1. Relevant D2 Steel Specifications Country USA German Japan Standard ASTM A681 DIN EN ISO 4957 JIS G4404 Grades D2 1.2379/X153CrMo12 SKD11 2. D2 Tool Steel Chemical Composition ASTM A681 C Mn P S Si Cr V Mo D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2 DIN ISO 4957 C Mn P S Si Cr V Mo 1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1 JIS G4404 C Mn P S Si Cr V Mo SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2 3. AISI Grade...


  • Length: 3-5.8mm or Customization
  • Surface: black, peeled, or rough turned
  • Heat treatment: air-cooling, normalized, annealed, Q&T
  • Smelting process: EAF+LF+VD
  • Product Detail

    Product Tags

    continue to improve, to ensure product quality in line with market and customer standard requirements. Our company has a quality assurance system have been established for 11 Years Factory D2 Tool Steel | 1.2379 | X153CrMo12 | SKD11 Factory for Kenya, We are sincerely welcome good friends from numerous circles at dwelling and abroad come to cooperate!


    1. Relevant D2 Steel Specifications

    Country USA German Japan
    Standard ASTM A681 DIN EN ISO 4957 JIS G4404
    Grades D2 1.2379/X153CrMo12 SKD11

    2. D2 Tool Steel Chemical Composition

    ASTM A681 C Mn P S Si Cr V Mo
    D2 1.4 1.6 0.1 0.6 0.03 0.03 0.1 0.6 11 13 0.5 1.1 0.7 1.2
    DIN ISO 4957 C Mn P S Si Cr V Mo
    1.2379/X153CrMo12 1.45 1.6 0.2 0.6 0.03 0.03 0.15 1.6 11 13 0.7 1 0.7 1
    JIS G4404 C Mn P S Si Cr V Mo
    SKD11 1.4 1.6 0.6 0.03 0.03 0.4 11 13 0.2 0.5 0.8 1.2

    3. AISI Grade D2 Steel Mechanical Properties

    Mechanical Properties Metric Imperial
    Hardness, Knoop (converted from Rockwell C hardness) 769 769
    Hardness, Rockwell C 62 62
    Hardness, Vickers 748 748
    Izod impact unnotched 77.0 J 56.8 ft-lb
    Poisson’s ratio 0.27-0.30 0.27-0.30
    Elastic modulus 190-210 GPa 27557-30457 ksi

    Thermal Properties

    Properties

    Conditions

    T (°C)

    Treatment

    Thermal expansion 10.4 x 10-6/ºC 20-100

    4. AISI/ASTM A681 D2 Grade Steel Forging

    Heating for forging of AISI D2 tool steel should
    be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often
    as necessary, stopping work when the temperature drops below 1700°F(926℃). After D2
    die steel forging, cool slowly in lime, mica, dry ashes or furnace. AISI D2 steel
    should always be annealed after forging.

    5. D2 Tool Steel Heat Treatment

    • Heat Treatment

    ASTM  D2 steels alloy should be preheated very slowly to 815oC (1500oF) and  then temperature can be increased to 1010oC (1850oF). They are then held  at 1010oC (1850oF) for 20 to 45 minutes and air cooled (air quenched).

    • Annealing

    Annealing  of D2 tool steels material should be done at 871 to 898oC (1600 to  1650oF) followed by slow furnace cooling at 4.4oC (40oF) per hour or  less.after which cooling rate may be increased. Suitable precautions  must be taken to prevent excessive carburization or decarburization.

    • Stress Relieving

    When  desirable to relieve the strains of machining, heat D2 grade steel  slowly to 1050°-1250°F, allow to equalize, and then cool in still air  (Strain Relieving).

    • Preheat Prior To Hardening

    Preheat slowly to 1350°-1450°F and hold at this temperature until grade steel D2 material is uniformly heated.

    • Hardening

    After  thorough preheating, heat to 1800°-1850°F. Hold the work piece at the  hardening temperature until it is completely and uniformly heated.

    • Quenching

    AISI  D2 steel tool material is an air hardening steel and will develop  hardness on cooling in still air. To avoid scaling and prevent  decarburization of the work piece surface, controlled atmosphere or  vacuum furnaces are recommended. If these furnaces are not available,  pack hardening, salt baths or wrapping the piece in stainless steel foil  will provide some degree of surface protection in the hardening  process. Parts should be allowed to cool to 150F, or to where they can  be held in the bare hand, and then temper immediately.

    • Tempering

    The  tempering temperature on material D2 steel may be varied according to  the desired hardness. D2 steels can be tempered at 204oC (400oF) for  achieving Rockwell C hardness of 61 and at 537oC (1000oF) for a Rockwell  C hardness of 54.

    6. D2 Tool Steel Material Application
     AISI grade D2 tool steels are used for long run tooling applications,  where wear resistance is important, such as blanking or forming dies and  thread rolling dies.

    Some main applications for D2 tool steel are as below:

    Blanking  Dies, Forming Dies, Coining Dies, Slitting Cutters, Heading Tools, Long  Punches, Forming Rolls, Edging Rolls, Master Tools, Beading Rolls,  Intricate Punches, Extrusion Dies, Drawing Dies, Lamination Dies, Thread  Rolling Dies, Shear Blades, Burnishing Tools, Gauges, Knurls, Wear  Parts.

    We usually hold D2 tool  steel on sale activities, and you would have our price on regular  schedule. Contact us and sign in our newsletter to have D2 tool steel  materials price list and commercial quote today.

  • Previous:
  • Next:



  • You can’t have confidence in a product until you test it…. Here I test even a failure just to see how bad it is… looks bad… works great… tastes better!



    Educational video clip teaching how to braze brass tubing to a piece of metal. Mike works by using a propane torch and Muggy Weld SSF-6 56% Silver Solder.

    For a lot more films and details, or to get, take a look at http://MuggyWeld.com

    Please read all guidelines prior to use at: http://muggyweld.com/packets/ssff6ssq6postsale.pdf

    _______________________

    Please take a look at http://www.aws.org/technical/details/ prior to applying Muggy Weld solutions, and adhere to all AWS welding protection pointers. Additional item protection details is obtainable at http://muggyweld.com/protection-pointers.

    Muggy Weld LLC shall not be liable for any loss, damage, declare, liability, or harm of any type resulting in any way from (a) your use of this Internet site, (b) any expert services or solutions attained from this Internet site, (c) any errors in or omissions from this Internet site, (d) the unavailability or interruption of this Internet site or any functions thereof, (e) any material contained on this Internet site.

    MSDS sheets obtainable with invest in from MuggyWeld.com, on request.

    Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the Car

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Plane