|BS EN 10250 – 3: 2000|
3. EN/DIN 34CrNiMo6 Steel Chemical Composition Properties
|BS EN 10083 – 3:2006||34CrNiMo6
|0.30-0.38||0.5-0.8||0.40 max||0.025 max||0.035 max||1.3-1.7||0.15-0.30||1.3-1.7|
|BS EN 10250-3:2000||C||Mn||Si||P||S||Cr||Mo||Ni|
|0.30-0.38||0.5-0.8||0.40 max||0.035 max||0.035 max||1.3-1.7||0.15-0.30||1.3-1.7|
|ASTM A29: 2004||4337||C||Mn||Si||P||S||Cr||Mo||Ni|
|0.30-0.40||0.6-0.8||0.20-0.35||0.035 max||0.040 max||0.70-0.90||0.20-0.30||1.65-2.00|
4.Mechanical Properties of EN/DIN 34CrNiM06 / 1.6582 Alloy Steel
|Properties||< 16||>16 – 40||>40 – 100||>100 – 160||>160 – 250|
|Thickness t [mm]||< 8||8<t<20||20<t<60||60<t<100||100<t<160|
|Yield strength Re [N/mm²]||min. 1000||min. 900||min. 800||min. 700||min. 600|
|Tensile strength Rm [N/mm2]||1200 – 1400||1100 – 1300||1000 – 1200||900 – 1100||800 – 950|
|Elongation A [%]||min. 9||min. 10||min. 11||min. 12||min. 13|
|Reduction of area Z [%]||min. 40||min. 45||min. 50||min. 55||min. 55|
|Toughness CVN [J]||min. 35||min. 45||min. 45||min. 45||min. 45|
5.Heat Treatment of 34CrNiMo6 Engineering Steel
Quenched and Tempered (Q+T) of 34CrNiMo6 Steel
Heat 34CrNiMo6 round steel slowly to the temperature of 850°C;
Soak at this hardening temperature quench in oil;
Temper as soon as 34CrNiMo6 steels reach room temperature.
Heat uniformly to the suitable temperature;
Withdraw from the furnace and cool in the air.
The usual tempering temperature is 600°C which depending on the actual requirements.
6.Forging of DIN 34CrNiMo6 / 1.6582 Steel
Hot forming temperature: 1100-900oC.
7.Machinability of Steel 34CrNiMo6
is best done with this 1.6582 alloy steel in the annealed or normalized
and tempered condition. It can be machined by all conventional methods.
alloy materials can be fusion or resistance welded. Preheat and post
heat weld procedures should be followed when welding this alloy by
34CrNiMo6 steel is used to make tools which demands good plasticity and
high strength. It is usually selected to make the big size and important
parts, such as heavy machinery axle,turbine shaft blade, high load of
transmission parts, fasteners, crank shafts, gears, as well as heavily
loaded parts for motor construction etc.
Otai Steel is reliable to
supply engineering 34CrNiMo6 steels / 1.6582 engineering alloy steels.
Please tell us your detailed requirements and have the best offer soon.
A not-so-quick video demonstrating the basics of Mapped Keys within ISBoxer. Apologies for the long video but, there was much to be covered in this one.
For more information on ISBoxer and multiboxing:
Stover Pump Jack Base in 5 pieces was welded by a novice welder.
Muggyweld.com customer Herman Ginger used the 77 arc rod to repair the base with a Miller AC/DC welding machine at 70 amps, and sent us the photos and testimonial of the repair. He tacked the part together and beveled the area to be welded for netter penetration. The 77 arc rods will work on cast iron, cast steel and mild steel in any combination. Some welders use the 77 as a TIG rod without removing the coating.
For more videos and information, or to order, visit http://MuggyWeld.com
Please read all instructions prior to use at: http://muggyweld.com/packets/castironpostsale.pdf
Please use common sense and adhere to all AWS welding safety guidelines when using Muggy Weld products http://www.aws.org/technical/facts/ These guidelines apply to each step of use, from lighting torch, to manipulating flux, to applying rod, to grinding/polishing/finishing.
Muggy Weld LLC shall not be liable for any loss, injury, claim, liability, or damage of any kind resulting in any way from (a) your use of this Site, (b) any products obtained from this Site, (c) any errors in or omissions from this Site, (d) any content contained on this Site.
MSDS sheets available with purchase from MuggyWeld.com, upon request.